Chemical and morphological features of nanofilled composite resin: Influence of finishing and polishing procedures and fluoride solutions

This study evaluated the influence of finishing and polishing procedures and different fluoride solutions on superficial morphology and chemistry of the nanofilled composite resin Supreme XT (3M) through the EDX analysis and SEM evaluation. Circular specimens (n = 30) of 10 mm diameter and 2 mm thickness were prepared, with half of the sample assays finished and polished with Super-Snap (R) sandpaper. The experimental groups were divided according to the presence or absence of finishing and polishing and solutions (artificial saliva, 0.05% of manipulated sodium fluoride solution, Fluordent Reach, Oral B, Fluorgard). Specimens were immersed in each respective solution for 1 min per day, during 60 days and stored in artificial saliva at 37 +/- 1 degrees C between immersion periods. Topography and chemical analysis was qualitative. It was observed that specimens submitted to finishing and polishing procedures had lower superficial degradation. Fluoride solutions promoted superficial alterations on specimens, being the highest degradation obtained with Fluordent Reach. It can be concluded that finishing and polishing procedures and the immersion media influence the superficial morphology of composite resin tested; the Fluordent Reach was the fluoride solution that most affected the material's surface. Microsc. Res. Tech. 2011., (c) 2011 Wiley Periodicals, Inc.

The filler content of the dental composite resins and their influence on different properties

The purpose of this study was to compare the inorganic content and morphology of one nanofilled and one nanohybrid composite with one universal microhybrid composite. The Vickers hardness, degree of conversion and scanning electron microscope of the materials light-cured using LED unit were also investigated. One nanofilled (Filtek (TM) Supreme XT), one nanohybrid (TPH (R) 3) and one universal microhybrid (Filtek (TM) Z-250) composite resins at color A2 were used in this study. The samples were made in a metallic mould (4 mm in diameter and 2 mm in thickness). Their filler weight content was measured by thermogravimetric analysis (TG). The morphology of the filler particles was determined using scanning electron microscope equipped with a field emission gun (SEM-FEG). Vickers hardness and degree of conversion using FT-IR spectroscopy were measured. Filtek (TM) Z-250 (microhybrid) composite resin shows higher degree of conversion and hardness than those of Filtek (TM) Supreme XT (nanofilled) and TPH (R) 3 (nanohybrid) composites, respectively. The TPH3 (R) (nanohybrid) composite exhibits by far the lowest mechanical property. Nanofilled composite resins show mechanical properties at least as good as those of universal hybrids and could thus be used for the same clinical indications as well as for anterior restorations due to their high aesthetic properties. Microsc. Res. Tech. 75:758765, 2012. (C) 2011 Wiley Periodicals, Inc

Judiciary as the last resort to protect children and adolescents: intersectoral actions, investment in human resources, and structuring of services

This study aimed to identify the work developed by the Judiciary to prevent sexual violence against children and adolescents within the family. The approach to social representations in a cultural perspective was used. The field study consisted in the 1st and 2nd Court of Crimes against Children and Adolescents, at the State Supreme Court of Pernambuco, Brazil. Participant observation, semi-structured interviews, and focus group with 17 subjects were the techniques for data collection, analyzed through the interpretation of meanings, allowing the identification of the category "The Judiciary as the ultimate level" and the following subcategories: "The public policies to prevent violence" and "The structure and dynamics of Courts". This study allows the visualization of the Judiciary's limitations with regard to the full protection and absolute priority, and that the work along with the victims demands investments in structure and human resources.

