Alkaline sulfite/anthraquinone pretreatment followed by disk refining of Pinus radiata and Pinus caribaea wood chips for biochemical ethanol production

BACKGROUND: Alkaline sulfite/anthraquinone (ASA) cooking of Pinus radiata and Pinus caribaea wood chips followed by disk refining was used as a pretreatment for the production of low lignified and high fibrillated pulps. The pulps produced with different delignification degrees and refined at different energy inputs (250, 750 and 1600 Wh) were saccharified with cellulases and fermented to ethanol with Saccharomyces cerevisiae using separated hydrolysis and fermentation (SHF) or semi-simultaneous saccharification and fermentation (SSSF) processes. RESULTS: Delignification of ASA pulps was between 25% and 50%, with low glucans losses. Pulp yield was from 70 to 78% for pulps of P. radiata and 60% for the pulp of P. caribaea. Pulps obtained after refining were evaluated in assays of enzymatic hydrolysis. Glucans-to-glucose conversion varied from 20 to 70%, depending on the degree of delignification and fibrillation of the pulps. The best ASA pulp of P. radiata was used in SHF and SSSF experiments of ethanol production. Such experiments produced maximum ethanol concentration of 20 g L-1, which represented roughly90% of glucose conversion and an estimated amount of 260 L ethanol ton(-1) wood. P. caribaea pulp also presented good performance in the enzymatic hydrolysis and fermentation but, due to the low amount of cellulose present, only 140 L ethanol would be obtained from each ton of wood. CONCLUSION: ASA cooking followed by disk refining was shown to be an efficient pretreatment process, which generated a low lignified and high-fibrillated substrate that allowed the production of ethanol from the softwoods with high conversion yields. (C) 2012 Society of Chemical Industry

Grain size effect on the structural and dielectric properties of Pb0.85La0.15TiO3 ferroelectric ceramic compound

This paper presents a study of the influence of particle size on the structural and dielectric properties of Pb0.85La0.15TiO3 (PLT15) ferroelectric ceramic samples. The samples were prepared with average grain size of 1.69 +/- 0.08 mu m and 146 +/- 8 nm using, respectively, conventional and spark plasma sintering techniques. A decrease in the tetragonality degree as the crystallite size decreased was explained by an internal stress caused by the existence of a large amount of grain boundaries. The local structure exhibited no significant modification and the dielectric measurements showed a diffuse phase transition and a reduction in the permittivity magnitude at T-m as the average grain size decreased. The nanostructured ceramic sample prepared at a relatively lower temperature and sintering time presented a dielectric constant value of approximately 2000 at room temperature. (c) 2012 Elsevier Ltd and Techna Group S.r.l. All rights reserved.

Studying the genetic basis of drought tolerance in sorghum by managed stress trials and adjustments for phenological and plant height differences

Managed environments in the form of well watered and water stressed trials were performed to study the genetic basis of grain yield and stay green in sorghum with the objective of validating previously detected QTL. As variations in phenology and plant height may influence QTL detection for the target traits, QTL for flowering time and plant height were introduced as cofactors in QTL analyses for yield and stay green. All but one of the flowering time QTL were detected near yield and stay green QTL. Similar co-localization was observed for two plant height QTL. QTL analysis for yield, using flowering time/plant height cofactors, led to yield QTL on chromosomes 2, 3, 6, 8 and 10. For stay green, QTL on chromosomes 3, 4, 8 and 10 were not related to differences in flowering time/plant height. The physical positions for markers in QTL regions projected on the sorghum genome suggest that the previously detected plant height QTL, Sb-HT9-1, and Dw2, in addition to the maturity gene, Ma5, had a major confounding impact on the expression of yield and stay green QTL. Co-localization between an apparently novel stay green QTL and a yield QTL on chromosome 3 suggests there is potential for indirect selection based on stay green to improve drought tolerance in sorghum. Our QTL study was carried out with a moderately sized population and spanned a limited geographic range, but still the results strongly emphasize the necessity of corrections for phenology in QTL mapping for drought tolerance traits in sorghum.

Effect of pH-induced nanopowder deagglomeration on sintering, microstructure and dielectric properties of Ba0.77Ca0.23TiO3 ceramics

Ba0.77Ca0.23TiO3 ceramics were produced in this work starting from nanopowders synthesized via a polymeric precursor method. By adjusting the pH values of the precursor solutions above 7, it was possible to prepare powders weakly aggregated and with a smaller particle size, both facts which traduced into an enhanced nanopowders' sintering process at comparatively lower temperatures. Irrespective of the initial pH value, highly-dense and second phase-free ceramics were obtained following optimal sintering parameters (temperature and time) extracted from dilatometric and density measurements. By considering these and other sintering conditions, moreover, polycrystalline materials with an average grain size varying from 0.35 to 8 mm were produced, the grain growth process involving liquid phase-assisted sintering for heat treatments achieved at 1320 °C. The study of grain size effects on the ferroelectric properties of these materials was conducted, the results being discussed in the light of previous debates, including grain size-dependent degree of tetragonal distortion in such materials, as verified in this work.

