Film based on Y2O3: Eu3+ (5 mol% of Eu3+) for flat panel display

This paper reports on Y2O3:Eu3+ containing 1 mol% of Ag-0 nanoparticle films recovered with a SiO2 layer by using glass foil as a substrate for a possible optical display device application. The obtained film showed an intense emission at 612 nm due to the Eu3+ 5D0 -> F-7(2) hypersensitive transition, a high transmittance in that emission range, an excellent optical quality, and a high absorption only below 300 nm. Moreover, despite the presence of the SiO2 layer used to improve the phosphor adhesion on Corning (R) foil substrates, the intensity ratios between the emissions assigned to Eu3+ D-5(0) -> F-7(2) (dipole electric transition) and D-5(0) -> F-7(1) (dipole magnetic transition) were not affected by it. The x and y coordinate values found in the 1931 Commission Internationale de l'Eclairage Chromaticity Diagram for this film reveal that it has a suitable pure red color emission for optical displays devices. (C) 2012 Elsevier B. V. All rights reserved.

Diametral tensile strength and film thickness of an experimental dental luting agent derived from castor oil

The need to develop new dental luting agents in order to improve the success of treatments has greatly motivated research. Objective: The aim of this study was to evaluate the diametral tensile strength (DTS) and film thickness (FT) of an experimental dental luting agent derived from castor oil (COP) with or without addition of different quantities of filler (calcium carbonate - CaCO3). Material and Methods: Eighty specimens were manufactured (DTS N=40; FT N=40) and divided into 4 groups: Pure COP; COP 10%; COP 50% and zinc phosphate (control). The cements were mixed according to the manufacturers' recommendations and submitted to the tests. The DTS test was performed in the MTS 810 testing machine (10 KN, 0.5 mm/min). For FT test, the cements were sandwiched between two glass plates (2 cm(2)) and a load of 15 kg was applied vertically on the top of the specimen for 10 min. The data were analyzed by means of one-way ANOVA and Tukey's test (alpha=0.05). Results: The values of DTS (MPa) were: Pure COP- 10.94 +/- 1.30; COP 10%- 30.06 +/- 0.64; COP 50%- 29.87 +/- 0.27; zinc phosphate- 4.88 +/- 0.96. The values of FT (pm) were: Pure COP- 31.09 +/- 3.16; COP 10%- 17.05 +/- 4.83; COP 50%- 13.03 +/- 4.83; Zinc Phosphate- 20.00 +/- 0.12. One-way ANOVA showed statistically significant differences among the groups (DTS - p=1.01E-40; FT - p=2.4E-10). Conclusion: The experimental dental luting agent with 50% of filler showed the best diametral tensile strength and film thickness.