In the present study, the polycyclic aromatic hydrocarbon (PAH) genotoxicity was investigated in a one-step predator-prey relationship with the trophic-related marine species. Florida pompanos were fed for 5 and 10 days with pink shrimp post larvae previously exposed to benzo(a)pyrene (BaP) concentrations. Parent BaP body burden was measured in samples of Farfantepenaeus brasiliensis. BaP metabolites were determined in bile samples of Trachinotus carolinus and DNA damage was assessed through the comet and erythrocyte nuclear abnormalities (ENAs) assays in fish erythrocytes. BaP body burden increased significantly with the PAH concentration in pink shrimp PLs as well as the fish bile BaP metabolites. Both, comet and ENAs assays indicated significant increase on erythrocyte DNA damage of Florida pompanos fed with BaP-exposed pink shrimp on both feeding periods. The trophic route of BaP genotoxicity is discussed as well as the PAH biotransformation as the inducing mechanism for the DNA damages observed.

Assessment of cumulative damage by using ultrasonic C-scan on carbon fiber/epoxy composites under thermal cycling

In recent years, structural composites manufactured by carbon fiber/epoxy laminates have been employed in large scale in aircraft industries. These structures require high strength under severe temperature changes of -56° until 80 °C. Regarding this scenario, the aim of this research was to reproduce thermal stress in the laminate plate developed by temperature changes and tracking possible cumulative damages on the laminate using ultrasonic C-scan inspection. The evaluation was based on attenuation signals and the C-scan map of the composite plate. The carbon fiber/epoxy plain weave laminate underwent temperatures of -60° to 80 °C, kept during 10 minutes and repeated for 1000, 2000, 3000 and 4000 times. After 1000 cycles, the specimens were inspected by C-scanning. A few changes in the laminate were observed using the inspection methodology only in specimens cycled 3000 times, or so. According to the found results, the used temperature range did not present enough conditions to cumulative damage in this type of laminate, which is in agreement with the macro - and micromechanical theory.