Pore size regulates cell and tissue interactions with PLGA-CaP scaffolds used for bone engineering

A common subject in bone tissue engineering is the need for porous scaffolds to support cell and tissue interactions aiming at repairing bone tissue. As poly(lactide-co-glycolide)calcium phosphate (PLGACaP) scaffolds can be manufactured with different pore sizes, the aim of this study was to evaluate the effect of pore diameter on osteoblastic cell responses and bone tissue formation. Scaffolds were prepared with 85% porosity, with pore diameters in the ranges 470590, 590850 and 8501200 mu m. Rat bone marrow stem cells differentiated into osteoblasts were cultured on the scaffolds for up to 10 days to evaluate cell growth, alkaline phosphatase (ALP) activity and the gene expression of the osteoblast markers RUNX2, OSX, COL, MSX2, ALP, OC and BSP by real-time PCR. Scaffolds were implanted in critical size rat calvarial defects for 2, 4, and 8 weeks for histomorphometric analysis. Cell growth and ALP activity were not affected by the pore size; however, there was an increase in the gene expression of osteoblastic markers with the increase in the pore sizes. At 2 weeks all scaffolds displayed a similar amount of bone and blood vessels formation. At 4 and 8 weeks much more bone formation and an increased number of blood vessels were observed in scaffolds with pores of 470590 mu m. These results show that PLGACaP is a promising biomaterial for bone engineering. However, ideally, combinations of larger (similar to 1000 mu m) and smaller (similar to 500 mu m) pores in a single scaffold would optimize cellular and tissue responses during bone healing. Copyright (C) 2011 John Wiley & Sons, Ltd.

The influence of pore size on osteoblast phenotype expression in cultures grown on porous titanium

This study investigated the effect of pore size on osteoblastic phenotype development in cultures grown on porous titanium (Ti). Porous Ti discs with three different pore sizes, 312 mu m (Ti 312), 130 mu m (Ti 130) and 62 mu m (Ti 62) were fabricated using a powder metallurgy process. Osteoblastic cells obtained from human alveolar bone were cultured on porous Ti samples for periods of up to 14 days. Cell proliferation was affected by pore size at day 3 (p = 0.0010), day 7 (p = 0.0005) and day 10 (p = 0.0090) in the following way: Ti 62 < Ti 130 < Ti 312. Gene expression of bone markers evaluated at 14 days was affected, RUNX2 (p = 0.0153), ALP (p = 0.0153), BSP (p = 0.0156), COL (p = 0.0156), and OPN (p = 0.0156) by pore size as follows: Ti 312 < Ti 130 < Ti 62. Based on these results, the authors suggest that porous Ti surfaces with pore sizes near 62 mu m, compared with those of 312 mu m and 130 mu m, yield the highest expression of osteoblast phenotype as indicated by the lower cell proliferation rate and higher gene expression of bone markers.

Investigation of the pore blockage of a Brazilian dolomite during the sulfation reaction

The influence of the temperature and reaction time on the sulfation process of a dolomite is investigated in this paper. The sulfation effectiveness was evaluated and correlated with changes in the physical characteristics of a Brazilian dolomite during the reactive process. Calcination and sulfation experiments were performed under isothermal conditions for dolomite samples with average particle sizes of 545 mu m at temperatures of 750 degrees C, 850 degrees C and 950 degrees C at different times of sulfation. Thermogravimetric tests were applied to establish the reactivity variation of the dolomite in function of the time in the sulfation reaction and evaluate the methodology of the samples preparation. Porosimetry tests were performed to study the pore blockage of dolomite during the sulfation reaction. The highest values of BET surface area were 25.55 m(2)/g, 29.55 m(2)/g and 12.62 m(2)/g for calcined samples and after their sulfation processes, conversions of 51.5%, 61.9% and 42.8% were obtained at 750 degrees C, 850 degrees C and 950 degrees C, respectively. Considering the process as a whole, the best fit was provided by a first-order exponential decay equation. Moreover, the results have shown that it is possible to quantify the decreasing in the dolomite reactivity for sulfur dioxide sorption and understand the changes in the behavior of the sulfation process of limestones when applied to technologies, as fluidized bed combustor, in which sulfur dioxide is present. (C) 2011 Elsevier B. V. All rights reserved.