Effect of EVA on the fresh properties of cement paste

The improved workability effect of latex in dry mortars has not been fully clarified. The purpose of this research was to investigate the influence cif the EVA copolymer on the cement hydration and on the rheological properties of cement pastes. The results pointed to a minor influence of EVA on cement hydration and to a ball-bearing effect. In fact, the shear thinning behavior of reference paste at 15 min after mixing changed to shear thickening owing to the EVA addition. This behavior could be explained by the decrease in the interparticle separation distance as consequence of the solid content increase in case of shearing detachment of weakly adhered EVA particles from the cement particles surfaces. The expected EVA plasticizing effect was observed at 60 min. Such behavior points to the stabilization of EVA on the cement particles surfaces, thus resulting in a steric barrier effect. (C) 2011 Elsevier Ltd. All rights reserved.

Avaliação do comportamento de mistura de argamassas através de reometria rotacional

A principal etapa de preparação das argamassas consiste na mistura dos materiais sólidos com água. A introdução do líquido conduz a uma série de eventos de aglomeração e desaglomeração no sistema, que, por sua vez, irão resultar em esforços durante essa etapa. Estudos previamente realizados demonstraram a capacidade de mensuração desses esforços através de curvas que relacionam o torque com o tempo em equipamentos como os reômetros. Nessa perspectiva, o objetivo deste trabalho é avaliar como o tempo influencia a energia de mistura e as propriedades reológicas de argamassas de revestimento com e sem a utilização de aditivo dispersante. O material foi misturado no reômetro rotacional do tipo planetário por tempos distintos (17, 47, 87 e 297 s) e em seguida foi submetido a três ciclos de cisalhamento consecutivos. Em tempos curtos verificou-se que a energia de mistura é baixa, não sendo capaz de romper os aglomerados e homogeneizar o sistema, resultando em materiais reologicamente instáveis e menos fluidos. Por sua vez, a mistura de 297 s demonstrou ser mais eficiente, produzindo uma argamassa estável e fluida. Nas argamassas com o dispersante, os níveis de energia de mistura envolvidos foram mais baixos, e o sistema tendeu a homogeneizar-se mais rapidamente, além de ter resultado em argamassas mais fluidas.

Effect of EVA on the fresh properties of cement paste

The improved workability effect of latex in dry mortars has not been fully clarified. The purpose of this research was to investigate the influence of the EVA copolymer on the cement hydration and on the rheological properties of cement pastes. The results pointed to a minor influence of EVA on cement hydration and to a ball-bearing effect. In fact, the shear thinning behavior of reference paste at 15 min after mixing changed to shear thickening owing to the EVA addition. This behavior could be explained by the decrease in the interparticle separation distance as consequence of the solid content increase in case of shearing detachment of weakly adhered EVA particles from the cement particles surfaces. The expected EVA plasticizing effect was observed at 60 min. Such behavior points to the stabilization of EVA on the cement particles surfaces, thus resulting in a steric barrier effect.