Influence of artificial accelerated ageing on the colour stability of paints used for ocular prosthesis iris painting

Objectives: To evaluate the colour stability of paints used for ocular prosthesis iris painting submitted for accelerated artificial ageing (AAA). Materials and methods: Forty specimens of acrylic resin for sclera (16 x 2 mm) were made and separated into eight groups (n = 10) according to the type of paint (gouache, GP; oil, OP; acrylic AP; and composite resin for characterisation, CR) and the colours used (blue/brown). After drying (72 h), a new layer of colourless acrylic resin was applied and the initial colour readout was performed (Spectrophotometer PCB 6807). New colour readouts were performed after AAA, and Delta E was calculated. Results: Statistical analysis (two-way ANOVA-Bonferroni, p < 0.05) demonstrated that the brown colour showed lower Delta E means in comparison with the blue colour, with statistically significant difference for AP only. Blue colour showed no statistically significant difference with regard to the type of paint used. Brown AP showed lower Delta E than the other groups, with significant difference for OP and GP. GP showed greater alteration in Delta E for the brown colour, being statistically similar only to OP. Conclusions: Only the AP group for brown pigment shows clinically acceptable values for colour stability after AAA.

Color stability of modern composites subjected to different periods of accelerated artificial aging

The aim of this study was to evaluate the color stability of composites subjected to different periods of accelerated artificial aging (AAA). A polytetrafluorethylene matrix (10 x 2 mm) was used to fabricate 24 test specimens of three different composites (n=8): Tetric Ceram (Ivoclar/Vivadent); Filtek P90 and Z250 (3M ESPE), shade A3. After light activation for 20 s (FlashLite 1401), polishing and initial color readout (Spectrophotometer PCB 687; BYK Gardner), the test specimens were subjected to AAA (C-UV; Comexim), in 8-h cycles: 4 h exposure to UV-B rays at 50°C and 4 h condensation at 50°C. At the end of each cycle, color readouts were taken and the test ended when the mean value of ΔE attained a level ≥3.30. Tetric Ceram presented alteration in ΔE equal to 3.33 in the first aging cycle. For Filtek P90 and Z250, two (ΔE=3.60) and four (ΔE=3.42) AAA cycles were necessary. After each cycle, there was a reduction of luminosity in all the samples (ΔL). It was concluded that a short period of AAA was sufficient to promote clinically unacceptable color alteration in composites, and that this alteration was material-dependent.