A study of the oxygen electrochemistry of ruthenium and iridium

This thesis is concerned with an investigation of the anodic behaviour of ruthenium and iridium in aqueous solution and particularly of oxygen evolution on these metals. The latter process is of major interest in the large-scale production of hydrogen gas by the electrolysis of water. The presence of low levels of ruthenium trichloride ca. 10-4 mol dm-3 in acid solution give a considerable increase in the rate of oxygen evolution from platinum and gold, but not graphite, anodes. The mechanism of this catalytic effect was investigated using potential step and a.c. impedance technique. Earlier suggestions that the effect is due to catalysis by metal ions in solution were proved to be incorrect and it was shown that ruthenium species were incorporated into the surface oxide film. Changes in the oxidation state of these ruthenium species is probably responsible for the lowering of the oxygen overvoltage. Both the theoretical and practical aspects of the reaction were complicated by the fact that at constant potential the rates of both the catalysed and the uncatalysed oxygen evolution processes exhibit an appreciable, continuous decrease with either time or degree of oxidation of the substrate. The anodic behaviour of iridium in the oxide layer region has been investigated using conventional electrochemical techniques such as cyclic voltammetry. Applying a triangular voltage sweep at 10 Hz, 0.01 to 1.50V increases the amount of electric charge which the surface can store in the oxide region. This activation effect and the mechanism of charge storage is discussed in terms of both an expanded lattice theory for oxide growth on noble metals and a more recent theory of irreversible oxide formation with subsequent stoichiometry changes. The lack of hysteresis between the anodic and cathodic peaks at ca. 0.9 V suggests that the process involved here is proton migration in a relatively thick surface layer, i.e. that the reaction involved is some type of oxide-hydroxide transition. Lack of chloride ion inhibition in the anodic region also supports the irreversible oxide formation theory; however, to account for the hydrogen region of the potential sweep a compromise theory involving partial reduction of the outer regions of iridium oxide film is proposed. The loss of charge storage capacity when the activated iridium surface is anodized for a short time above ca. 1.60 V is attributed to loss by corrosion of the outer active layer from the metal surface. The behaviour of iridium at higher anodic potentials in acid solution was investigated. Current-time curves at constant potential and Tafel plots suggested that a change in the mechanism of the oxygen evolution reaction occurs at ca. 1.8 V. Above this potential, corrosion of the metal occurred, giving rise to an absorbance in the visible spectrum of the electrolyte (λ max = 455 nm). It is suggested that the species involved was Ir(O2)2+. A similar investigation in the case of alkaline electrolyte gave no evidence for a change in mechanism at 1.8 V and corrosion of the iridium was not observed. Oxygen evolution overpotentials were much lower for iridium than for platinum in both acidic and alkaline solutions.

HIF-1alpha role in oxygen-dependent radio- and chemosensitivity

Poor oxygenation (hypoxia) is a common characteristic of human solid tumours, and is associated with cell survival, metastasis and resistance to radio- and chemotherapies. Hypoxia-induced stabilisation of hypoxia-inducible factor-1α (HIF-1α) leads to changes in expression of various genes associated with growth, vascularisation and metabolism. However whether HIF-1α plays a causal role in promoting hypoxic resistance to antitumour therapies remains unclear. In this study we used pharmacological and genetic methods to investigate the HIF-1α contribution to radio- and chemoresistance in four cancer cell lines derived from cervical, breast, prostate and melanoma human tumours. Under normoxia or hypoxia (<0.2% or 0.5% oxygen) the cells were exposed to either a standard irradiation dose (6.2 Gy) or chemotherapeutic drug (cisplatin), and subsequent cell proliferation (after 7 days) was measured in terms of resazurin reduction. Oxygen-dependent radio- and chemosensitivity was evident in all wild type whereas it was reduced or abolished in HIF-1α (siRNA) knockdown cells. The effects of HIF-1α-modulating drugs (EDHB, CoCl2, deferoxamine to stabilise and R59949 to destabilise it) reflected both HIF-1α-dependent and independent mechanisms. Collectively the data show that HIF-1α played a causal role in our in vitro model of hypoxia-induced radioresistance whereas its contribution to oxygendependent sensitivity to cisplatin was less clear-cut. Although this behavior is likely to be conditioned by further biological and physical factors operating in vivo, it is consistent with the hypothesis that interventions directed at HIF-1α may improve the clinical effectiveness of tumour treatments.

Low valence cation doping of bulk Cr2O3: Charge compensation and oxygen vacancy formation

The different oxidation states of chromium allow its bulk oxide form to be reducible, facilitating the oxygen vacancy formation process, which is a key property in applications such as catalysis. Similar to other useful oxides such as TiO2, and CeO2, the effect of substitutional metal dopants in bulk Cr2O3 and its effect on the electronic structure and oxygen vacancy formation are of interest, particularly in enhancing the latter. In this paper, density functional theory (DFT) calculations with a Hubbard + U correction (DFT+U) applied to the Cr 3d and O 2p states, are carried out on pure and metal-doped bulk Cr2O3 to examine the effect of doping on the electronic and geometric structure. The role of dopants in enhancing the reducibility of Cr2O3 is examined to promote oxygen vacancy formation. The dopants are Mg, Cu, Ni, and Zn, which have a formal +2 oxidation state in their bulk oxides. Given this difference in host and, dopant oxidation states, we show that to predict the correct ground state two metal dopants charge compensated with an oxygen vacancy are required. The second oxygen atom removed is termed "the active" oxygen vacancy and it is the energy required to remove this atom that is related to the reduction process. In all cases, we find that substitutional doping improves the oxygen vacancy formation of bulk Cr2O3 by lowering the energy cost.