Comparative degradation of ZnO- and SnO(2)-based polycrystalline non-ohmic devices by current pulse stress

The degradation behaviour of SnO(2)-based varistors (SCNCr) due to current pulses (8/20 mu s) is reported here for the first time in comparison with the ZnO-based commercial varistors (ZnO). Puncturing and/or cracking failures were observed in ZnO-based varistors possessing inferior thermo-mechanical properties in comparison with that found in a SCNCr system free of failures. Both systems presented electric degradation related to the increase in the leakage current and decrease in the electric breakdown field, non-linear coefficient and average value of the potential barrier height. However, it was found that a more severe degradation occurred in the ZnO-based varistors concerning their non-ohmic behaviour, while in the SCNCr system, a strong non-ohmic behaviour remained after the degradation. These results indicate that the degradation in the metal oxide varistors is controlled by a defect diffusion process whose rate depends on the mobility, the concentration of meta-stable defects and the amount of electrically active interfaces. The improved behaviour of the SCNCr system is then inferred to be associated with the higher amount of electrically active interfaces (85%) and to a higher energy necessary to activate the diffusion of the specific defects.

Investigation of the optical absorption of a magnetic colloid from the thermal to the electronic time-scale regime: measurement of the free-carrier absorption cross-section

The free-carrier absorption cross-section sigma of a magnetic colloid composed of magnetite nanoparticles dispersed in oil is obtained by using the Z-scan technique in different experimental conditions of the laser beam. We show that it is possible to obtain sigma with picosecond pulsed and millisecond chopped beams with pulse frequencies smaller than about 30 Hz. For higher pulse frequencies, the heating of the colloidal system triggers the appearance of the Soret effect. This effect artificially increases the value of sigma calculated from the experimental results. The limits of the different experimental setups are discussed. (C) 2012 Optical Society of America

Use of Carr-Purcell pulse sequence with low refocusing flip angle to measure T-1 and T-2 in a single experiment

The Carr-Purcell pulse sequence, with low refocusing flip angle, produces echoes midway between refocusing pulses that decay to a minimum value dependent on T*(2). When the refocusing flip angle was pi/2 (CP90) and tau > T*(2), the signal after the minimum value, increased to reach a steady-state free precession regime (SSFP), composed of a free induction decay signal after each pulse and an echo, before the next pulse. When tau < T*(2), the signal increased from the minimum value to the steady-state regime with a time constant (T*) = 2T(1)T(2)/(T-1 + T-2). identical to the time constant observed in the SSFP sequence, known as the continuous wave free precession (CWFP). The steady-state amplitude obtained with M-cp90 = M0T2/(T-1+T-2) was identical to CWFP. Therefore, this sequence was named CP-CWFP because it is a Carr-Purcell sequence that produces results similar to the CWFP. However, CP-CWFP is a better sequence for measuring the longitudinal and transverse relaxation times in single scan, when the sample exhibits T-1 similar to T-2. Therefore, this sequence can be a useful method in time domain NMR and can be widely used in the agriculture, food and petrochemical industries because those samples tend to have similar relaxation times in low magnetic fields. (C) 2011 Elsevier Inc. All rights reserved.