Nanogravimetric study of lead underpotential deposition on selenium thin films as a semiconductor alloy formation procedure

An electrochemical quartz crystal microbalance Au electrode modified with a Se thin film was used to investigate the electrochemical behavior of lead ad-atoms using underpotential deposition (UPD) conditions. A specific quasi-reversible process was observed during the reduction of Pb2+ on Se thin films in perchloric acid media. The charge density of Pb ad-atoms on Se thin film (46.86 mu C cm(-2)) suggests a recovery of 0.1 monolayers, which is in good agreement with EQCM data. The Se thin film can be successfully alloyed with Pb atoms that are deposited by chronoamperometry using time intervals large enough to allow for diffusion toward the inner Se phase. Linear sweep voltammetry combined with EQCM in perchloric acid was used to characterize the amount of Pb absorbed in the Se thin film. These findings offer a new strategy for alloy formation in semiconductor films using UPD as an effective tool to quantify the exact amount of the incorporated metal.

Necrosis response to photodynamic therapy using light pulses in the femtosecond regime

One of the clinical limitations of the photodynamic therapy (PDT) is the reduced light penetration into biological tissues. Pulsed lasers may present advantages concerning photodynamic response when compared to continuous wave (CW) lasers operating under the same average power conditions. The aim of this study was to investigate PDT-induced response when using femtosecond laser (FSL) and a first-generation photosensitizer (Photogem) to evaluate the induced depth of necrosis. The in vitro photodegradation of the sensitizer was monitored during illumination either with CWor an FSL as an indirect measurement of the PDT response. Healthy liver of Wistar rats was used to evaluate the tissue response. The photosensitizer was endovenously injected and 30 min after, an energy dose of 150 Jcm-2 was delivered to the liver surface. We observed that the photodegradation rate evaluated via fluorescence spectroscopy was higher for the FSL illumination. The FSL-PDT produced a necrosis nearly twice as deep when compared to the CW-PDT. An increase of the tissue temperature during the application was measured and was not higher than 2.5 °C for the CW laser and not higher than 4.5 °C for the pulsed laser. FSL should be considered as an alternative in PDT applications for improving the results in the treatment of bulky tumors where higher light penetration is required.

The β to α phase transition of tantalum coatings deposited by modulated pulsed power magnetron sputtering

Tantalum coatings are of particular interest today as promising candidates to replace potentially hazardous electrodeposited chromium coatings for tribological and corrosion resistant applications, such as the internal lining on large-caliber gun barrels. Tantalum coatings have two crystalline phases, α-Ta (body-centered-cubic) and β-Ta (metastable tetragonal) that exhibit relatively different properties. Alpha-Ta is typically preferred for wear and corrosion resistant applications and unfortunately, is very difficult to deposit without the assistance of substrate heating or post-annealing treatments. Furthermore, there is no general consensus on the mechanism which causes α or β to form or if there is a phase transition or transformation from β → α during coating deposition. In this study, modulated pulsed power (MPP) magnetron sputtering was used to deposit tantalum coatings with thicknesses between 2 and 20 μm without external substrate heating. The MPP Ta coatings showed good adhesion and low residual stress. This study shows there is an abrupt β → α phase transition when the coating is 5–7 μm thick and not a total phase transformation. Thermocouple measurements reveal substrate temperature increases as a function of deposition time until reaching a saturation temperature of ~ 388 °C. The importance of substrate temperature evolution on the β → α phase transition is also explained.