Processing and mechanical properties evaluation of glass fiber-reinforced PTFE laminates

A specific manufacturing process to obtain continuous glass fiber-reinforced RIFE laminates was studied and some of their mechanical properties were evaluated. Young's modulus and maximum strength were measured by three-point bending test and tensile test using the Digital Image Correlation (DIC) technique. Adhesion tests, thermal analysis and microscopy were used to evaluate the fiber-matrix adhesion, which is very dependent on the sintering time. The composite material obtained had a Young's modulus of 14.2 GPa and ultimate strength of 165 MPa, which corresponds to approximately 24 times the modulus and six times the ultimate strength of pure RIFE. These results show that the RIFE composite, manufactured under specific conditions, has great potential to provide structural parts with a performance suitable for application in structural components. (C) 2012 Elsevier Ltd. All rights reserved.

Natural fiber-reinforced thermoplastic starch composites obtained by melt processing

Thermoplastic starch (TPS) from industrial non-modified corn starch was obtained and reinforced with natural strands. The influence of the reinforcement on physical-chemical properties of the composites obtained by melt processing has been analyzed. For this purpose, composites reinforced with different amounts of either sisal or hemp strands have been prepared and evaluated in terms of crystallinity, water sorption, thermal and mechanical properties. The results showed that the incorporation of sisal or hemp strands caused an increase in the glass transition temperature (T-g) of the TPS as determined by DMTA. The reinforcement also increased the stiffness of the material, as reflected in both the storage modulus and the Young's modulus. Intrinsic mechanical properties of the reinforcing fibers showed a lower effect on the final mechanical properties of the materials than their homogeneity and distribution within the matrix. Additionally, the addition of a natural latex plasticizer to the composite decreased the water absorption kinetics without affecting significantly the thermal and mechanical properties of the material. (c) 2012 Elsevier Ltd. All rights reserved.

Effect of storage and processing of Brazilian flaxseed on lipid and lignan contents

Flaxseed has been widely studied around the world; its incorporation into products habitually consumed by human populations has been stimulated due to its unique nutritional value. The objective of this study was to evaluate the chemical composition of Brazilian flaxseed, to analyze the stability of lipids present in whole flaxseed flour (WFF) or partially defatted flaxseed flour (DFF) stored under several temperatures, and to investigate the effect of bread making on a product containing flaxseed. Whole flaxseed flour presented (g.100 g-1) 25.7 of insoluble fiber, 10.7 of soluble fiber, 38.9 of lipids, and 2.65 of lignan. Defatted flaxseed flour presented 65% less lipids, 36% more fiber and 56% more lignan than whole flaxseed flour. The fatty acid profile was maintained in the defatted flaxseed flour, and it presented a stable composition during storage under ambient temperature, refrigeration, and freezing. The fatty acid profile was similar in the bread containing defatted flaxseed flour after dough development, baking, and storage at room temperature or refrigerated. After baking, 89% of the lignan content was kept in bread. Results show that Brazilian flaxseed has an interesting chemical composition, and that defatted flaxseed, by-product of lipid extraction, presents a good stability to grind and storage under several temperatures. Thus, defatted flaxseed flour can be incorporated in bread, increasing its nutritional and functional value.