Efficient removal of paracetamol using LaCu1-xMxO3 (M=Mn, Ti) perovskites as heterogeneous Fenton-like catalysts

A series of perovskite-like oxides LaCu1-xMxO3 (M=Mn, Ti; 0.0 ⩽ x ⩽ 0.8) was prepared by amorphous citrate decomposition and characterized by XRD, ICP-OES and XPS techniques. The catalysts were tested in the Fenton-like degradation of paracetamol with H2O2, under mild reaction conditions, 25 °C and nearly neutral pH. Values of decomposition of paracetamol between 80 and 97% at 300 min were achieved for most of samples. The presence of the Cu2+/Cu+ pair at the surface of the catalysts is necessary to carry out the reaction and the catalysts containing higher amount of copper at the surface, resulted to be more active. The leaching of metals was less than 1%, which discards the contribution of the homogenous Fenton-like reaction and remarks the high stability of the metals into the mixed oxide network. The catalytic activity of LaCu0.8Mn0.2O3 was maintained after three cycles of reaction, which proves the stability and reusability of the catalyst.

Preparation of manganese oxide - graphite electrodes by electrophoretic deposition

Manganese oxide is a promising active material for supercapacitors (SCs) with pseudocapacitance due to its high capacitance and its environmentally friendly character. This paper deals with the preparation of electrodes for supercapacitors consisting of manganese oxide supported onto graphite by electrophoretic deposition. Manganese oxide powders were characterized and dispersed in water by controlling the colloidal and rheological behavior in order to obtain stable suspensions. Optimized manganese oxide suspensions were deposited onto graphite electrodes by electrophoretic deposition. The deposited mass per unit area in the electrodes was optimized by controlling the applied current density and the deposition time. It has been demonstrated that the introduction of a binder helped to improve the adherence to graphite; otherwise the deposit thickness obtained by EPD is limited and no films can be obtained by simply dipping. These conditions allowed us to obtain more homogeneous deposits with higher specific energy than without binder.