Application of an active attachment model as a high-throughput demineralization biofilm model

Objectives: To investigate the potential of an active attachment biofilm model as a highthroughput demineralization biofilm model for the evaluation of caries-preventive agents. Methods: Streptococcus mutans UA159 biofilms were grown on bovine dentine discs in a highthroughput active attachment model. Biofilms were first formed in a medium with high buffer capacity for 24 h and then subjected to various photodynamic therapies (PACT) using the combination of Light Emitting Diodes (LEDs, Biotable (R)) and Photogem (R). Viability of the biofilms was evaluated by plate counts. To investigate treatment effects on dentine lesion formation, the treated biofilms were grown in a medium with low buffer capacity for an additional 24 h. Integrated mineral loss (IML) and lesion depth (LD) were assessed by transversal microradiography. Calcium release in the biofilm medium was measured by atomic absorption spectroscopy. Results: Compared to the water treated control group, significant reduction in viability of S. mutans biofilms was observed when the combination of LEDs and Photogem (R) was applied. LEDs or Photogem (R) only did not result in biofilm viability changes. Similar outcomes were also found for dentine lesion formation. Significant lower IML and LD values were only found in the group subjected to the combined treatment of LEDs and Photogem (R). There was a good correlation between the calcium release data and the IML or LD values. Conclusions: The high-throughput active attachment biofilm model is applicable for evaluating novel caries-preventive agents on both biofilm and demineralization inhibition. PACT had a killing effect on 24 h S. mutans biofilms and could inhibit the demineralization process. (C) 2011 Elsevier Ltd. All rights reserved.

Impact of experimental Nano-HAP pastes on bovine enamel and dentin submitted to a pH cycling model

This in vitro study evaluated the preventive potential of experimental pastes containing 10% and 20% hydroxyapatite nanoparticles (Nano-HAP), with or without fluoride, on dental demineralization. Bovine enamel (n=15) and root dentin (n=15) specimens were divided into 9 groups according to their surface hardness: control (without treatment), 20 Nanop paste (20% HAP), 20 Nanop paste plus (20% HAP + 0.2% NaF), 10 Nanop paste (10% HAP), 10 Nanop paste plus (10% HAP + 0.2% NaF), placebo paste (without fluoride and HAP), fluoride paste (0.2% NaF), MI paste (CPP-ACP, casein phosphopeptide-amorphous calcium phosphate), and MI paste plus (CPP-ACP + 0.2% NaF). Both MI pastes were included as commercial control products containing calcium phosphate. The specimens were treated with the pastes twice a day (1 min), before and after demineralization. The specimens were subjected to a pH-cycling model (demineralization–6-8 h/ remineralization-16-18 h a day) for 7 days. The dental subsurface demineralization was analyzed using cross-sectional hardness (kgf/mm 2 , depth 10-220 µm). Data were tested using repeated-measures two-way ANOVA and Bonferroni's test (p<0.05). The only treatment able to reduce the loss of enamel and dentin subsurface hardness was fluoride paste (0.2% NaF), which differed significantly from the control at 30- and 50-µm depth (p<0.0001). The other treatments were not different from each other or compared with the control. The experimental Nanop pastes, regardless of the addition of fluoride, were unable to reduce dental demineralization in vitro.