Effect of pH-induced nanopowder deagglomeration on sintering, microstructure and dielectric properties of Ba0.77Ca0.23TiO3 ceramics

Ba0.77Ca0.23TiO3 ceramics were produced in this work starting from nanopowders synthesized via a polymeric precursor method. By adjusting the pH values of the precursor solutions above 7, it was possible to prepare powders weakly aggregated and with a smaller particle size, both facts which traduced into an enhanced nanopowders' sintering process at comparatively lower temperatures. Irrespective of the initial pH value, highly-dense and second phase-free ceramics were obtained following optimal sintering parameters (temperature and time) extracted from dilatometric and density measurements. By considering these and other sintering conditions, moreover, polycrystalline materials with an average grain size varying from 0.35 to 8 mm were produced, the grain growth process involving liquid phase-assisted sintering for heat treatments achieved at 1320 °C. The study of grain size effects on the ferroelectric properties of these materials was conducted, the results being discussed in the light of previous debates, including grain size-dependent degree of tetragonal distortion in such materials, as verified in this work.

Comparative study on structure and magnetic properties of polycrystalline PrxY1-xBa2Cu3O7-delta prepared in oxygen and argon atmosphere

We report a systematic study on the influence of the synthesis routes on the structural and magnetic properties of polycrystalline PrxY1-xBa2Cu3O7-delta. We have prepared high-quality samples of this material by following a sol-gel method based on heat treatment in both inert argon and oxygen atmospheres in order to compare their effect on the formation of the superconducting phase using X-ray powder diffraction. Magnetic measurements (DC and AC susceptibility) clearly demonstrate that, for the same concentration of Pr, the superconducting transition temperature markedly increases in all samples prepared in argon atmosphere, including pure Pr-123. (C) 2012 Elsevier B.V. All rights reserved.