Morphology and Deformation Mechanisms and Tensile Properties of Tetrafunctional Multigraft Copolymers

Morphology and deformation mechanisms and tensile properties of tetrafunctional multigraft (MG) polystrene-g-polyisoprene (PS-g-PI) copolymers were investigated dependent on PS volume fraction and number of branch points. The combination of various methods such as TEM, real time synchrotron SAXS, rheo-optical FTIR, and tensile tests provides comprehensive information at different dimension levels.TEMand SAXS studies revealed that the number of branch points has no obvious influence on the microphase-separated morphology of tetrafunction MG copolymers with 16 wt % PS. But for tetrafunctional MG copolymers with 25 wt % PS, the size and integrity of PS microdomains decrease with increasing number of branch point. The deformation mechanisms ofMGcopolymers are highly related to the morphology. Dependent on the microphase-separated morphology and integrity of the PS phase, the strain-induced orientation of the PS phase is at different size scales. Polarized FT-IR spectra analysis reveals that, for all investigated MG copolymers, the PI phase shows strain-induced orientation along SD at molecular scale. The proportion of the PI block effectively bridging PS domains controls the tensile properties of the MGcopolymers at high strain, while the stress-strain behavior in the low-mediate strain region is controlled by the continuity of PS microdomains. The special molecular architecture, which leads to the higher effective functionality of PS domains and the higher possibility for an individual PI backbone being tethered with a large number of PS domains, is proposed to be the origin of the superelasticity for MG copolymers.

Structural and Magnetic Properties of Neodymium - Iron - Boron Clusters

Using inert gas condensation techniques the properties of sputtered neodymium-iron-born clusters were investigated. A D.C. magnetron sputtering source created vaporous Nd-Fe-B which was then condensed into clusters and deposited onto silicon substrates. A composite target of Nd-Fe-B discs on an iron plate and a composite target of Nd-(Fe-Co)-B were utilized to create clusters. The clusters were coated with a carbon layer through R.F. sputtering to prevent oxidation. Samples were investigated in the TEM and showed a size distribution with an average particle diameter of 8.11 nm. The clusters, upon deposition, were amorphous as indicated by diffuse diffraction patterns obtained through SAD. The EDS showed compositionally a direct correlation in the ratio of rare-earth to transition metals between the target and deposited samples. The magnetic properties of the as-deposited clusters showed superparamagnetic properties at high temperatures and ferromagnetic properties at low temperatures; these properties are indicative of rare-earth transition metal amorphous clusters. Annealing of samples showed an initial increase in the coercivity. Samples were annealed in an inert gas atmosphere at 600o C for increasing amounts of time. The samples showed an initial increase in coercivity, but showed no additional increases with additional annealing time. SAD of annealed cluster samples showed the presence of Nd2Fe17 and a bcc-Nd phase. The bcc-Nd is the result of oxidation at high temperatures created during annealing and surface interface energy. The magnetic properties of the annealed samples showed weak coercivity and a saturation magnetization equivalent to that of Nd2Fe17. The annealed clusters showed a slight increase in coercivity at low temperatures. These results indicate a loss of boron during the sputtering process.