AN ENTROPIC THEORY OF DAMAGE WITH APPLICATIONS TO CORROSION-FATIGUE STRUCTURAL INTEGRITY ASSESSMENT

This dissertation demonstrates an explanation of damage and reliability of critical components and structures within the second law of thermodynamics. The approach relies on the fundamentals of irreversible thermodynamics, specifically the concept of entropy generation due to materials degradation as an index of damage. All failure mechanisms that cause degradation, damage accumulation and ultimate failure share a common feature, namely energy dissipation. Energy dissipation, as a fundamental measure for irreversibility in a thermodynamic treatment of non-equilibrium processes, leads to and can be expressed in terms of entropy generation. The dissertation proposes a theory of damage by relating entropy generation to energy dissipation via generalized thermodynamic forces and thermodynamic fluxes that formally describes the resulting damage. Following the proposed theory of entropic damage, an approach to reliability and integrity characterization based on thermodynamic entropy is discussed. It is shown that the variability in the amount of the thermodynamic-based damage and uncertainties about the parameters of a distribution model describing the variability, leads to a more consistent and broader definition of the well know time-to-failure distribution in reliability engineering. As such it has been shown that the reliability function can be derived from the thermodynamic laws rather than estimated from the observed failure histories. Furthermore, using the superior advantages of the use of entropy generation and accumulation as a damage index in comparison to common observable markers of damage such as crack size, a method is proposed to explain the prognostics and health management (PHM) in terms of the entropic damage. The proposed entropic-based damage theory to reliability and integrity is then demonstrated through experimental validation. Using this theorem, the corrosion-fatigue entropy generation function is derived, evaluated and employed for structural integrity, reliability assessment and remaining useful life (RUL) prediction of Aluminum 7075-T651 specimens tested.

BEHAVIOR OF FIBER REINFORCED POLYMER COMPOSITE PILES WITH ELLIPTICAL CROSS SECTIONS IN INTEGRAL ABUTMENT BRIDGE FOUNDATIONS

Every year in the US and other cold-climate countries considerable amount of money is spent to restore structural damages in conventional bridges resulting from (or “caused by”) salt corrosion in bridge expansion joints. Frequent usage of deicing salt in conventional bridges with expansion joints results in corrosion and other damages to the expansion joints, steel girders, stiffeners, concrete rebar, and any structural steel members in the abutments. The best way to prevent these damages is to eliminate the expansion joints at the abutment and elsewhere and make the entire bridge abutment and deck a continuous monolithic structural system. This type of bridge is called Integral Abutment Bridge which is now widely used in the US and other cold-climate countries. In order to provide lateral flexibility, the entire abutment is constructed on piles. Piles used in integral abutments should have enough capacity in the perpendicular direction to support the vertical forces. In addition, piles should be able to withstand corrosive environments near the surface of the ground and maintain their performance during the lifespan of the bridge. Fiber Reinforced Polymer (FRP) piles are a new type of pile that can not only accommodate large displacements, but can also resist corrosion significantly better than traditional steel or concrete piles. The use of FRP piles extends the life of the pile which in turn extends the life of the bridge. This dissertation studies FRP piles with elliptical shapes. The elliptical shapes can simultaneously provide flexibility and stiffness in two perpendicular axes. The elliptical shapes can be made using the filament winding method which is a less expensive method of manufacturing compared to the pultrusion or other manufacturing methods. In this dissertation a new way is introduced to construct the desired elliptical shapes with the filament winding method. Pile specifications such as dimensions, number of layers, fiber orientation angles, material, and soil stiffness are defined as parameters and the effects of each parameter on the pile stresses and pile failure have been studied. The ANSYS software has been used to model the composite materials. More than 14,000 nonlinear finite element pile models have been created, each slightly different from the others. The outputs of analyses have been used to draw curves. Optimum values of the parameters have been defined using generated curves. The best approaches to find optimum shape, angle of fibers and types of composite material have been discussed.