Microwave Hydrothermal Synthesis and Photocatalytic Performance of ZnO and M:ZnO Nanostructures (M = V, Fe, Co)

ZnO and doped M:ZnO (M = V, Fe and Co) nanostructures were synthesized by microwave hydrothermal synthesis using a low temperature route without addition of any surfactant. The transition metal ions were successfully doped in small amount (3% mol) into ZnO structure. Analysis by X-ray diffraction reveals the formation of ZnO with the hexagonal (wurtzite-type) crystal structure for all the samples. The as-obtained samples showed a similar flower-like morphology except for Fe:ZnO samples, which presented a plate-like morphology. The photocatalytic performance for Rhodamine B (RhB) degradation confirmed that the photoactivity of M:ZnO nanostructures decreased for all dopants in structure, according to their eletronegativity. Photoluminescence spectroscopy was employed to correlate M:ZnO structure with its photocatalytical properties. It was suggested that transition metal ions in ZnO lattice introduce defects that act as trapping or recombination centers for photogenerated electrons and holes, making it impossible for them reach the surface and promote the photocatalytical process.

Synthesis of self-assembled tubes in direct conjugated porphyrin-gold nanohybrid solution

We report on the formation of self-assembled meso-tetrakis (p-sulfonatofenyl) porphyrin (H2 TPP'S POT. 4-''IND. 4') tubes stabilized by gold nanoparticles (NPs) in basic solution and on their spectroscopic chareterization. The role of the gold NPs in the aggregation dynamics of free-base sulfonated porphyrin (H2TPP'S POT. 4-''IND. 4') is also investigated. The direct conjugation of the gold NPs to the H2TPPS4 molecule quenches the fluorescence intensity, while absorption peaks are blue-shifted, indicating predominant H-type aggregation. It is observed that porphyrin molecules adsorbed on the surface of the gold NP interact and form tubes of maximum diameter ∼1.5 μm and length >100 μm. Steady-state and time-resolved spectroscopic techniques confirm nonradiative energy transfer from porphyrin to gold NP.

GREEN MACHINING ORIENTED TO DIMINISH DENSITY GRADIENT FOR MINIMIZATION OF DISTORTION IN ADVANCED CERAMICS

After sintering advanced ceramics, there are invariably distortions, caused in large part by the heterogeneous distribution of density gradients along the compacted piece. To correct distortions, machining is generally used to manufacture pieces within dimensional and geometric tolerances. Hence, narrow material removal limit conditions are applied, which minimize the generation of damage. Another alternative is machining the compacted piece before sintering, called the green ceramic stage, which allows machining without damage to mechanical strength. Since the greatest concentration of density gradients is located in the outer-most layers of the compacted piece, this study investigated the removal of different allowance values by means of green machining. The output variables are distortion after sintering, tool wear, cutting force, and the surface roughness of the green ceramics and the sintered ones. The following results have been noted: less distortion is verified in the sintered piece after 1mm allowance removal; and the higher the tool wear the worse the surface roughness of both green and sintered pieces.