AN ENTROPIC THEORY OF DAMAGE WITH APPLICATIONS TO CORROSION-FATIGUE STRUCTURAL INTEGRITY ASSESSMENT

This dissertation demonstrates an explanation of damage and reliability of critical components and structures within the second law of thermodynamics. The approach relies on the fundamentals of irreversible thermodynamics, specifically the concept of entropy generation due to materials degradation as an index of damage. All failure mechanisms that cause degradation, damage accumulation and ultimate failure share a common feature, namely energy dissipation. Energy dissipation, as a fundamental measure for irreversibility in a thermodynamic treatment of non-equilibrium processes, leads to and can be expressed in terms of entropy generation. The dissertation proposes a theory of damage by relating entropy generation to energy dissipation via generalized thermodynamic forces and thermodynamic fluxes that formally describes the resulting damage. Following the proposed theory of entropic damage, an approach to reliability and integrity characterization based on thermodynamic entropy is discussed. It is shown that the variability in the amount of the thermodynamic-based damage and uncertainties about the parameters of a distribution model describing the variability, leads to a more consistent and broader definition of the well know time-to-failure distribution in reliability engineering. As such it has been shown that the reliability function can be derived from the thermodynamic laws rather than estimated from the observed failure histories. Furthermore, using the superior advantages of the use of entropy generation and accumulation as a damage index in comparison to common observable markers of damage such as crack size, a method is proposed to explain the prognostics and health management (PHM) in terms of the entropic damage. The proposed entropic-based damage theory to reliability and integrity is then demonstrated through experimental validation. Using this theorem, the corrosion-fatigue entropy generation function is derived, evaluated and employed for structural integrity, reliability assessment and remaining useful life (RUL) prediction of Aluminum 7075-T651 specimens tested.

Neural Modulation of Leg Stiffness in Response to Neuromuscular Fatigue

The spring-mass model is able to accurately represent hopping spring-like behavior (leg and joint stiffness), and leg and joint stiffness changes can reveal overall motor control responses to neural and muscular contributors of neuromuscular fatigue. By understanding leg stiffness modulation, we can determine which variables the nervous system targets to maintain motor performance and stability. The purpose of this study was to determine how neuromuscular fatigue affects hopping behavior by examining leg and joint stiffness before and after a single-leg calf raise fatiguing protocol. Post-fatigue, leg stiffness decreased for the exercised leg, but not for the non-exercised leg. Ankle and knee joint stiffness did not significantly change for either leg. This indicates that leg stiffness decreases primarily from muscular fatigue, but was not explained by ankle and knee joint stiffness. The decrease in leg stiffness may be an attempt to soften landing impact, while at the same time maintaining performance.

Evaluation of Information Entropy from Acoustic Emission Waveforms as a Fatigue Damage Metric for Al7075-T6

Information entropy measured from acoustic emission (AE) waveforms is shown to be an indicator of fatigue damage in a high-strength aluminum alloy. Several tension-tension fatigue experiments were performed with dogbone samples of aluminum alloy, Al7075-T6, a commonly used material in aerospace structures. Unlike previous studies in which fatigue damage is simply measured based on visible crack growth, this work investigated fatigue damage prior to crack initiation through the use of instantaneous elastic modulus degradation. Three methods of measuring the AE information entropy, regarded as a direct measure of microstructural disorder, are proposed and compared with traditional damage-related AE features. Results show that one of the three entropy measurement methods appears to better assess damage than the traditional AE features, while the other two entropies have unique trends that can differentiate between small and large cracks.