4 resultados para Organic matrix
em Biblioteca Digital da Produção Intelectual da Universidade de São Paulo
Resumo:
This proof-of-concept study assessed whether the reduction of the degradation of the demineralized organic matrix (DOM) by pre-treatment with protease inhibitors (PI) is effective against dentin matrix loss. Bovine dentin slices were demineralized with 0.87 M citric acid, pH 2.3, for 36 hrs. In sequence, specimens were treated or not (UT, untreated) for 1 min with gels containing epigallocatechin 3-gallate (EGCG, 400 A mu M), chlorhexidine (CHX, 0.012%), FeSO4 (1 mM), NaF (1.23%), or no active compound (P, placebo). Specimens were then stored in artificial saliva (5 days, 37 degrees C) with the addition of collagenase (Clostridium histolyticum, 100 U/mL). We analyzed collagen degradation by assaying hydroxyproline (HYP) in the incubation solutions (n = 5) and evaluated the dentin matrix loss by profilometry (n = 12). Data were analyzed by ANOVA and Tukey's test (p < 0.05). Treatment with gels containing EGCG, CHX, or FeSO4 led to significantly lower HYP concentrations in solution and dentin matrix loss when compared with the other treatments. These results strongly suggest that the preventive effects of the PI tested against dentin erosion are due to their ability to reduce the degradation of the DOM.
Resumo:
Iron has been suggested to reduce the erosive potential of cola drinks in vitro. Objective: The aim of this study was to evaluate in situ the effect of ferrous sulfate supplementation on the inhibition of the erosion caused by a cola drink. Material and Methods: Ten adult volunteers participated in a crossover protocol conducted in two phases of 5 days, separated by a washout period of 7 days. In each phase, they wore palatal devices containing two human enamel and two human dentin blocks. The volunteers immersed the devices for 5 min in 150 mL of cola drink (Coca-Cola (TM), pH 2.6), containing ferrous sulfate (10 mmol/L) or not (control), 4 times per day. The effect of ferrous sulfate on the inhibition of erosion was evaluated by profilometry (wear). Data were analyzed by paired t tests (p<0.05). Results: The mean wear (+/- se) was significantly reduced in the presence of ferrous sulfate, both for enamel (control: 5.8 +/- 1.0 mu m; ferrous sulfate: 2.8 +/- 0.6 mu m) and dentin (control: 4.8 +/- 0.8 mu m; ferrous sulfate: 1.7 +/- 0.7 mu m). Conclusions: The supplementation of cola drinks with ferrous sulfate can be a good alternative for the reduction of their erosive potential. Additional studies should be done to test if lower ferrous sulfate concentrations can also have a protective effect as well as the combination of ferrous sulfate with other ions.
Resumo:
Objectives. This in vitro study aimed to analyze the effect of TiF4 compared to NaF varnishes and solutions, to protect against dentin erosion associated with abrasion. Materials and methods. Bovine dentin specimens were pre-treated with NaF-Duraphat (2.26% F), NaF/CaF2-Duofluorid (5.63% F), experimental-NaF (2.45% F), experimental-TiF4 (2.45% F) and placebo varnishes; NaF (2.26% F) and TiF4 (2.45% F) solutions. Controls remained untreated. The erosive pH cycling was performed using a soft drink (pH 2.6) 4 x 90 s/day and the toothbrushing-abrasion 2 x 10 s/day, in vitro for 5 days. Between the challenges, the specimens were exposed to artificial saliva. Dentin tissue loss was measured profilometrically (mu m). Results. ANOVA/Tukey's test showed that all fluoridated varnishes (Duraphat, 7.5 +/- 1.1; Duofluorid, 6.8 +/- 1.1; NaF, 7.2 +/- 1.9; TiF4, 6.5 +/- 1.0) were able to significantly reduce dentin tissue loss (40.7% reduction compared to control) when compared to placebo varnish (11.2 +/- 1.3), control (11.8 +/- 1.7) and fluoridated (NaF, 9.9 +/- 1.8; TiF4, 10.3 +/- 2.1) solutions (p < 0.0001), which in turn did not significantly differ from each other. Conclusion. All fluoridated varnishes, but not the solutions, had a similar performance and a good potential to reduce dentin tissue loss under mild erosive and abrasive conditions in vitro. Risk patients for erosion and abrasion, especially those with exposed dentin, should benefit from this clinical preventive measure. Further research has to confirm this promising result in the clinical situation.
Resumo:
This study aimed to evaluate the chemical interaction of collagen with some substances usually applied in dental treatments to increase the durability of adhesive restorations to dentin. Initially, the similarity between human dentin collagen and type I collagen obtained from commercial bovine membranes of Achilles deep tendon was compared by the Attenuated Total Reflectance technique of Fourier Transform Infrared (ATR-FTIR) spectroscopy. Finally, the effects of application of 35% phosphoric acid, 0.1M ethylenediaminetetraacetic acid (EDTA), 2% chlorhexidine, and 6.5% proanthocyanidin solution on microstructure of collagen and in the integrity of its triple helix were also evaluated by ATR-FTIR. It was observed that the commercial type I collagen can be used as an efficient substitute for demineralized human dentin in studies that use spectroscopy analysis. The 35% phosphoric acid significantly altered the organic content of amides, proline and hydroxyproline of type I collagen. The surface treatment with 0.1M EDTA, 2% chlorhexidine, or 6.5% proanthocyanidin did not promote deleterious structural changes to the collagen triple helix. The application of 6.5% proanthocyanidin on collagen promoted hydrogen bond formation. (c) 2012 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater, 2012.