A comparative study of the structural, mechanical and tribological characteristics of TiSiC-Cr coatings prepared in CH4 and C2H2 reactive atmosphere by cathodic vacuum arc

TiSiC-Cr coatings, with Cr and Si as additional elements, were deposited on Si, C 45 and 316 L steel substrates via cathodic arc evaporation. Two series of coatings with thicknesses in the range of 3.6–3.9 μm were produced, using either CH4 or C2H2 as carbon containing gas. For each series, different coatings were prepared by varying the carbon rich gas flow rate between 90 and 130 sccm, while maintaining constant cathode currents (110 and 100 A at TiSi and Cr cathodes, respectively), substrate bias (–200 V) and substrate temperature (∼320 °C). The coatings were analyzed for their mechanical characteristics (hardness, adhesion) and tribological performance (friction, wear), along with their elemental and phase composition, chemical bonds, crystalline structure and cross-sectional morphology. The coatings were found to be formed with nano-scale composite structures consisting of carbide crystallites (grain size of 3.1–8.2 nm) and amorphous hydrogenated carbon. The experimental results showed significant differences between the two coating series, where the films formed from C2H2 exhibited markedly superior characteristics in terms of microstructure, morphology, hardness, friction behaviour and wear resistance. For the coatings prepared using CH4, the measured values of crystallite size, hardness, friction coefficient and wear rate were in the ranges of 7.2–8.2 nm, 26–30 GPa, 0.3–0.4 and 2.1–4.8 × 10−6 mm3 N−1 m−1, respectively, while for the coatings grown in C2H2, the values of these characteristics were found to be in the ranges of 3.1–3.7 nm, 41–45 GPa, 0.1–0.2 and 1.4–3.0 × 10−6 mm3 N−1 m−1, respectively. Among the investigated coatings, the one produced using C2H2 at the highest flow rate (130 sccm) exhibited the highest hardness (45.1 GPa), the lowest friction coefficient (0.10) and the best wear resistance (wear rate of 1.4 × 10−6 mm3 N−1 m−1).

Involvement of incipient hydrous oxide species in electrocatalysis at some metal electrode surfaces

In this thesis a novel theory of electrocatalysis at metal (especially noble metal)/solution interfaces was developed based on the assumption of metal adatom/incipient hydrous oxide cyclic redox transitions. Adatoms are considered as metastable, low coverage species that oxidise in-situ at potentials of often significantly cathodic to the regular metal/metal oxide transition. Because the adatom coverage is so low the electrochemical or spectroscopic response for oxidation is frequently overlooked; however, the product of such oxidation, referred to here as incipient hydrous oxide seems to be the important mediator in a wide variety of electrocatalytically demanding oxidation processes. Conversely, electrocatalytically demanding reductions apparently occur only at adatom sites at the metal/solution interface - such reactions generally occur only at potentials below, i.e. more cathodic than, the adatom/hydrous oxide transition. It was established that while silver in base oxidises in a regular manner (forming initially OHads species) at potentials above 1.0 V (RHE), there is a minor redox transition at much lower potentials, ca. o.35 v (RHE). The latter process is assumed to an adatom/hydrous oxide transition and the low coverage Ag(l) hydrous oxide (or hydroxide) species was shown to trigger or mediate the oxidation of aldehydes, e. g. HCHO. The results of a study of this system were shown to be in good agreement with a kinetic model based on the above assumptions; the similarity between this type of behaviour and enzyme-catalysed processes - both systems involve interfacial active sites - was pointed out. Similar behaviour was established for gold where both Au(l) and Au(lll) hydrous oxide mediators were shown to be the effective oxidants for different organic species. One of the most active electrocatalytic materials known at the present time is platinum. While the classical view of this high activity is based on the concept of activated chemisorption (and the important role of the latter is not discounted here) a vital role is attributed to the adatom/hydrous oxide transition. It was suggested that the well known intermediate (or anomalous) peak in the hydrogen region of the cyclic voltanmogram for platinum region is in fact due to an adatom/hydrous oxide transition. Using potential stepping procedures to minimise the effect of deactivating (COads) species, it was shown that the onset (anodic sweep) and termination (cathodic sweep) potential for the oxidation of a wide variety of organics coincided with the potential for the intermediate peak. The converse was also shown to apply; sluggish reduction reactions, that involve interaction with metal adatoms, occur at significant rates only in the region below the hydrous oxide/adatom transition.

