Influence of Alloying Elements Upon the Solidification Interval of CA6NM Cast Martensitic Stainless Steel

The influence of different Cr and C contents upon the solidification interval of ASTM A352M-06 Grade CA6NM cast martensitic stainless steel has been investigated using computational thermodynamics, and checked against DTA measurements in samples taken from 13 large cast parts, in order to identify potential sources for improvement on the part castability. Calculation results suggest, indeed, that this would be the case for C: when its content increases from 0.018 to 0.044 wt.% C (within the allowed range in the alloy specification), the solidification intervals increases from 25 to 43 K, which suggests improved castability with decreasing C contents. DTA results, however, do not support this prediction, showing a fairly constant solidification interval around 23 K for all investigated samples. The results are discussed both regarding the impact in alloy processing and the fitness of the existing databases to reproduce experimental results in these limiting cases.

ANNEALING BEHAVIOR OF RAFM ODS-EUROFER STEEL

Oxide-dispersion-strengthened (ODS) ferritic-martensitic steels are candidates for applications in fusion power plants where micro structural long-term stability at temperatures of 650 degrees C to 700 degrees C are required. The microstructural stability of 80% cold-rolled reduced-activation ferritic-martensitic 9% Cr ODS-Eurofer steel was investigated within a wide range of temperatures (300 degrees C to 1350 degrees C). Fine oxide dispersion is very effective to prevent recrystallization in the ferritic phase field. The low recrystallized volume fraction (<0.1) found in samples annealed at 800 degrees C is associated with the nuclei found at prior grain boundaries and around coarse M23C6 particles. The combination of retarding effects such as Zener drag and concurrent recovery decrease the local stored energy and impede further growth of the recrystallization nuclei. Above 90 degrees C, martensitic transformation takes place with consequent coarsening. Significant changes in crystallographic texture are also reported.