DEVELOPMENT OF LI+ AND NA+ CONDUCTING CERAMICS AND CERAMIC STRUCTURES FOR USE IN SOLID STATE BATTERIES

A solid state lithium metal battery based on a lithium garnet material was developed, constructed and tested. Specifically, a porous-dense-porous trilayer structure was fabricated by tape casting, a roll-to-roll technique conducive to high volume manufacturing. The high density and thin center layer (< 20 μm) effectively blocks dendrites even over hundreds of cycles. The microstructured porous layers, serving as electrode supports, are demonstrated to increase the interfacial surface area available to the electrodes and increase cathode loading. Reproducibility of flat, well sintered ceramics was achieved with consistent powderbed lattice parameter and ball milling of powderbed. Together, the resistance of the LLCZN trilayer was measured at an average of 7.6 ohm-cm2 in a symmetric lithium cell, significantly lower than any other reported literature results. Building on these results, a full cell with a lithium metal anode, LLCZN trilayer electrolyte, and LiCoO2 cathode was cycled 100 cycles without decay and an average ASR of 117 ohm-cm2. After cycling, the cell was held at open circuit for 24 hours without any voltage fade, demonstrating the absence of a dendrite or short-circuit of any type. Cost calculations guided the optimization of a trilayer structure predicted that resulting cells will be highly competitive in the marketplace as intrinsically safe lithium batteries with energy densities greater than 300 Wh/kg and 1000 Wh/L for under $100/kWh. Also in the pursuit of solid state batteries, an improved Na+ superionic conductor (NASICON) composition, Na3Zr2Si2PO12, was developed with a conductivity of 1.9x10-3 S/cm. New super-lithiated lithium garnet compositions, Li7.06La3Zr1.94Y0.06O12 and Li7.16La3Zr1.84Y0.16O12, were developed and studied revealing insights about the mechanisms of conductivity in lithium garnets.

Increasing Stability of Lithium-Ion Batteries with Ordered Graphene Silicon Negative Electrodes

Currently, lackluster battery capability is restricting the widespread integration of Smart Grids, limiting the long-term feasibility of alternative, green energy conversion technologies. Silicon nanoparticles have great conductivity for applications in rechargeable batteries, but have degradation issues due to changes in volume during lithiation/delithiation cycles. To combat this, we use electrochemical deposition to uniformly space silicon particles on graphene sheets to create a more stable structure. We found the process of electrochemical deposition degraded the graphene binding in the electrode material, severely reducing charge capacity. But, the usage of mechanically mixing silicon particles with grapheme yielded batteries better than those that are commercially available.