Raman and XRD study on brookite-anatase coexistence in cathodic electrosynthesized titania

Among the many methods developed for the synthesis of titanium dioxide, cathodic electrosynthesis has not received much attention because the resulting amorphous oxy-hydroxide matrix demands a further thermal annealing step to be transformed into crystalline titania. However, the possibility of filling deep recessed templates by the control of the solidliquid interface makes it a potentially suitable technique for the fabrication of porous scaffolds for photovoltaics and photocatalysis. Furthermore, a careful control of the crystallization process enables the growth of larger grains with lower density of grain boundaries, which act as electron traps that slow down electronic transport and promote charge recombination. In this report, well crystallized titania deposits were obtained by thermal annealing of amorphous deposits fabricated by cathodically assisted electrosynthesis on indium-tin oxide (ITO)substrates. The combined use of Raman spectroscopy and X-ray diffraction showed that the crystallization process is more intricate than previously assumed. It is shown that the amorphous matrix evolves into a rutile-free mixture of brookite and anatase at temperatures as low as 200 degrees C that persists up to 800 degrees C, when pure anatase dominates. The amount of brookite in the brookiteanatase mixture reaches a maximum at 400 degrees C. This very simple method for obtaining a brookiteanatase mixture and the ability to tune their proportions by thermal annealing is a promising alternative whose potential for solar cells and photocatalysis deserves a careful evaluation. Copyright (C) 2011 John Wiley & Sons, Ltd.

Pb0.90Ba0.10Zr0.40Ti0.60O3 Nanostructured Ferroelectric Ceramics Prepared by Spark Plasma Sintering

Nanostructured Pb0.90Ba0.10Zr0.40Ti0.60O3 dense ceramics presenting an average grain size of 62 +/- 5 nm was prepared by the polymeric precursor method and using the spark plasma sintering technique. The dielectric permittivity curves versus temperature exhibit broad anomaly, indicative of a diffuse phase transition. This result can be explained by the spread of Curie temperatures which are expected to depend on the degree of tetragonality related to the grain size distribution. A pronounced decrease in the maximum of the dielectric permittivity value is attributed to the existence of a large amount of grain boundaries which are non-ferroelectric regions.

Laboratory and in situ studies on a compacted clayey silt fill

This paper presents laboratory and in situ studies carried out on a 200 000 m(3) large clayey silt compacted embankment. Laboratory studies carried out on undeformed block samples included index tests, strength tests and water retention curves using the filter paper technique. Grain size analyses with and without a deflocculating agent clearly showed the existence of grain clusters, which appear to be naturally formed. Field instrumentation installed at depths from 0.25 m to 1.0 m included tensiometers, equitensiometers, time domain reflectometry and geothermometers. Pluviometer data from a nearby weather station are also used to analyse the field data. The ranges of water content and suction values were measured, both of which correlated well with the pluviometer data. The water retention curves including laboratory and field data showed a bimodal shape, consistent with the presence of microand macropores shown in the grain size analysis.

Size-induced diffuse behavior in Pb0.89La0.11Zr0.40Ti0.60O3 nanocrystalline ferroelectric ceramics

The Pb1-xLaxZryTi1-yO3 system is a perovskite ABO(3) structured material which presents ferroelectric properties and has been used as capacitors, actuators, transducers and electro-optic devices. In this paper, we describe the synthesis and the characterization of Pb0.89La0.11Zr0.40Ti0.60O3 (PLZT11) nanostructured material. The precursor polymeric method and the spark plasma sintering technique were respectively used to prepare ceramic samples. In order to compare the effect of grain size, microcrystalline PLZT11 ceramic samples were also prepared. PLZT11 samples were characterized by X-ray diffraction technique which results show a reduction on the degree of tetragonality as the average grain size decreases. Moreover, the grain size decrease to a nanometer range induces a diffuse behavior on the dielectric permittivity curves as a function of the temperature and a reduction on the dielectric permittivity magnitude. Furthermore, the large number of grain boundaries due to the nanometer size gives rise to a dielectric anomaly. (C) 2012 Elsevier Masson SAS. All rights reserved.