Thermo and mechanical cycling and veneering method do not influence Y-TZP core/veneer interface bond strength

Objectives: The purpose of this study was to evaluate the influence of thermal and mechanical cycling and veneering technique on the shear bond strength of Y-TZP (yttrium oxide partially stabilized tetragonal zirconia polycrystal) core–veneer interfaces. Materials and methods: Cylindrical Y-TZP specimens were veneered either by layering (n = 20) or by pressing technique (n = 20). A metal ceramic group (CoCr) was used as control (n = 20). Ten specimens for each group were thermal and mechanical cycled and then all samples were subjected to shear bond strength in a universal testing machine with a 0.5 mm/min crosshead speed. Mean shear bond strength (MPa) was analysed with a 2-way analysis of variance and Tukey’s test ( p < 0.05). Failure mode was determined using stereomicroscopy and scanning electron microscopy (SEM). Results: Thermal and mechanical cycling had no influence on the shear bond strength for all groups. The CoCr group presented the highest bond strength value ( p < 0.05) (34.72 7.05 MPa). There was no significant difference between Y-TZP veneered by layering (22.46 2.08 MPa) or pressing (23.58 2.1 MPa) technique. Failure modes were predominantly adhesive for CoCr group, and cohesive within veneer for Y-TZP groups. Conclusions: Thermal and mechanical cycling, as well as the veneering technique does not affect Y-TZP core–veneer bond strength. Clinical significance: Different methods of veneering Y-TZP restorations would not influence the clinical performance of the core/veneer interfaces.

Residual stresses in Y-TZP crowns due to changes in the thermal contraction coefficient of veneers

Objective. To test the hypothesis that the difference in the coefficient of thermal contraction of the veneering porcelain above (˛liquid) and below (˛solid) its Tg plays an important role in stress development during a fast cooling protocol of Y-TZP crowns. Methods. Three-dimensional finite element models of veneered Y-TZP crowns were developed. Heat transfer analyses were conducted with two cooling protocols: slow (group A) and fast (groups B–F). Calculated temperatures as a function of time were used to determine the thermal stresses. Porcelain ˛solid was kept constant while its ˛liquid was varied, creating different ˛/˛solid conditions: 0, 1, 1.5, 2 and 3 (groups B–F, respectively). Maximum ( 1) and minimum ( 3) residual principal stress distributions in the porcelain layer were compared. Results. For the slowly cooled crown, positive 1 were observed in the porcelain, orientated perpendicular to the core–veneer interface (“radial” orientation). Simultaneously, negative 3 were observed within the porcelain, mostly in a hoop orientation (“hoop–arch”). For rapidly cooled crowns, stress patterns varied depending on ˛/˛solid ratios. For groups B and C, the patterns were similar to those found in group A for 1 (“radial”) and 3 (“hoop–arch”). For groups D–F, stress distribution changed significantly, with 1 forming a “hoop-arch” pattern while 3 developed a “radial” pattern. Significance. Hoop tensile stresses generated in the veneering layer during fast cooling protocols due to porcelain high ˛/˛solid ratio will facilitate flaw propagation from the surface toward the core, which negatively affects the potential clinical longevity of a crown.

Porcelain monolayers and porcelain/alumina bilayers reinforced by Al2O3/GdAlO3 fibers

Aim. This work tested the effect of the addition of Al2O3/GdAlO3 longitudinal fibers in different contents to veneering porcelain of two dental all ceramic systems. Methods: Fibers (0.5 mm diameter) obtained by the Laser Heated Pedestal Growth (LHPG) method were added to bar-shaped specimens made by veneer porcelain (monolayers) or both the veneer and the core ceramic (bilayers) of two all-ceramic systems: In-Ceram Alumina - glass infiltrated alumina composite (GIA) and In-Ceram 2000 AL Cubes - alumina polycrystal (AP) (VITA Zahnfabrik). The longitudinal fibers were added to veneering porcelain (VM7) in two different proportions: 10 or 17 vol%. The bars were divided into nine experimental conditions (n = 10) according to material used: VM7 porcelain monolayers, VM7/GIA, VM7/AP; and according to the amount of fibers within the porcelain layer: no fibers, 10 vol% or 17 vol%. After grinding and polishing the specimens were submitted to a three point bending test (crosshead speed = 0.5 mm/min) with porcelain positioned at tensile side. Data were analyzed by means of one-way ANOVA and a Tukey's test (alpha = 5%). Scanning electronic microscopy (SEM) was conducted for fractographic analysis. Results. Regarding the groups without fiber addition, VM7/AP showed the highest flexural strength (MPa), followed by VM7/GIA and VM7 monolayers. The addition of fibers led to a numerical increase in flexural strength for all groups. For VM7/GIA bilayers the addition of 17 vol% of fibers resulted in a significant 48% increase in the flexural strength compared to the control group. Fractographic analysis revealed that the crack initiation site was in porcelain at the tensile surface. Cracks also propagated between fibers before heading for the alumina core. Conclusions. The addition of 17 vol% of Al2O3/GdAlO3 longitudinal fibers to porcelain/glass infiltrated alumina bilayers significantly improved its flexural strength. 10 vol% or 17 vol% of fibers inclusion increased the flexural strength for all groups. (C) 2011 Elsevier Ltd. All rights reserved.

Clinical Performance of Porcelain Laminate Veneers: Outcomes of the Aesthetic Pre-evaluative Temporary (APT) Technique

This article evaluates the long-term clinical performance of porcelain laminate veneers bonded to teeth prepared with the use of an additive mock-up and aesthetic pre-evaluative temporary (APT) technique over a 12-year period. Sixty-six patients were restored with 580 porcelain laminate veneers. The technique, used for diagnosis, esthetic design, tooth preparation, and provisional restoration fabrication, was based on the APT protocol. The influence of several factors on the durability of veneers was analyzed according to pre- and postoperative parameters. With utilization of the APT restoration, over 80% of tooth preparations were confined to the dental enamel. Over 12 years, 42 laminate veneers failed, but when the preparations were limited to the enamel, the failure rate resulting from debonding and microleakage decreased to 0%. Porcelain laminate veneers presented a successful clinical performance in terms of marginal adaptation, discoloration, gingival recession, secondary caries, postoperative sensitivity, and satisfaction with restoration shade at the end of 12 years. The APT technique facilitated diagnosis, communication, and preparation, providing predictability for the restorative treatment. Limiting the preparation depth to the enamel surface significantly increases the performance of porcelain laminate veneers. (Int J Periodontics Restorative Dent 2012;32:625-635.)

Surface treatment of dental porcelain with CO2 laser: porosity analysis and AFM.

The effect of CO2 continuous laser irradiation on the surface properties of veneering porcelains has already been tested. The surface observed after laser irradiation is similar to that achieved by auto-glaze in terms of roughness and color parameters (Sgura R, et al. Dental Materials 2011;27(Suppl. 1):e72–73). The purpose of this study was to analyze the surface porosity of porcelain discs after CO2 laser treatment and compare it to auto-glaze treatment, in furnace. A morphological analysis of the porcelain surface was conducted using atomic force microscopy (AFM) and conventional optical microscopy (OM).