Hot metal desulfurization by marble waste and fluorspar

The objective of this paper is to present an analysis of the use of residual marble mixtures in the pig iron desulfurization process. The study involved the use of: marble waste, fluorspar, lime, and hot metal. Four mixtures were made and added to a liquid hot metal - with known chemical composition - at a temperature of 1450ºC. The mass of each element was calculated from its chemical analysis and compared with an industrial mixture. All of the four mixtures used in the experiments were stirred by a mechanical stirrer. Samples were collected by vacuum sampling for times of 5, 10, 15, 20, and 30 minutes, and analysis was performed to check sulfur variation in the bath with time. The results were analyzed and they verified that it was possible to use marble waste as a desulfurizer.

Caracterização de resíduos industriais visando a seu aproveitamento na fabricação de aço

Esse trabalho consiste na caracterização do resíduo de mármore, lama fina de aciaria e borra de alumínio, para averiguar a viabilidade técnica da utilização de tais resíduos na dessulfuração e desfosforação de ferro-gusa líquido. A caracterização desses resíduos foi feita através de análises químicas, granulométricas, difração de raios X e microscopia eletrônica de varredura (MEV) com micro análise por Espectroscopia por Energia Dispersiva de Raios X (EDS). A lama fina de aciaria apresenta um teor de FeO de 84,90%, o resíduo de mármore apresentou um teor de 61,5% de CaO e 33,9% de MgO e a borra de alumínio apresentou 36,5% de Al metálico e 62% de Al2O3. A granulometria do resíduo de mármore apresentou um tamanho de grão médio igual 42,810 µm. Já, na borra de alumínio, o tamanho médio foi de 101,803 µm. A lama fina de aciaria LD apresentou, em torno de 54,7% de sua granulometria, entre 0,15 e 0,075mm. Esses resultados apontam para a viabilidade técnica da utilização desses materiais na dessulfuração e desfosforação do ferro-gusa.