Influence of alloy microstructure on the microshear bond strength of basic alloys to a resin luting cement

The aim of this study was to evaluate the influence of microstructure and composition of basic alloys on their microshear bond strength (µSBS) to resin luting cement. The alloys used were: Supreme Cast-V (SC), Tilite Star (TS), Wiron 99 (W9), VeraBond II (VBII), VeraBond (VB), Remanium (RM) and IPS d.SIGN 30 (IPS). Five wax patterns (13mm in diameter and 4mm height) were invested, and cast in a centrifugal casting machine for each basic alloy. The specimens were embedded in resin, polished with a SiC paper and sandblasted. After cleaning the metal surfaces, six tygon tubes (0.5 mm height and 0.75 mm in diameter) were placed on each alloy surface, the resin cement (Panavia F) was inserted, and the excess was removed before light-curing. After storage (24 h/37°C), the specimens were subjected to µSBS testing (0.5 mm/min). The data were subjected to a one-way repeated measures analysis of variance and Turkey's test (α=0.05). After polishing, their microstructures were revealed with specific conditioners. The highest µSBS (mean/standard deviation in MPa) were observed in the alloys with dendritic structure, eutectic formation or precipitation: VB (30.6/1.7), TS (29.8/0.9), SC (30.6/1.7), with the exception of IPS (31.1/0.9) which showed high µSBS but no eutectic formation. The W9 (28.1/1.5), VBII (25.9/2.0) and RM (25.9/0.9) showed the lowest µSBS and no eutectic formation. It seems that alloys with eutectic formation provide the highest µSBS values when bonded to a light-cured resin luting cement.

Analysis of surface hardness of artificially aged resin composites

This study evaluated the effect of artificially accelerated aging (AAA) on the surface hardness of eight composite resins: Filtek Z250, Filtek Supreme, 4 Seasons, Herculite, P60, Tetric Ceram, Charisma, and Filtek Z100. Sixteen specimens were made from the test piece of each material, using an 8.0 × 2.0 mm teflon matrix. After 24 hours, eight specimens from each material were submitted to three surface hardness readings using a Shimadzu Microhardness Tester for 5 seconds at a load of 50 gf. The other eight specimens remained in the artificially accelerated aging machine for 382 hours and were submitted to the same surface hardness analysis. The means of each test specimen were submitted to the Kolmogorov-Smirnov test (p > 0.05), ANOVA and Tukey test (p < 0.05). With regard to hardness (F = 86.74, p < 0.0001) the analysis showed significant differences among the resin composite brands. But aging did not influence the hardness of any of the resin composites (F = 0.39, p = 0.53). In this study, there was interaction between the resin composite brand and the aging factors (F = 4.51, p < 0.0002). It was concluded that notwithstanding the type of resin, AAA did not influence surface hardness. However, with regard to hardness there was a significant difference among the resin brands.

Shear bond strength of nanofilled flowable resins used for indirect bracket bonding

AIM: To evaluate the bond strength of brackets fixed with different materials (two light-cured nanofilled resins - Transbond Supreme LV and Flow Tain LV, a light-cured resin - Transbond XT (control) and two chemically cured resins for indirect bonding - Sondhi Rapid- Set and Custom I.Q.) using the indirect bonding technique after 10 min and 24 h, and evaluate the type of failure. METHODS: One hundred premolars were selected and randomly divided into groups (n=10) according to the material and fixation period. The brackets were bonded through the indirect technique following the manufacturer's instructions and stored in deionized water at 37°C for 10 min or 24 h. After, the specimens were submitted to a shear bond strength (SBS) test (Instron) at 0.5 mm/min and evaluated for adhesive remnant index (ARI). The data were submitted to ANOVA and Tukey's test (p<0.05) and the ARI scores were submitted to the chi-square test. RESULTS: It could be observed a significant difference among the materials (Flow Tain LV = Transbond Supreme LV = Transbond XT> Sondhi Rapid-Set > Custom I.Q.). There was no significant difference in resistance values between 10 min and 24 h, regardless of the materials. Most groups showed adhesive remaining adhered to the enamel (scores 2 and 3) without statistically significant difference (p>0.05). CONCLUSIONS: It was concluded that the light-cured nanofilled materials used in indirect bonding showed greater resistance than the chemically cured materials. The period of fixation had no influence on the resistance for different materials.