EFFECT OF THERMAL TREATMENT ON THE CHEMICAL CHARACTERISTICS OF WOOD FROM Eucalyptus grandis W. Hill ex Maiden UNDER DIFFERENT ATMOSPHERIC CONDITIONS

Thermal treatment (thermal rectification) is a process in which technological properties of wood are modified using thermal energy, the result of Which is often value-added wood. Thermally treated wood takes on similar color shades to tropical woods and offers considerable resistance to destructive microorganisms and climate action, in addition to having high dimensional stability and low hygroscopicity. Wood samples of Eucalyptus grandis were subjected to various thermal treatments, as performed in presence (140 degrees C; 160 degrees C; 180 degrees C) or in absence of oxygen (160 degrees C; 180 degrees C; 200 degrees C) inside a thermal treatment chamber, and then studied as to their chemical characteristics. Increasing the maximum treatment temperatures led to a reduction in the holocellulose content of samples as a result of the degradation and volatilization of hemicelluloses, also leading to an increase in the relative lignin content. Except for glucose, all monosaccharide levels were found to decrease in samples after the thermal treatment at a maximum temperature of 200 degrees C. The thermal treatment above 160 degrees C led to increased levels of total extractives in the wood samples, probably ascribed to the emergence of low molecular weight substances as a result of thermal degradation. Overall, it was not possible to clearly determine the effect of presence or absence of oxygen in the air during thermal treatment on the chemical characteristics of the relevant wood samples.

Alkaline sulfite/anthraquinone pretreatment followed by disk refining of Pinus radiata and Pinus caribaea wood chips for biochemical ethanol production

BACKGROUND: Alkaline sulfite/anthraquinone (ASA) cooking of Pinus radiata and Pinus caribaea wood chips followed by disk refining was used as a pretreatment for the production of low lignified and high fibrillated pulps. The pulps produced with different delignification degrees and refined at different energy inputs (250, 750 and 1600 Wh) were saccharified with cellulases and fermented to ethanol with Saccharomyces cerevisiae using separated hydrolysis and fermentation (SHF) or semi-simultaneous saccharification and fermentation (SSSF) processes. RESULTS: Delignification of ASA pulps was between 25% and 50%, with low glucans losses. Pulp yield was from 70 to 78% for pulps of P. radiata and 60% for the pulp of P. caribaea. Pulps obtained after refining were evaluated in assays of enzymatic hydrolysis. Glucans-to-glucose conversion varied from 20 to 70%, depending on the degree of delignification and fibrillation of the pulps. The best ASA pulp of P. radiata was used in SHF and SSSF experiments of ethanol production. Such experiments produced maximum ethanol concentration of 20 g L-1, which represented roughly90% of glucose conversion and an estimated amount of 260 L ethanol ton(-1) wood. P. caribaea pulp also presented good performance in the enzymatic hydrolysis and fermentation but, due to the low amount of cellulose present, only 140 L ethanol would be obtained from each ton of wood. CONCLUSION: ASA cooking followed by disk refining was shown to be an efficient pretreatment process, which generated a low lignified and high-fibrillated substrate that allowed the production of ethanol from the softwoods with high conversion yields. (C) 2012 Society of Chemical Industry

Effect of thermal treatment on the chemical characteristics of wood from Eucalyptus grandis W. Hill ex Maiden under different atmospheric conditions

Thermal treatment (thermal rectification) is a process in which technological properties of wood are modified using thermal energy, the result of which is often value-added wood. Thermally treated wood takes on similar color shades to tropical woods and offers considerable resistance to destructive microorganisms and climate action, in addition to having high dimensional stability and low hygroscopicity. Wood samples of Eucalyptus grandis were subjected to various thermal treatments, as performed in presence (140ºC; 160ºC; 180ºC) or in absence of oxygen (160ºC; 180ºC; 200ºC) inside a thermal treatment chamber, and then studied as to their chemical characteristics. Increasing the maximum treatment temperatures led to a reduction in the holocellulose content of samples as a result of the degradation and volatilization of hemicelluloses, also leading to an increase in the relative lignin content. Except for glucose, all monosaccharide levels were found to decrease in samples after the thermal treatment at a maximum temperature of 200ºC. The thermal treatment above 160ºC led to increased levels of total extractives in the wood samples, probably ascribed to the emergence of low molecular weight substances as a result of thermal degradation. Overall, it was not possible to clearly determine the effect of presence or absence of oxygen in the air during thermal treatment on the chemical characteristics of the relevant wood samples.