Well-Defined Poly(4-vinylbenzocyclobutene): Synthesis by Living Anionic Polymerization and Characterization

Living anionic polymerization of 4-vinylbenzocylobutene was performed in benzene at room temperature using sec-butyllithium as the initiator. Results of the kinetic studies indicated the termination- and transfer-free nature of the polymerization. Homopolymers with predictable molecular weights and narrow molecular weight distributions were produced, excluding the interference of the cyclobutene rings during initiation and propagation. Thermogravimetric analysis of poly(4-vinylbenzocyclobutene) in air showed a small weight gain at ~200 °C, a rapid decomposition at ~455 °C, and a gradual decomposition at ~566 °C. This behavior was attributed to the formation of radicals from the pendent benzocyclobutene functionality through o-quinodimethane intermediates and simultaneous decomposition/cross-linking reactions at high temperature. The living nature of the polymerization was also examined via sequential copolymerization with butadiene to form diblock copolymers.

Impact of Solvent Quality on the Density Profiles of Looped Triblock Copolymer Brushes by Neutron Reflectivity Measurements

Preferential adsorption of poly(2-vinylpyridine)-deuterated polystyrene-poly(2-vinylpyridine) (PVP-dPS-PVP) triblock copolymers from toluene onto silicon leads to the formation of dPS loops tethered by the PVP end blocks. Using neutron reflectometry, we have determined the segment density profiles of these looped polymer brushes in toluene, a good solvent for the dPS block, and in cyclohexane at 20 °C (poor solvent), 32 °C, (near-Θ solvent), and 50 °C (marginal solvent). While the swelling behavior qualitatively agrees with that observed for singly grafted brushes, there are interesting differences in the local structural details: In a good solvent, the segment density profiles are composed of an inner parabolic region and a long, extended tail. In cyclohexane, the profiles are described by exponential decays. We ascribe these features to a novel polydispersity effect that arises due to tethering the PS loops by both ends. The results also show that the less dense layers undergo more significant changes in swollen height as solvent quality is changed and that the looped brushes of different molecular weight, asymmetry, and tethering density adhere to scaling relationships derived for lightly cross-linked polymer gels.