We review our recent work on the anodization of InP in KOH electrolytes. The anodic oxidation processes are shown to be remarkably different in different concentrations of KOH. Anodization in 2 - 5 mol dm-3 KOH electrolytes results in the formation of porous InP layers but, under similar conditions in a 1 mol dm-3 KOH, no porous structure is evident. Rather, the InP electrode is covered with a thin, compact surface film at lower potentials and, at higher potentials, a highly porous surface film is formed which cracks on drying. Anodization of electrodes in 2 - 5 mol dm-3 KOH results in the formation of porous InP under both potential sweep and constant potential conditions. The porosity is estimated at ~65%. A thin layer (~ 30 nm) close to the surface appears to be unmodified. It is observed that this dense, near-surface layer is penetrated by a low density of pores which appear to connected it to the electrolyte. Well-defined oscillations are observed when InP is anodized in both the KOH and (NH4)2S. The charge per cycle remains constant at 0.32 C cm-2 in (NH4)2S but increases linearly with potential in KOH. Although the characteristics of the oscillations in the two systems differ, both show reproducible and well-behaved values of charge per cycle.

Relevância:

30.00% 30.00%

Publicador:

Resumo:

The observation of current oscillations under potential sweep conditions when an n-InP electrode is anodized in a KOH electrolyte is reported and compared to the oscillatory behavior noted during anodization in an (NH4)2S electrolyte. In both cases oscillations are observed above 1.7 V (SCE). The charge per cycle was found to increase linearly with potential for the InP/KOH system but was observed to be independent of potential for the InP/(NH4)2S system. The period of the oscillations in the InP/KOH was found to increase with applied potential. In this case the oscillations are asymmetrical and the rising and falling segments have a different dependence on potential. Although the exact mechanism is not yet know for either system, transmission electron microscopy studies show that in both cases, the electrode is covered by a thick porous film in the oscillatory region.