Chemistry of B1- and B10- boranes containing halogen or pseudohalogen groups

The research described in this thesis involved the chemistry of borane-species which contain one or more halide or pseudohalide groups. Both monoboron species e.g. [BH3X]- and "cluster" borane species e.g. [B10H9X]2- and I-Se B11H10 were studied. The first chapter is a review of the syntheses, properties and reactions of halide and pseudohalide species containing from one to ten boron atoms. Chapter Two is a theoretical investigation of' the electronic and molecular structures of two series of boranes i. e. [BH3X]- and [B10H9X]2- where X = H, CI, CN, NCS, SCN and N3. The calculational method used was the Modified Neglect of Differential Overlap (MNDO) method of Dewar et al. The results were compared where possible with experimental results such as the X-ray crystallographically determined structures of [BH3CI]- and [B10H10]2-. Chapter Three concerns halogenated selenaborane clusters and reports an improved synthesis of 12-Br-SeB11H10 and the first structural data for a simple non-metal containing selenaborane cage with the X-ray crystallographically determined structure of 12-1-SeB11H10. Finally, an indepth n.m.r. study of Se2B9H9 is also reported together with attempts to halogenate this compound. The last two chapters are based on single boron systems. Chapter Four concerns the synthetic routes to amine-boranes and -cyanoboranes from [BH4]- and [BH3CN]- substrates. This chapter discusses some difficulties encountered when polyamines were used in these reactions. The characterisation of an unusual ketone isolated from some of these reactions, the X-ray crystallographically determined structure of 4-dimethylamino-pyridine-cyanoborane and a new route to pyrazabole dimeric species are also discussed. The final chapter reports on work carried out at producing BH2X (X = H, CN) adducts of aminophosphines. Three routes were attempted to generate P-B and N-B bonded species with varying degrees of success. Some unusual products of these reactions are discussed including [Ph2(O) PPPh2 ] [Ph2NH]2, the structure of which was determined by X-ray crystallography.

A study of the oxygen electrochemistry of ruthenium and iridium

This thesis is concerned with an investigation of the anodic behaviour of ruthenium and iridium in aqueous solution and particularly of oxygen evolution on these metals. The latter process is of major interest in the large-scale production of hydrogen gas by the electrolysis of water. The presence of low levels of ruthenium trichloride ca. 10-4 mol dm-3 in acid solution give a considerable increase in the rate of oxygen evolution from platinum and gold, but not graphite, anodes. The mechanism of this catalytic effect was investigated using potential step and a.c. impedance technique. Earlier suggestions that the effect is due to catalysis by metal ions in solution were proved to be incorrect and it was shown that ruthenium species were incorporated into the surface oxide film. Changes in the oxidation state of these ruthenium species is probably responsible for the lowering of the oxygen overvoltage. Both the theoretical and practical aspects of the reaction were complicated by the fact that at constant potential the rates of both the catalysed and the uncatalysed oxygen evolution processes exhibit an appreciable, continuous decrease with either time or degree of oxidation of the substrate. The anodic behaviour of iridium in the oxide layer region has been investigated using conventional electrochemical techniques such as cyclic voltammetry. Applying a triangular voltage sweep at 10 Hz, 0.01 to 1.50V increases the amount of electric charge which the surface can store in the oxide region. This activation effect and the mechanism of charge storage is discussed in terms of both an expanded lattice theory for oxide growth on noble metals and a more recent theory of irreversible oxide formation with subsequent stoichiometry changes. The lack of hysteresis between the anodic and cathodic peaks at ca. 0.9 V suggests that the process involved here is proton migration in a relatively thick surface layer, i.e. that the reaction involved is some type of oxide-hydroxide transition. Lack of chloride ion inhibition in the anodic region also supports the irreversible oxide formation theory; however, to account for the hydrogen region of the potential sweep a compromise theory involving partial reduction of the outer regions of iridium oxide film is proposed. The loss of charge storage capacity when the activated iridium surface is anodized for a short time above ca. 1.60 V is attributed to loss by corrosion of the outer active layer from the metal surface. The behaviour of iridium at higher anodic potentials in acid solution was investigated. Current-time curves at constant potential and Tafel plots suggested that a change in the mechanism of the oxygen evolution reaction occurs at ca. 1.8 V. Above this potential, corrosion of the metal occurred, giving rise to an absorbance in the visible spectrum of the electrolyte (λ max = 455 nm). It is suggested that the species involved was Ir(O2)2+. A similar investigation in the case of alkaline electrolyte gave no evidence for a change in mechanism at 1.8 V and corrosion of the iridium was not observed. Oxygen evolution overpotentials were much lower for iridium than for platinum in both acidic and alkaline solutions.

Grooming and hygienic behaviours of the honey bee (Apis mellifera) toward the parasitic mite Varroa destructor

Despite a multitude of environmental stressors, the Varroa mite is still regarded as the greatest cause of honey bee mortality in its invaded range. Breeding honey bees that are resistant to the mite is an important area of research. This thesis aimed to gain a better understanding of the grooming and hygienic behaviours of Russian honey bees (RHB). The effect of a break in the synchrony of a mite’s life cycle on reproductive success was tested through brood inoculation experiments. Mites released by hygienic behaviour and forced to enter a new cell are less likely to lay male offspring. Through laboratory cage assays it was found that daughter mites are more susceptible to grooming behaviour. A new method of marking Varroa mites was developed which would enable a single cohort of mites to be followed after inoculation. A strong brood removal trait was noticed in RHB colonies, therefore they were tested for Varroa sensitive hygienic (VSH) behaviour. RHB demonstrated levels of VSH as high as the USDA line bred specifically for this behaviour. In addition the same QTL found to be responsible for the trait in VSH bees, was associated with VSH in RHB stock. Previous work showed that the ratio of older mites to total trapped mites (O/T) in the debris of honey bee colonies demonstrated the strongest association with colony infestation. This research showed that O/T is associated with VSH and brood removal behaviour. In addition, bees that displayed high levels of VSH in this study were also more likely to spend a longer amount of time grooming in laboratory assays. This indicates that both grooming and hygienic behaviours play important roles in the resistance of RHB stock. Their likelihood to be expressed by other stocks is discussed and recommendations for further research are provided.