Influence of the substitutional solute on the mechanical properties of Ti-Nb binary alloys for biomedical use

Titanium alloys are widely used in the manufacture of biomedical implants because they possess an excellent combination of physical properties and outstanding biocompatibility. Today, the most widely used alloy is Ti-6Al-4V, but some studies have reported adverse effects with the long-term presence of Al and V in the body, without mentioning that the elasticity modulus value of this alloy is far superior to the bone. Thus, there is a need to develop new Ti-based alloys without Al and V that have a lower modulus, greater biocompatibility, and similar mechanical strength. In this paper, we investigated the effect of Nb as a substitutional solute on the mechanical properties of Ti-Nb alloys, prepared in an arc-melting furnace and characterized by density, X-ray diffraction, optical microscopy, hardness and elasticity modulus measurements. The X-ray and microscopy measurements show a predominance of the α phase. The microhardness values showed a tendency to increase with the concentration of niobium in the alloy. Regarding the elasticity modulus, it was observed a nonlinear behavior with respect to the concentration of niobium. This behavior is associated with the presence of the α phase.

The influence of B4C and MgB2 additions on the behavior of MgO-C bricks

Carbon-containing refractory materials have received great attention over the last years due to their importance in the steelmaking process. The oxidation of carbon present in refractory materials at temperatures above 500 degrees C is usually accompanied by the decrease of their mechanical strength and chemical resistance. Aiming to improve the oxidation resistance of carbon-oxide refractories, the use of materials known as antioxidants has been extensively studied. In this work we evaluated the performance of MgB2 and B4C antioxidants when incorporated into MgO-C bricks. We observed that the co-addition of metallic antioxidants and B4C or MgB2 leads to refractory bricks with enhanced hot modulus of rupture and resistance against oxidation and slag corrosion. However, the excessive addition of these antioxidants could impair the performance of the obtained bricks. Thus, when determining the optimum concentration of MgB2 and B4C to be added into MgO-C refractories, one must take into consideration this behavior. (c) 2012 Elsevier Ltd and Techna Group S.r.l. All rights reserved.

Bending stiffness evaluation of Teca and Guajara lumber through tests of transverse and longitudinal vibration

The grading of structural lumber besides contributing for increasing the structure's safety, due to the reduction of the material variability, also allows its rational use. Due to the good correlation between strength and bending stiffness, the latter has been used in estimating the mechanical strength of lumber pieces since the 60's. For industrial application, there are equipment and techniques to evaluate the bending stiffness of lumber, through dynamic tests such as the longitudinal vibration technique, also known as stress wave, and the transverse vibration technique. This study investigated the application of these two techniques in the assessment of the modulus of elasticity in bending of Teca beams (Tectona grandis), from reforestation, and of the tropical species Guajara (Micropholis venulosa). The modulus of elasticity estimated by dynamic tests showed good correlation with the modulus measured in the static bending test. Meantime, we observed that the accuracy of the longitudinal vibration technique was significantly reduced in the evaluation of the bending stiffness of Teca pieces due to the knots existing in this species.

GREEN MACHINING ORIENTED TO DIMINISH DENSITY GRADIENT FOR MINIMIZATION OF DISTORTION IN ADVANCED CERAMICS

After sintering advanced ceramics, there are invariably distortions, caused in large part by the heterogeneous distribution of density gradients along the compacted piece. To correct distortions, machining is generally used to manufacture pieces within dimensional and geometric tolerances. Hence, narrow material removal limit conditions are applied, which minimize the generation of damage. Another alternative is machining the compacted piece before sintering, called the green ceramic stage, which allows machining without damage to mechanical strength. Since the greatest concentration of density gradients is located in the outer-most layers of the compacted piece, this study investigated the removal of different allowance values by means of green machining. The output variables are distortion after sintering, tool wear, cutting force, and the surface roughness of the green ceramics and the sintered ones. The following results have been noted: less distortion is verified in the sintered piece after 1mm allowance removal; and the higher the tool wear the worse the surface roughness of both green and sintered pieces.

