Modificação superficial de fibras de juta com descarga corona para melhora da aderência com matriz poliéster

Seeking alternatives for the total or partial substitution of synthetic fibers for natural fibers, with reinforcement in polymeric materials, this work was conducted with the objective of evaluating the treatment with corona discharge on the adherence of juta fibers with resin. The fibers were exposed to corona discharge for 1, 5, 10 and 15 minutes, as well as after treatment with hot water, molding composites fiber-reinforced with filaments treated for 10 and 15 minutes, and without the treatment. The chemical structures were evaluated by spectrometry in the region of Fourier transform infrared with attenuated total reflection (FTIR/ATR), observing the formation of a new band and the increase in the absorption of groupings with oxygen. The thermal analyses, such as thermogravimetry (TG) and differential scanning calorimetry (DSC) revealed the degradation of cellulose, hemicellulose and lignin. The microstructural characterization by scanning electron microscopy (SEM) showed changes in the surface of the fiber, such as roughness, superficial depressions, surface degradation and cavity formation. The adhesion of the fibers was evaluated by the pullout test, allowing us to verify the increase in adhesion strength after treatment with corona discharge. In conclusion, the treatment with corona discharge changes the surface of the juta fibers, resulting in better adherence with the resin.

Síntese e aplicação de catalisadores à base de óxidos de cério, tungstênio e HZSM-5 para a produção do biodiesel

This work presents a study on the production of biodiesel by esterification reaction of oleic acid with methanol using batch reactor and different catalysts based on CeO2 and WO3 and HZSM-5. Acid treatment was performed in order to increase the catalytic activity. Different characterization techniques were performed, among them X-ray diffraction (XRD), Thermogravimetric analysis TGA/DTA, Spectroscopy in the Region in Fourier Transform Infrared (FTIR) and X-ray fluorescence (XRF). The effects of independent variables: temperature, molar ratio of oil: alcohol and the amount of catalyst and their interactions on the dependent variable (conversion of oleic acid to the corresponding ester). Overall, through the results obtained in the characterization was observed that the applied treatments were efficient, however the XRF technique, indicated that tungsten oxide leaching could occur during the preparation of the materials. The treatments performed on HZSM-5 caused no significant changes in the structure indicating that the zeolite was quite resistant to the treatments used. It was evaluated using complete 23 factorial design. For the catalysts investigated, the best reaction conditions were obtained when using higher levels of the independent variables temperature and amount of catalyst. However, for the variable molar ratio the lowest level showed significant yields for most of the synthesized catalyst, obtaining maximum conversion to the OC (67.97%), OW (74.37%), HZSM-5 (61.16%) OC-OW 1 (75.93%), OC-OW 2 (82.57%), OC-OW 3 (79.15%), S/OC-OW 1 (86.90%), S/OC-OW 2 (91.04%), S/OC-OW 3 (88.60%), S/OC-OW/H 1 (92.34%), S/OC-OW/H 2 (100%) and S/OC-OW/H 3 (98.16%). According to the experimental design, the temperature has the biggest influence on the reaction variable for all the synthesized catalysts. Among the catalysts investigated S/OC-OW/H 2 e S/OC-OW/H 3 were more effective. Reuse tests showed that the catalyst activity decreased after each cycle, indicating that the regeneration process was effective. The leaching test indicated that the catalysts are heterogeneous in the evaluated operating range. The catalysts investigated showed themselves promising for the production of biodiesel.