In vitro analysis of the influence of surface treatment of dental implants on primary stability

Surface treatment interferes with the primary stability of dental implants because it promotes a chemical and micromorphological change on the surface and thus stimulates osseointegration. This study aimed to evaluate the effects of different surface treatments on primary stability by analyzing insertion torque (IT) and pullout force (PF). Eight samples of implants with different surface treatments (TS - external hexagon with acid surface treatment; and MS - external hexagon, machined surface), all 3.75 mm in diameter x 11.5 mm in length, were inserted into segments of artificial bones. The IT of each sample was measured by an electronic torquemeter, and then the pullout test was done with a universal testing machine. The results were subjected to ANOVA (p < 0.05), followed by Tukey's test (p < 0.05). The IT results showed no statistically significant difference, since the sizes of the implants used were very similar, and the bone used was not highly resistant. The PF values (N) were, respectively, TS = 403.75 +/- 189.80 and MS = 276.38 +/- 110.05. The implants were shown to be different in terms of the variables of maximum force (F = 4.401, p = 0.0120), elasticity in maximum flexion (F = 3.672, p = 0.024), and relative stiffness (F = 4.60, p = 0.01). In this study, external hexagonal implants with acid surface treatment showed the highest values of pullout strength and better stability, which provide greater indication for their use.

Evaluation of a nanometer roughness scale resorbable media-processed surface: a study in dogs

Objectives: This study compared the biomechanical fixation and bone-to-implant contact (BIC) of implants with different surfaces treatment (experimental resorbable blasting media-processed nanometer roughness scale surface, and control dual acid-etched) in a dog model. Material and methods: Surface characterization was made in six implants by means of scanning electron microscopic imaging, atomic force microscopy to evaluate roughness parameters, and X-ray photoelectron spectroscopy (XPS) for chemical assessment. The animal model comprised the bilateral placement of control (n = 24) and experimental surface (n = 24) implants along the proximal tibiae of six mongrel dogs, which remained in place for 2 or 4 weeks. Half of the specimens were biomechanically tested (torque), and the other half was subjected to histomorphologic/ morphometric evaluation. BIC and resistance to failure measures were each evaluated as a function of time and surface treatment in a mixed model ANOVA. Results: Surface texturing was significantly higher for the experimental compared with the control surface. The survey XPS spectra detected O, C, Al, and Ti at the control group, and Ca (similar to 0.2-0.9%) and P (similar to 1.7-4.1%) besides O, C, Al, and Ti at experimental surfaces. While no statistical difference in BIC was found between experimental and control surfaces or between 2 and 4 weeks in vivo, both longer time and use of experimental surface significantly increased resistance to failure. Conclusions: The experimental surface resulted in enhanced biomechanical fixation but comparable BIC relative to control, suggesting higher bone mechanical properties around the experimental implants.

Evaluation of Chemical Treatment on Zirconia Surface with Two Primer Agents and an Alkaline Solution on Bond Strength

Objectives: This study evaluated the effect of an alkaline solution and two 10-methacryloyloxydecyl dihydrogen phosphate (MDP)-based primer agents on bond strength to zirconia (yttria-stabilized tetragonal zirconium polycrystal [Y-TZP]) through the shear bond strength (SBS) test. Materials and Methods: Sixty square-shaped Y-TZP samples were embedded in an acrylic resin mold, polished, and randomly assigned to one of six groups (n=10) according to treatment surface: group CR, no treatment (control); group NaOH, 0.5 M NaOH; group AP, Alloy Primer; group ZP, Z-Primer Plus; group NaOH-AP, 0.5 M NaOH + Alloy Primer; and group NaOH-ZP, 0.5 M NaOH + Z-Primer Plus. The resin cement (Rely X U100) was applied inside a matrix directly onto the Y-TZP surface, and it was light-cured for 40 seconds. The samples were stored in distilled water at 37 C for 24 hours prior to the test, which was performed in a universal machine at a crosshead-speed of 0.5 mm/min. The data were analyzed by one-way analysis of variance and Tukey tests (p<0.05). Light stereomicroscopy and scanning electron microscopy were used to assess the surface topography and failure mode. Results: The SBS was significantly affected by the chemical treatment (p<0.0001). The AP group displayed the best results, and the use of NaOH did not improve SBS results relative to either AP or ZP. The samples treated with Alloy Primer displayed mainly mixed failures, whereas those conditioned with Z-Primer Plus or with 0.5 M NaOH presented a balanced distribution of adhesive and mixed failure modes. Conclusions: The use of a NaOH solution may have modified the reactivity of the Y-TZP surface, whereas the employment of a MDP/6-4-vinylbenzyl-n-propyl amino-1,3,5-triazine2,4-dithione-based primer enhanced the Y-TZP bond strength.

Surface treatment of dental porcelain with CO2 laser: porosity analysis and AFM.

The effect of CO2 continuous laser irradiation on the surface properties of veneering porcelains has already been tested. The surface observed after laser irradiation is similar to that achieved by auto-glaze in terms of roughness and color parameters (Sgura R, et al. Dental Materials 2011;27(Suppl. 1):e72–73). The purpose of this study was to analyze the surface porosity of porcelain discs after CO2 laser treatment and compare it to auto-glaze treatment, in furnace. A morphological analysis of the porcelain surface was conducted using atomic force microscopy (AFM) and conventional optical microscopy (OM).