Reversible ferromagnetic switching in ZnO:(Co,Mn) powders

We report here on the magnetic properties of ZnO:Mn- and ZnO:Co-doped nanoparticles. We have found that the ferromagnetism of ZnO:Mn can be switched on and off by consecutive low-temperature annealings in O2 and N2, respectively, while the opposite phenomenology was observed for ZnO:Co. These results suggest that different defects (presumably n-type for ZnO:Co and p-type for ZnO:Mn) are required to induce a ferromagnetic coupling in each case. We will argue that ferromagnetism is likely to be restricted to a very thin, nanometric layer at the grain surface. These findings reveal and give insight into the dramatic relevance of surface effects to the occurrence of ferromagnetism in ZnO-doped oxides.

Polyconductivity in polypyrrole: The correlated electron gas

p-toluensulfonate doped polypyrrole (PPy), undergoes an electric-field induced reversible transition from an insulating state to a highly conductive one. The spatially average field can be as small as 200 V/cm, when the temperature of the sample is below 20 K. The applied electric field leads to a sharp jump in the value of the current to a value which is nearly five orders of magnitude higher than before. When the applied electric field is reduced to below a critical value, the system switches back to a low conductive state. The effect is reversible, symmetric in voltage, and reproducible for different samples. The switching is, we believe, an electronic glass melting transition and it is due to the disordered, highly charged granular nature of PPy.

Giant heat dissipation at the low temperature reversible-irreversible transition in Gd5Ge4

The heat exchanged at the low-temperature first-order magnetostructural transition is directly measured in Gd5Ge4 . Results show that the origin and the temperature dependence of the heat exchanged varies with the reversible/irreversible character of the first-order transition. In the reversible regime, the heat exchanged by the sample is mostly due to the latent heat at the transition and decreases with decreasing temperature, while in the irreversible regime, the heat is irreversibly dissipated and increases strongly with decreasing temperature, reaching a value of 237 J/kg at 4 K.