INVESTIGATION OF MAGNESIUM ION CHARGE STORAGE MECHANISM IN MANGANESE DIOXIDE

Magnesium (Mg) battery is considered as a promising candidate for the next generation battery technology that could potentially replace the current lithium (Li)-ion batteries due to the following factors. Magnesium possesses a higher volumetric capacity than commercialized Li-ion battery anode materials. Additionally, the low cost and high abundance of Mg compared to Li makes Mg batteries even more attractive. Moreover, unlike metallic Li anodes which have a tendency to develop a dendritic structure on the surface upon the cycling of the battery, Mg metal is known to be free from such a hazardous phenomenon. Due to these merits of Mg as an anode, the topic of rechargea¬ble Mg batteries has attracted considerable attention among researchers in the last few decades. However, the aforementioned advantages of Mg batteries have not been fully utilized due to the serious kinetic limitation of Mg2+ diffusion process in many hosting compounds which is believed to be due to a strong electrostatic interaction between divalent Mg2+ ions and hosting matrix. This serious kinetic hindrance is directly related to the lack of cathode materials for Mg battery that provide comparable electrochemical performances to that of Li-based system. Manganese oxide (MnO2) is one of the most well studied electrode materials due to its excellent electrochemical properties, including high Li+ ion capacity and relatively high operating voltage (i.e., ~ 4 V vs. Li/Li+ for LiMn2O4 and ~ 3.2 V vs. Mg/Mg2+). However, unlike the good electrochemical properties of MnO2 realized in Li-based systems, rather poor electrochemical performances have been reported in Mg based systems, particularly with low capacity and poor cycling performances. While the origin of the observed poor performances is believed to be due to the aforementioned strong ionic interaction between the Mg2+ ions and MnO2 lattice resulting in a limited diffusion of Mg2+ ions in MnO2, very little has been explored regarding the charge storage mechanism of MnO2 with divalent Mg2+ ions. This dissertation investigates the charge storage mechanism of MnO2, focusing on the insertion behaviors of divalent Mg2+ ions and exploring the origins of the limited Mg2+ insertion behavior in MnO2. It is found that the limited Mg2+ capacity in MnO2 can be significantly improved by introducing water molecules in the Mg electrolyte system, where the water molecules effectively mitigated the kinetic hindrance of Mg2+ insertion process. The combination of nanostructured MnO2 electrode and water effect provides a synergic effect demonstrating further enhanced Mg2+ insertion capability. Furthermore, it is demonstrated in this study that pre-cycling MnO2 electrodes in water-containing electrolyte activates MnO2 electrode, after which improved Mg2+ capacity is maintained in dry Mg electrolyte. Based on a series of XPS analysis, a conversion mechanism is proposed where magnesiated MnO2 undergoes a conversion reaction to Mg(OH)2 and MnOx and Mn(OH)y species in the presence of water molecules. This conversion process is believed to be the driving force that generates the improved Mg2+ capacity in MnO2 along with the water molecule’s charge screening effect. Finally, it is discussed that upon a consecutive cycling of MnO2 in the water-containing Mg electrolyte, structural water is generated within the MnO2 lattice, which is thought to be the origin of the observed activation phenomenon. The results provided in this dissertation highlight that the divalency of Mg2+ ions result in very different electrochemical behaviors than those of the well-studied monovalent Li+ ions towards MnO2.

MEMS SENSOR PLATFORMS FOR IN SITU CHARACTERIZATION OF LI-ION BATTERY ELECTRODES

Lithium-ion batteries provide high energy density while being compact and light-weight and are the most pervasive energy storage technology powering portable electronic devices such as smartphones, laptops, and tablet PCs. Considerable efforts have been made to develop new electrode materials with ever higher capacity, while being able to maintain long cycle life. A key challenge in those efforts has been characterizing and understanding these materials during battery operation. While it is generally accepted that the repeated strain/stress cycles play a role in long-term battery degradation, the detailed mechanisms creating these mechanical effects and the damage they create still remain unclear. Therefore, development of techniques which are capable of capturing in real time the microstructural changes and the associated stress during operation are crucial for unravelling lithium-ion battery degradation mechanisms and further improving lithium-ion battery performance. This dissertation presents the development of two microelectromechanical systems sensor platforms for in situ characterization of stress and microstructural changes in thin film lithium-ion battery electrodes, which can be leveraged as a characterization platform for advancing battery performance. First, a Fabry-Perot microelectromechanical systems sensor based in situ characterization platform is developed which allows simultaneous measurement of microstructural changes using Raman spectroscopy in parallel with qualitative stress changes via optical interferometry. Evolutions in the microstructure creating a Raman shift from 145 cm−1 to 154 cm−1 and stress in the various crystal phases in the LixV2O5 system are observed, including both reversible and irreversible phase transitions. Also, a unique way of controlling electrochemically-driven stress and stress gradient in lithium-ion battery electrodes is demonstrated using the Fabry-Perot microelectromechanical systems sensor integrated with an optical measurement setup. By stacking alternately stressed layers, the average stress in the stacked electrode is greatly reduced by 75% compared to an unmodified electrode. After 2,000 discharge-charge cycles, the stacked electrodes retain only 83% of their maximum capacity while unmodified electrodes retain 91%, illuminating the importance of the stress gradient within the electrode. Second, a buckled membrane microelectromechanical systems sensor is developed to enable in situ characterization of quantitative stress and microstructure evolutions in a V2O5 lithium-ion battery cathode by integrating atomic force microscopy and Raman spectroscopy. Using dual-mode measurements in the voltage range of the voltage range of 2.8V – 3.5V, both the induced stress (~ 40 MPa) and Raman intensity changes due to lithium cycling are observed. Upon lithium insertion, tensile stress in the V2O5 increases gradually until the α- to ε-phase and ε- to δ-phase transitions occur. The Raman intensity change at 148 cm−1 shows that the level of disorder increases during lithium insertion and progressively recovers the V2O5 lattice during lithium extraction. Results are in good agreement with the expected mechanical behavior and disorder change in V2O5, highlighting the potential of microelectromechanical systems as enabling tools for advanced scientific investigations. The work presented here will be eventually utilized for optimization of thin film battery electrode performance by achieving fundamental understanding of how stress and microstructural changes are correlated, which will also provide valuable insight into a battery performance degradation mechanism.