Development and optimization of biodegradable films based on achira flour

The influence of glycerol concentration (C-g), process temperature (T-p), drying temperature (T-s), and relative humidity (RH) on the properties of achira flour films was initially assessed. The optimized process conditions were C-g of 17g glycerol/100g flour, T-p of 90 degrees C, T-s of 44.8 degrees C, and RH of 36.4%. The films produced under these conditions displayed high mechanical strength (7.0 MPa), low solubility (38.3%). and satisfactory elongation values (14.6%). This study showed that achira flour is a promising source for the development of biodegradable films with good mechanical properties, low water vapor permeability, and solubility compared to films based on other tubers. (c) 2011 Elsevier Ltd. All rights reserved.

Abrasividade pendular e a resistência mecânica das rochas

Esse trabalho emprega o método para avaliar a abrasividade proposto por Golovanevskiy e Bearman (2008). Esse método, ensaio de abrasão por impacto deslizante (Gouging Abrasion Test), é realizado em condições de alta tensão/alto impacto de desgaste. O método consiste de uma ponteira cilíndrica com uma ponta cônica de 90º, que, em trajetória pendular, atinge uma amostra de rocha com energia de impacto de 300 J e velocidade da ordem de 5,2 m/s. O Gouging Abrasion Index (Gi) é calculado como sendo a média do diâmetro da ponta cônica, após desgaste, em milímetros e o resultado é multiplicado por 10. Esse trabalho verificou a adequabilidade do Gouging Abrasion Test, para um pequeno número de amostras de rocha, que representam, qualitativamente, os principais tipos de rocha encontrados em trabalhos de corte, perfuração e britagem no Brasil, e a sua correlação com outros ensaios consagrados como a resistência à compressão, o desgaste Amsler e a dureza Knoop. Essa análise mostrou alta correlação entre Gi e a dureza Knoop (R² = 0,94), baixa correlação com o desgaste

Disintegration on heating of a Brazilian manganese lump ore

This pioneering study characterized the chemical, physical and mineralogical aspects of the Urucum Standard manganese ore typology, and evaluated some of its metallurgical characteristics, such as the main mineral heat decompositions, and the particle disintegration at room temperature and under continuous heating. A one-ton sample of ore was received, homogenized and quartered. Representative samples were collected and characterized with the aid of techniques, such as ICP-AES, XRD, SEM-EDS, BET and OM. Representative samples with particle sizes between 9.5 mm and 15.9 mm were separated to perform tumbling tests at room temperature, and thermogravimetry tests for both air and nitrogen constant flow at different temperatures. After each heating cycle, the mechanical strength of the orewas evaluated by means of screening and tumbling procedures. The Urucum Standard typology was classified as an oxidized anhydrous ore, with a high manganese content (~47%). This typology ismainly composed of cryptomelane and pyrolusite; however there is a significantamount of hematite. The Urucum Standard particles presented low susceptibility to disintegration at room temperature, but as temperature increased, susceptibility increased. No significant differences were observed between the tests done with the air or nitrogen injections.

Fiber Post Cementation Strategies: Effect of Mechanical Cycling on Push-out Bond Strength and Cement Polymerization Stress

