Spectral Induced Polarization (SIP) signatures of clayey soils containing toluene

We performed laboratory experiments to investigate the sensitivity of the Spectral Induced Polarization (SIP) method to toluene contamination in clayey soils. We used mixtures of quartzitic sand and montmorillonite as soil samples, artificially contaminated with varying amounts of toluene. Care was taken to quantify the experimental uncertainty resulting from packing since such effects must be quantified if variations in SIP signatures between samples are to be reliably interpreted in terms of the effects of hydrocarbon concentration. The SIP response of all samples following addition of toluene was monitored for a period of 40 days following sample preparation. Stepwise regression was used to examine the statistical significance of correlations between (i) clay content and (ii) toluene concentration and SIP parameters. Both single-frequency real and imaginary conductivity measurements, along with the integral chargeability, normalized chargeability, DC conductivity and time constant obtained from a Debye decomposition fitting, were examined in this regression analysis. The SIP measurements show a clear time dependence following sample preparation, indicating that samples containing toluene may take significant time to reach an equilibrium electrical response. SIP measurements are significantly related to toluene content shortly after sample preparation, when the expected dependence of SIP on clay concentration is apparently suppressed. However, for the state of electrical equilibrium after 40 days (interpreted to indicate surface chemistry at equilibrium) there is no significant relation between SIP measurements and toluene content; instead SIP measurements are then significantly correlated with clay concentration. The total chargeability, normalized chargeability and relaxation time obtained from the Debye decomposition show no correlation with toluene content, indicating that this procedure, which likely integrates over multiple mechanisms, may not be suitable for understanding relationships between SIP and hydrocarbon contamination. We find only small low-frequency polarization signals observed in relation to toluene concentration (2 mrad at 0.01 Hz), which initially decreases the interfacial polarization. Unlike earlier works, our results do not support the use of the SIP method as a tool for monitoring toluene contamination in clay soils.

Langmuir and Langmuir-Blodgett films of a quinoline-fluorene based copolymer

The fabrication of Langmuir-Blodgett (LB) films of synthetic polymers allows the control of molecular architecture in order to optimize physical properties. In this paper, the surface chemistry of a quinoline-fluorene based copolymer spread on the air-water interface is investigated. Surface pressure-area isotherms as well as Polarization-Modulation Infrared Reflection-Absorption Spectroscopy (PM-IRRAS) were employed to characterize the films, which could be transferred to solid supports by the LB technique. Atomic force microscopy as well as UV-Vis and fluorescence spectroscopies have shown a regular deposition of the polymers, and the luminescence properties could be controlled with the number of layers deposited on the solid support. As a result, the photoluminescence of the LB films was considerably higher than that observed for the spin coated film, and the maximum emission peak was shifted to higher energies, which is attributed to the molecular-level interactions within the layer-ordered structure of the LB film. The luminescence response would possibly be tuned to approach the highest level, which allows the films to be employed in future applications in efficient optical devices such as organic light-emitting diodes (OLEDs). (C) 2011 Elsevier B.V. All rights reserved.

Evaluation of sun protection factor of cosmetic formulations by a simple visual in vitro method mimicking the in vivo method

A new concept for in vitro visual evaluation of sun protection factor (SPF) of cosmetic formulations based on a supramolecular ultraviolet (UV) dosimeter was clearly demonstrated. The method closely parallels the method validated for in vivo evaluation and relies on the determination of the slightest perceptible bleaching of an iron-complex dye/nanocrystallinetitanium dioxide interface (UV dosimeter) in combination with an artificial skin substrate simulating the actual human skin in the presence and absence of a cosmetic formulation. The successful evaluation of SPF was ensured by the similarity of the erythema response of our dosimeter and human skin to UV light irradiation. A good linear correlation of in vitro and in vivo data up to SPF 40 confirmed the effectiveness of such a simple, cheap, and fast method. In short, here we unravel a convenient and accessible visual FPS evaluation method that can help improving the control on cosmetic products contributing to the reduction of skin cancer, one of the critical public health issues nowadays. (C) 2011 Wiley Periodicals, Inc. and the American Pharmacists Association J Pharm Sci 101:726732, 2012

Toward the Optimization of an e-Tongue System Using Information Visualization: A Case Study with Perylene Tetracarboxylic Derivative Films in the Sensing Units

