A CURRENT EXAMINATION OF DIETARY INTAKES OF FIBER, CALCIUM, IRON, AND ZINC AND THEIR RELATIONSHIP TO BLOOD LEAD LEVELS IN U.S. CHILDREN AGED 1-5 YEARS

A CURRENT EXAMINATION OF DIETARY INTAKES OF FIBER, CALCIUM, IRON, AND ZINC AND THEIR RELATIONSHIP TO BLOOD LEAD LEVELS IN U.S. CHILDREN AGED 1-5 YEARS Stephanie Ann Melchert, M.S. University of Nebraska, 2010 Adviser: Kaye Stanek Krogstrand The effect of lead on the health and well-being of those exposed has been well documented and many efforts have been made to reduce exposure of lead to the United States population. Despite these efforts, many studies have documented cognitive impairments and behavioral problems in children with even low levels of lead in their blood. Previous studies have suggested that a proper diet may have a role in the prevention of elevated blood lead levels in children. The objective of this study was to determine if there was an inverse correlation of blood lead levels (BLL) in children to their dietary intakes of fiber, calcium, iron, and zinc considering low levels of lead exposure. This study examined 1019 children in the National Health and Nutrition Examination Survey (NHANES) conducted from 2005-2006. Data were analyzed using Spearman’s rank correlations to correlate continuous variables to BLL in children and independent samples t-tests were used to compare mean blood lead levels of categorical variables. Results indicate that BLL in children is significantly correlated with and weight, recumbent length/standing height, dietary fiber intake and continine, a marker of cigarette smoke exposure. BLL was not significantly correlated with calcium, iron, zinc, or vitamin C. A significant difference was found in the mean BLL of children who took supplements, lived in smoking homes, as well as those who lived in homes built before 1978. Overall, this study shows that children living in homes built before 1978 remain at greater risk for lead exposure, and adequate dietary fiber intake may provide benefits to children who are exposed to lead.

Structural and Magnetic Properties of Neodymium - Iron - Boron Clusters

Using inert gas condensation techniques the properties of sputtered neodymium-iron-born clusters were investigated. A D.C. magnetron sputtering source created vaporous Nd-Fe-B which was then condensed into clusters and deposited onto silicon substrates. A composite target of Nd-Fe-B discs on an iron plate and a composite target of Nd-(Fe-Co)-B were utilized to create clusters. The clusters were coated with a carbon layer through R.F. sputtering to prevent oxidation. Samples were investigated in the TEM and showed a size distribution with an average particle diameter of 8.11 nm. The clusters, upon deposition, were amorphous as indicated by diffuse diffraction patterns obtained through SAD. The EDS showed compositionally a direct correlation in the ratio of rare-earth to transition metals between the target and deposited samples. The magnetic properties of the as-deposited clusters showed superparamagnetic properties at high temperatures and ferromagnetic properties at low temperatures; these properties are indicative of rare-earth transition metal amorphous clusters. Annealing of samples showed an initial increase in the coercivity. Samples were annealed in an inert gas atmosphere at 600o C for increasing amounts of time. The samples showed an initial increase in coercivity, but showed no additional increases with additional annealing time. SAD of annealed cluster samples showed the presence of Nd2Fe17 and a bcc-Nd phase. The bcc-Nd is the result of oxidation at high temperatures created during annealing and surface interface energy. The magnetic properties of the annealed samples showed weak coercivity and a saturation magnetization equivalent to that of Nd2Fe17. The annealed clusters showed a slight increase in coercivity at low temperatures. These results indicate a loss of boron during the sputtering process.