Enhancement of Electrical Conductivity in Plasticized Chitosan Based Membranes

Plasticized natural macromolecules-based polymer electrolyte samples were prepared and characterized. The plasticization of chitosonium acetate with glycerol increased the ionic conductivity value from 3.0 x 10(-7) S/cm to 1.1 x 10(-5) S/cm. The conductivity temperature relationship of the samples exhibits either VTF or Arrhenius type depending on the glycerol concentration in the sample. The dielectric studies evidencing the relaxation process in the plasticized sample at low frequency region are due to the electric polarization effect. Moreover, the samples were transparent in the Vis region, showed thermal stability up to 160 degrees C and good surface uniformity.

Effect of sorbitan-based surfactants on glass transition temperature of cellulose esters

Thermal behavior of mixtures composed of cellulose acetate butyrate (CAB), carboxymethylcellulose acetate butyrate (CMCAB), or cellulose acetate phthalate (CAPh), and sorbitan-based surfactants was investigated as a function of mixture composition by means of differential scanning calorimetry (DSC). Surfactants with three different alkyl chain lengths, namely, polyoxyethylenesorbitan monolaurate (Tween 20), polyoxyethylenesorbitan monopalmitate (Tween 40), and polyoxyethylene sorbitan monostearate (Tween 60) were chosen. DSC measurements revealed that Tween 20, 40, and 60 act as plasticizers for CAB, CMCAB, and CAPh (except for Tween 60), leading to a dramatic reduction of glass transition temperature (T-g). The dependence of experimental T-g values on the mixture composition was compared with theoretical predictions using the Fox equation. Plasticization was strongly dependent on mixture composition, surfactant hydrophobic chain length, and type of cellulose ester functional group.