Reversible ferromagnetic switching in ZnO:(Co,Mn) powders

We report here on the magnetic properties of ZnO:Mn- and ZnO:Co-doped nanoparticles. We have found that the ferromagnetism of ZnO:Mn can be switched on and off by consecutive low-temperature annealings in O2 and N2, respectively, while the opposite phenomenology was observed for ZnO:Co. These results suggest that different defects (presumably n-type for ZnO:Co and p-type for ZnO:Mn) are required to induce a ferromagnetic coupling in each case. We will argue that ferromagnetism is likely to be restricted to a very thin, nanometric layer at the grain surface. These findings reveal and give insight into the dramatic relevance of surface effects to the occurrence of ferromagnetism in ZnO-doped oxides.

Giant heat dissipation at the low temperature reversible-irreversible transition in Gd5Ge4

The heat exchanged at the low-temperature first-order magnetostructural transition is directly measured in Gd5Ge4 . Results show that the origin and the temperature dependence of the heat exchanged varies with the reversible/irreversible character of the first-order transition. In the reversible regime, the heat exchanged by the sample is mostly due to the latent heat at the transition and decreases with decreasing temperature, while in the irreversible regime, the heat is irreversibly dissipated and increases strongly with decreasing temperature, reaching a value of 237 J/kg at 4 K.