Subdivision of Hysteresis Loss in Mn-Zn Ferrite Toroidal Cores

The hysteresis loss subdivision method proved to be a strong tool to help in the analysis of different energy dissipation mechanisms along the quasi-static hysteresis loop measured on electrical steels. This paper used the samemethod to discuss the mechanisms involving the energy loss dissipation in Mn-Zn ferrite toroidal cores. The samples, sintered under controlled atmosphere in industrial conditions, were measured under triangular waveform excitation at very low frequency (5 mHz) and peak flux densities varying from 0.05 T to 0.45 T. The results show a different behavior between the low inductions hysteresis loss (WLI) and the high induction hysteresis loss (WHI) which proves the existence of different energy dissipation mechanisms affecting these loss components.

Magnetic Properties of Liquid-Phase Sintered CoFe2O4 for Application in Magnetoelastic and Magnetoelectric Transducers

Cobalt ferrite is a ferrimagnetic magnetostrictive ceramic that has potential application in magnetoelastic and magnetoelectric transducers. In this work, CoFe2O4 was obtained using a conventional ceramic method and Bi2O3 was used as additive in order to obtain liquid-phase sintered samples. Bi2O3 was added to the ferrite in amounts ranging from 0.25 mol% to 0.45 mol% and samples were sintered at 900 degrees C and 950 degrees C. It was observed the presence of Bi-containing particles in the microstructure of the sintered samples and the magnetostriction results indicated microstructural anisotropy. It was verified that it is possible to get dense cobalt ferrites, liquid-phase sintered, with relative densities higher than 90% and with magnetostriction values very close to samples sintered without additives.

Preparation and Structural Characterization of Vulcanized Natural Rubber Nanocomposites Containing Nickel-Zinc Ferrite Nanopowders

Single-phase polycrystalline mixed nickel-zinc ferrites belonging to Ni0.5Zn0.5Fe2O4 were prepared on a nanometric scale (mean crystallite size equal to 14.7 nm) by chemical synthesis named the modified poliol method. Ferrite nanopowder was then incorporated into a natural rubber matrix producing nanocomposites. The samples were investigated by means of infrared spectroscopy, X-ray diffraction, scanning electron microscopy and magnetic measurements. The obtained results suggest that the base concentration of nickel-zinc ferrite nanoparticles inside the polymer matrix volume greatly influences the magnetic properties of nanoconnposites. A small quantity of nanoparticles, less than 10 phr, in the nanocomposite is sufficient to produce a small alteration in the semi-crystallinity of nanocomposites observed by X-ray diffraction analysis and it produces a flexible magnetic composite material with a saturation magnetization, a coercivity field and an initial magnetic permeability equal to 3.08 emu/g, 99.22 Oe and 9.42 X 10(-5) respectively.