Maltodextrin-incorporated-vacuum-dried honey powder: processing and stability

Honey is rich in sugar content and dominated by fructose and glucose that make honey prone to crystallize during storage. Due to honey composition, the anhydrous glass transition temperature of honey is very low that makes honey difficult to dry alone and drying aid or filler is needed to dry honey. Maltodextrin is a common drying aid material used in drying of sugar-rich food. The present study aims to study the processing of honey powder by vacuum drying method and the impact of drying process and formulation on the stability of honey powder. To achieve the objectives, the series of experiments were done: investigating of maltodextrin DE 10 properties, studying the effect of drying temperature, total solid concentration, DE value, maltodextrin concentration and anti-caking agent on honey powder processing and stability. Maltodextrin provide stable glass compared to lower molecular weight sugars. Dynamic Dew Point Isotherm (DDI) data could be used to determine amorphous content of a system. The area under the first derivative curve from DDI curve is equal to the amount of water needed by amorphous material to crystallize. The drying temperature affected the amorphous content of vacuum-dried honey powder. The higher temperature seemed to result in honey powder with more amorphous component. The ratio of maltodextrin affected more significantly the stability of honey powder compared to the treatments of total solids concentration, DE value and drying temperature. The critical water activity of honey powder was lower than water activity of the equilibrium water content corresponding to BET monolayer water content. Addition of anti-caking agent increased stability and flow-ability of honey powder. Addition of Calcium stearate could inhibit collapse of the honey powder during storage.

A comparative study of the structural, mechanical and tribological characteristics of TiSiC-Cr coatings prepared in CH4 and C2H2 reactive atmosphere by cathodic vacuum arc

TiSiC-Cr coatings, with Cr and Si as additional elements, were deposited on Si, C 45 and 316 L steel substrates via cathodic arc evaporation. Two series of coatings with thicknesses in the range of 3.6–3.9 μm were produced, using either CH4 or C2H2 as carbon containing gas. For each series, different coatings were prepared by varying the carbon rich gas flow rate between 90 and 130 sccm, while maintaining constant cathode currents (110 and 100 A at TiSi and Cr cathodes, respectively), substrate bias (–200 V) and substrate temperature (∼320 °C). The coatings were analyzed for their mechanical characteristics (hardness, adhesion) and tribological performance (friction, wear), along with their elemental and phase composition, chemical bonds, crystalline structure and cross-sectional morphology. The coatings were found to be formed with nano-scale composite structures consisting of carbide crystallites (grain size of 3.1–8.2 nm) and amorphous hydrogenated carbon. The experimental results showed significant differences between the two coating series, where the films formed from C2H2 exhibited markedly superior characteristics in terms of microstructure, morphology, hardness, friction behaviour and wear resistance. For the coatings prepared using CH4, the measured values of crystallite size, hardness, friction coefficient and wear rate were in the ranges of 7.2–8.2 nm, 26–30 GPa, 0.3–0.4 and 2.1–4.8 × 10−6 mm3 N−1 m−1, respectively, while for the coatings grown in C2H2, the values of these characteristics were found to be in the ranges of 3.1–3.7 nm, 41–45 GPa, 0.1–0.2 and 1.4–3.0 × 10−6 mm3 N−1 m−1, respectively. Among the investigated coatings, the one produced using C2H2 at the highest flow rate (130 sccm) exhibited the highest hardness (45.1 GPa), the lowest friction coefficient (0.10) and the best wear resistance (wear rate of 1.4 × 10−6 mm3 N−1 m−1).