The wide variety of molecular architectures used in sensors and biosensors and the large amount of data generated with some principles of detection have motivated the use of computational methods, such as information visualization techniques, not only to handle the data but also to optimize sensing performance. In this study, we combine projection techniques with micro-Raman scattering and atomic force microscopy (AFM) to address critical issues related to practical applications of electronic tongues (e-tongues) based on impedance spectroscopy. Experimentally, we used sensing units made with thin films of a perylene derivative (AzoPTCD acronym), coating Pt interdigitated electrodes, to detect CuCl(2) (Cu(2+)), methylene blue (MB), and saccharose in aqueous solutions, which were selected due to their distinct molecular sizes and ionic character in solution. The AzoPTCD films were deposited from monolayers to 120 nm via Langmuir-Blodgett (LB) and physical vapor deposition (PVD) techniques. Because the main aspects investigated were how the interdigitated electrodes are coated by thin films (architecture on e-tongue) and the film thickness, we decided to employ the same material for all sensing units. The capacitance data were projected into a 2D plot using the force scheme method, from which we could infer that at low analyte concentrations the electrical response of the units was determined by the film thickness. Concentrations at 10 mu M or higher could be distinguished with thinner films tens of nanometers at most-which could withstand the impedance measurements, and without causing significant changes in the Raman signal for the AzoPTCD film-forming molecules. The sensitivity to the analytes appears to be related to adsorption on the film surface, as inferred from Raman spectroscopy data using MB as analyte and from the multidimensional projections. The analysis of the results presented may serve as a new route to select materials and molecular architectures for novel sensors and biosensors, in addition to suggesting ways to unravel the mechanisms behind the high sensitivity obtained in various sensors.

Synthesis of a functionalized europium complex and deposition of luminescent Langmuir-Blodgett (LB) films

The synthesis, characterization and formation of Langmuir-Blodgett (LB)films for the luminescent [(C12H25)(2)(CH3)(2)N][Eu(tta)(4)] complex, where [(C12H25)(2)(CH3)(2)](N+) is didodecyldimethylammonium and the tta ligand is thenoyltrifluoroacetone, are reported. The coordination of tta ligands to the Eu3+ ion was confirmed by FTIR spectroscopy and the emission spectrum comprised bands corresponding to D-5(0) -> F-7(0-4) transitions. The lifetime (tau) from the emission state (D-5(0))was 0.41 ms, measured by monitoring the hypersensitive D-5(0) -> F-7(2) transition, with the curve being fitted with a first-order exponential function. The surface pressure-area isotherm indicated that the anionic complex may form condensed structures at the air-water interface due to the amphiphilic properties of the counter ion and the beta-diketone ligand. Y-type LB films of [(C12H25)(2)(CH3)(2)N][Eu(tta)(4)] were deposited on quartz substrates, with preserved luminescence and a band assigned to the D-5(0) -> F-7(2) transition. The molecular arrangement at the air/water interface and the preserved luminescence in LB films are consistent with theoretical predictions using a semi-empirical Sparkle/AM1 calculation method for the molecule in vacuum. These tools were used for the first time to predict the behavior of organized films.

Changes in the surface of four calcium silicate-containing endodontic materials and an epoxy resin-based sealer after a solubility test

Aim To compare the changes in the surface structure and elemental distribution, as well as the percentage of ion release, of four calcium silicate-containing endodontic materials with a well-established epoxy resin-based sealer, submitted to a solubility test. Methodology Solubility of AH Plus, iRoot SP, MTA Fillapex, Sealapex and MTA-Angelus (MTA-A) was tested according to ANSI/ADA Specification 57. The deionized water used in the solubility test was submitted to atomic absorption spectrophotometry to determine and quantify Ca2+, Na+, K+, Zn2+, Ni2+ and Pb2+ ions release. In addition, the outer and inner surfaces of nonsubmitted and submitted samples of each material to the solubility test were analysed by means of scanning electron microscopy and energy-dispersive spectroscopy (SEM/EDX). Statistical analysis was performed by using one-way anova and Tukeys post hoc tests (a = 0.05). Results Solubility results, in percentage, sorted in an increasing order were -1.24 +/- 0.19 (MTA-A), 0.28 +/- 0.08 (AH Plus), 5.65 +/- 0.80 (Sealapex), 14.89 +/- 0.73 (MTA Fillapex) and 20.64 +/- 1.42 (iRoot SP). AH Plus and MTA-A were statistically similar (P > 0.05), but different from the other materials (P < 0.05). High levels of Ca2+ ion release were observed in all groups except AH Plus sealer. MTA-A also had the highest release of Na2+ and K+ ions. Zn+2 ion release was observed only with AH Plus and Sealapex sealers. After the solubility test, all surfaces had morphological changes. The loss of matrix was evident and the filler particles were more distinguishable. EDX analysis displayed high levels of calcium and carbon at the surface of Sealapex, MTA Fillapex and iRoot SP. Conclusions AH Plus and MTA-A were in accordance with ANSI/ADAs requirements regarding solubility whilst iRoot SP, MTA Fillapex and Sealapex did not fulfil ANSI/ADAs protocols. High levels of Ca2+ ion release were observed in all materials except AH Plus. SEM/EDX analysis revealed that all samples had morphological changes in both outer and inner surfaces after the solubility test. High levels of calcium and carbon were also observed at the surface of all materials except AH Plus and MTA-A.