Purpose: To evaluate the effect of mechanical cycling and cementation strategies on the push-out bond strength between fiber posts and root dentin and the polymerization stresses produced using three resin cements. Materials and Methods: Eighty bovine mandibular teeth were sectioned to a length of 16 mm, prepared to 12 mm, and embedded in self-curing acrylic resin. The specimens were then distributed into 8 groups (n = 10): Gr1 - Scotchbond Multi Purpose + RelyX ARC; Gr2 - Scotchbond Multi Purpose + RelyX ARC + mechanical cycling; Gr3 - AdheSE + Multilink Automix; Gr4 - AdheSE + Multilink Automix + mechanical cycling; Gr5 - phosphoric acid + RelyX U100 (self-adhesive cement); Gr6 - phosphoric acid+ RelyX U100 + mechanical cycling; Gr7 - RelyX U100; Gr8 - RelyX U100 + mechanical cycling. The values obtained from the push-out bond strength test were submitted to two-way ANOVA and Tukey's test (p = 0.05), while the values obtained from the polymerization stress test were subjected to one-way ANOVA and Tukey's test (alpha = 0.05). Results: Mechanical cycling did not affect the bond strength values (p = 0.236), while cementation strategies affected the push-out bond strength (p < 0.001). Luting with RelyX U100 and Scotch Bond Multi Purpose + RelyX ARC yielded higher push-out bond strength values. The polymerization stress results were affected by the factor "cement" (p = 0.0104): the self-adhesive cement RelyX U100 exhibited the lowest values, RelyX ARC resulted in the highest values, while Multi link Automix presented values statistically similar to the other two cements. Conclusion: The self-adhesive cement appears to be a good alternative for luting fiber posts due to the high push-out bond strengths and lower polymerization stress values.

Micro-mechanical bond strength tests for the assessment of the adhesion of GIC to dentine

Background. The aim of this study is to critically evaluate the bond strength (BS) of Glass-Ionomer Cements (GIC) to dentine with microtensile (mu TBS) and microshear (mu SBS) BS tests by assessing their rankings and failure patterns. Methods. Samples were made on flat dentine surfaces and submitted to mTBS and mSBS. The materials used were: high viscosity GIC (Ketac (TM) Molar Aplicap-KM), resin-modified GIC (Fuji II-FII), nano-filled resin-modified GIC (Ketac (TM) N100-N100) and an etch-and-rinse adhesive system with a composite resin (Adper (TM) Single Bond 2 and Z100 (TM)-Z100). All tests were performed with a Universal Testing Machine (24 h water storage, crosshead speed of 1 mm/min). Debonded surfaces were examined with a stereomicroscope (x40) to identify the failure mode. The data was analyzed with two-way ANOVA (p < 0.05) and LSD test. Results. Means were statistically different regarding the tests and materials, indicating that values for BS obtained for each material depend on the test performed. Failure analysis revealed that failures produced by mTBS were mainly cohesive for KM and FII. mu SBS failures were mainly adhesive or mixed for all materials. For the mTBS, the rank was Z100 > FII > KM = N100, whereas for the mSBS it was Z100 = FII = KM > N100. Conclusion: It may be concluded that distinct micro-mechanical tests present different failure patterns and rankings depending on the material to be considered.

Thermo and mechanical cycling and veneering method do not influence Y-TZP core/veneer interface bond strength

Objectives: The purpose of this study was to evaluate the influence of thermal and mechanical cycling and veneering technique on the shear bond strength of Y-TZP (yttrium oxide partially stabilized tetragonal zirconia polycrystal) core–veneer interfaces. Materials and methods: Cylindrical Y-TZP specimens were veneered either by layering (n = 20) or by pressing technique (n = 20). A metal ceramic group (CoCr) was used as control (n = 20). Ten specimens for each group were thermal and mechanical cycled and then all samples were subjected to shear bond strength in a universal testing machine with a 0.5 mm/min crosshead speed. Mean shear bond strength (MPa) was analysed with a 2-way analysis of variance and Tukey’s test ( p < 0.05). Failure mode was determined using stereomicroscopy and scanning electron microscopy (SEM). Results: Thermal and mechanical cycling had no influence on the shear bond strength for all groups. The CoCr group presented the highest bond strength value ( p < 0.05) (34.72 7.05 MPa). There was no significant difference between Y-TZP veneered by layering (22.46 2.08 MPa) or pressing (23.58 2.1 MPa) technique. Failure modes were predominantly adhesive for CoCr group, and cohesive within veneer for Y-TZP groups. Conclusions: Thermal and mechanical cycling, as well as the veneering technique does not affect Y-TZP core–veneer bond strength. Clinical significance: Different methods of veneering Y-TZP restorations would not influence the clinical performance of the core/veneer interfaces.