Biogenic calcium phosphate transformation in soils over millennial time scales

Changes in bioavailability of phosphorus (P) during pedogenesis and ecosystem development have been shown for geogenic calcium phosphate (Ca-P). However, very little is known about long-term changes of biogenic Ca-P in soil. Long-term transformation characteristics of biogenic Ca-P were examined using anthropogenic soils along a chronosequence from centennial to millennial time scales. Phosphorus fractionation of Anthrosols resulted in overall consistency with the Walker and Syers model of geogenic Ca-P transformation during pedogenesis. The biogenic Ca-P (e.g., animal and fish bones) disappeared to 3% of total P within the first ca. 2,000 years of soil development. This change concurred with increases in P adsorbed on metal-oxides surfaces, organic P, and occluded P at different pedogenic time. Phosphorus K-edge X-ray absorption near-edge structure (XANES) spectroscopy revealed that the crystalline and therefore thermodynamically most stable biogenic Ca-P was transformed into more soluble forms of Ca-P over time. While crystalline hydroxyapatite (34% of total P) dominated Ca-P species after about 600-1,000 years, beta-tricalcium phosphate increased to 16% of total P after 900-1,100 years, after which both Ca-P species disappeared. Iron-associated P was observable concurrently with Ca-P disappearance. Soluble P and organic P determined by XANES maintained relatively constant (58-65%) across the time scale studied. Disappearance of crystalline biogenic Ca-P on a time scale of a few thousand years appears to be ten times faster than that of geogenic Ca-P.

Cytocompatibility of Porous Biphasic Calcium Phosphate Granules With Human Mesenchymal Cells by a Multiparametric Assay

This work aims to evaluate the cytocompatibility of injectable and moldable restorative biomaterials based on granules of dense or porous biphasic calcium phosphates (BCPs) with human primary mesenchymal cells, in order to validate them as tools for stem cell-induced bone regeneration. Porous hydroxyapatite (HA) and HA/beta-tricalcium phosphate (beta-TCP) (60: 40) granules were obtained by the addition of wax spheres and pressing at 20 MPa, while dense materials were compacted by pressing at 100 MPa, followed by thermal treatment (1100 degrees C), grinding, and sieving. Extracts were prepared by 24-h incubation of granules on culture media, with subsequent exposition of human primary mesenchymal cells. Three different cell viability parameters were evaluated on the same samples. Scanning electron microscopy analysis of the granules revealed distinct dense and porous surfaces. After cell exposition to extracts, no significant differences on mitochondrial activity (2,3-bis(2-methoxy-4-nitro-5-sulfophenly)-5-[(phenylamino) carbonyl]-2H-tetrazolium hydroxide) or cell density (Crystal Violet Dye Elution) were observed among groups. However, Neutral Red assay revealed that dense materials extracts induced lower levels of total viable cells to porous HA/beta-TCP (P < 0.01). Calcium ion content was also significantly lower on the extracts of dense samples. Porogenic treatments on BCP composites do not affect cytocompatibility, as measured by three different parameters, indicating that these ceramics are well suited for further studies on future bioengineering applications.

Use of rhBMP-2 to reconstruct a severely atrophic mandible: a modified approach

This study reports the case of a patient with a severely resorbed mandible who was treated without a bone graft, using short implants, internal rigid fixation, rhBMP-2 and beta-tricalcium phosphate. A 76-year-old woman, with a severely resorbed mandible (less than 3 mm), reported a history of nearly 25 years of complete edentulism and consecutive treatment failures, with total bilateral exposed inferior alveolar nerves and complete bone resorption of the inferior border in some areas. The treatment of choice was the placement of a 2.0 mm thick unilock bone plate (MatrixMandible, Synthes Maxillofacial, Paoli, PA, USA), to reinforce the mandible. Eight short implants with a regular platform (Nobel Biocare, Goteborg, Sweden) were placed: three on the external oblique line on both sides and two on the symphysis. In order to augment mandible height and coat the exposed thread of the anterior implants, rhBMP-2 (Infuse Bone, Meditronic Sofamor Danek, Memphis, TN, USA) and beta-tricalcium phosphate (Cerasorb; Curasan, Kleinostheim, Germany) were used. Four 1.3 mm L miniplates were placed to support the graft. 14 months after surgery, the patient was satisfied and had excellent function without complications.

A comparative thermoluminescence and electron spin resonance study of synthetic carbonated A-type hydroxyapatite

Intensity of the 150 degrees C thermoluminescence peak of beta-irradiated carbonated synthetic A-type hydroxyapatite is approximately 12 times higher than that of the noncarbonated material. Deconvolution of the glow curve showed that this peak is a result of a trap distribution. An attempt was made to relate this thermoluminescence peak enhanced by carbonation with the ESR signal of the CO2- radical in natural or synthetic hydroxyapatite. (C) 2011 Elsevier Ltd. All rights reserved.