Transparent UV-absorbers thin films of zinc oxide: Ceria system synthesized via sol-gel process

Transparent nanostructure ZnO:CeO2 and ZnO thin films to use as solar protector were prepared by non-alkoxide sol-gel process and deposited on boronsilicate glass substrate by dip-coating technique and then heated at 300-500 degrees C. The films were characterized structurally, morphologically and optically by X-ray diffraction (XRD), atomic force microscopy (AFM), field emission gun-scanning electron microscopy (FEG-SEM), scanning electron microscopy (SEM) and UV-Vis transmittance spectroscopy. The coatings presented high transparency in the visible region and excellent absorption in the UV. The band gap of the deposited films was estimated between 3.10 and 3.18 eV. Absorption of the films in the UV was increased by presence of cerium. The results suggest that the materials are promising candidates to use as coating solar protective. (C) 2012 Elsevier B.V. All rights reserved.

Mass loss and wear mechanisms of HVOF-sprayed multi-component white cast iron coatings

In this work, multi-component white cast iron was applied by HVOF thermal spray process as alternative to other manufacture processes. Effects of substrate type, substrate pre-heating and heat treatment of coating on mass loss have been determined by rubber wheel apparatus in accordance with ASTM G-65. Furthermore, influence of heat treatment of coating on wear mechanisms was also determined by scanning electron microscopy analysis. Heat-treated coatings presented mass loss three times lower than as-sprayed coatings. Furthermore, wear mechanisms of as-sprayed coating are micro-cutting associated with cracks close to unmelted particles and pores. In heat-treated coating, lesser mass loss is due to sintering. (C) 2011 Elsevier B.V. All rights reserved.

Structural and mechanical analysis for the optimization of PVD oxide coatings for protection against metal dusting

The evolution of the structure and properties of Cr/Cr oxide thin films deposited on HK40 steel substrates by reactive magnetron sputtering (RMS) was investigated and linked to their potential protective behavior against metal dusting. Deposition time, mode of oxygen feeding, and application of bias voltage were varied to assess their effect on the density, adhesion, and integrity of the films. All the films showed a very fine columnar microstructure and the presence of amorphous Cr oxide. Both, an increasing time and a constant oxygen flow during deposition led to the development of relatively low density films and mud-like cracking patterns. A graded oxygen flow resulted in films with fewer cracks, but a careful control of the oxygen flow is required to obtain films with a truly graded structure. The effect of the bias voltage was much more significant and beneficial. An increasing negative bias voltage resulted in the development of denser films with a transition to an almost crack-free structure and better adhesion. The amorphous oxide resulted in low values of hardness and Young's modulus. (C) 2012 Elsevier B.V. All rights reserved.