Nano-Engineering of Densely Packed Electrochemical Energy Storage Architectures by Atomic Layer Deposition

Nanostructures are highly attractive for future electrical energy storage devices because they enable large surface area and short ion transport time through thin electrode layers for high power devices. Significant enhancement in power density of batteries has been achieved by nano-engineered structures, particularly anode and cathode nanostructures spatially separated far apart by a porous membrane and/or a defined electrolyte region. A self-aligned nanostructured battery fully confined within a single nanopore presents a powerful platform to determine the rate performance and cyclability limits of nanostructured storage devices. Atomic layer deposition (ALD) has enabled us to create and evaluate such structures, comprised of nanotubular electrodes and electrolyte confined within anodic aluminum oxide (AAO) nanopores. The V2O5- V2O5 symmetric nanopore battery displays exceptional power-energy performance and cyclability when tested as a massively parallel device (~2billion/cm2), each with ~1m3 volume (~1fL). Cycled between 0.2V and 1.8V, this full cell has capacity retention of 95% at 5C rate and 46% at 150C, with more than 1000 charge/discharge cycles. These results demonstrate the promise of ultrasmall, self-aligned/regular, densely packed nanobattery structures as a testbed to study ionics and electrodics at the nanoscale with various geometrical modifications and as a building block for high performance energy storage systems[1, 2]. Further increase of full cell output potential is also demonstrated in asymmetric full cell configurations with various low voltage anode materials. The asymmetric full cell nanopore batteries, comprised of V2O5 as cathode and prelithiated SnO2 or anatase phase TiO2 as anode, with integrated nanotubular metal current collectors underneath each nanotubular storage electrode, also enabled by ALD. By controlling the amount of lithium ion prelithiated into SnO2 anode, we can tune full cell output voltage in the range of 0.3V and 3V. This asymmetric nanopore battery array displays exceptional rate performance and cyclability. When cycled between 1V and 3V, it has capacity retention of approximately 73% at 200C rate compared to 1C, with only 2% capacity loss after more than 500 charge/discharge cycles. With increased full cell output potential, the asymmetric V2O5-SnO2 nanopore battery shows significantly improved energy and power density. This configuration presents a more realistic test - through its asymmetric (vs symmetric) configuration – of performance and cyclability in nanoconfined environment. This dissertation covers (1) Ultra small electrochemical storage platform design and fabrication, (2) Electron and ion transport in nanostructured electrodes inside a half cell configuration, (3) Ion transport between anode and cathode in confined nanochannels in symmetric full cells, (4) Scale up energy and power density with geometry optimization and low voltage anode materials in asymmetric full cell configurations. As a supplement, selective growth of ALD to improve graphene conductance will also be discussed[3]. References: 1. Liu, C., et al., (Invited) A Rational Design for Batteries at Nanoscale by Atomic Layer Deposition. ECS Transactions, 2015. 69(7): p. 23-30. 2. Liu, C.Y., et al., An all-in-one nanopore battery array. Nature Nanotechnology, 2014. 9(12): p. 1031-1039. 3. Liu, C., et al., Improving Graphene Conductivity through Selective Atomic Layer Deposition. ECS Transactions, 2015. 69(7): p. 133-138.