Urea-Based Synthesis of Zinc Oxide Nanostructures at Low Temperature

The preparation of nanometer-sized structures of zinc oxide (ZnO) from zinc acetate and urea as raw materials was performed using conventional water bath heating and a microwave hydrothermal (MH) method in an aqueous solution. The oxide formation is controlled by decomposition of the added urea in the sealed autoclave. The influence of urea and the synthesis method on the final product formation are discussed. Broadband photoluminescence (PL) behavior in visible-range spectra was observed with a maximum peak centered in the green region which was attributed to different defects and the structural changes involved with ZnO crystals which were produced during the nucleation process.

Nanosized precipitates in H13 tool steel low temperature plasma nitriding

A comprehensive study of pulsed nitriding in AISI H13 tool steel at low temperature (400 degrees C) is reported for several durations. X-ray diffraction results reveal that a nitrogen enriched compound (epsilon-Fe2-3N, iron nitride) builds up on the surface within the first process hour despite the low process temperature. Beneath the surface, X-ray Wavelength Dispersive Spectroscopy (WDS) in a Scanning Electron Microscope (SEM) indicates relatively higher nitrogen concentrations (up to 12 at.%) within the diffusion layer while microscopic nitrides are not formed and existing carbides are not dissolved. Moreover, in the diffusion layer, nitrogen is found to be dispersed in the matrix and forming nanosized precipitates. The small coherent precipitates are observed by High-Resolution Transmission Electron Microscopy (HR-TEM) while the presence of nitrogen is confirmed by electron energy loss spectroscopy (EELS). Hardness tests show that the material hardness increases linearly with the nitrogen concentration, reaching up to 14.5 GPa in the surface while the Young Modulus remains essentially unaffected. Indeed, the original steel microstructure is well preserved even in the nitrogen diffusion layer. Nitrogen profiles show a case depth of about similar to 43 mu m after nine hours of nitriding process. These results indicate that pulsed plasma nitriding is highly efficient even at such low temperatures and that at this process temperature it is possible to form thick and hard nitrided layers with satisfactory mechanical properties. This process can be particularly interesting to enhance the surface hardness of tool steels without exposing the workpiece to high temperatures and altering its bulk microstructure. (c) 2012 Elsevier B.V. All rights reserved.

Low-temperature thermodynamic properties near the field-induced quantum critical point in NiCl2-4SC(NH2)(2)

We present a comprehensive experimental and theoretical investigation of the thermodynamic properties: specific heat, magnetization, and thermal expansion in the vicinity of the field-induced quantum critical point (QCP) around the lower critical field H-c1 approximate to 2 T in NiCl2-4SC(NH2)(2). A T-3/2 behavior in the specific heat and magnetization is observed at very low temperatures at H = H-c1, which is consistent with the universality class of Bose-Einstein condensation of magnons. The temperature dependence of the thermal expansion coefficient at H-c1 shows minor deviations from the expected T-1/2 behavior. Our experimental study is complemented by analytical calculations and quantum Monte Carlo simulations, which reproduce nicely the measured quantities. We analyze the thermal and the magnetic Gruneisen parameters, which are ideal quantities to identify QCPs. Both parameters diverge at H-c1 with the expected T-1 power law. By using the Ehrenfest relations at the second-order phase transition, we are able to estimate the pressure dependencies of the characteristic temperature and field scales.

Regioregular improvement on the oxidative polymerization of poly-3-octylthiophenes by slow addition of oxidant at low temperature

Many pathways can be used to synthesize polythiophenes derivatives. The polycondensation reactions performed with organometallics are preferred since they lead to regioregular polymers (with high content of heat-to-tail coupling) which have enhanced conductivity and luminescence. However, these pathways have several steps; the reactants are highly moisture sensitive and expensive. On the other hand, the oxidative polymerization using FeCl3 is a one-pot reaction that requires less moisture sensitive reactants with lower cost, although the most common reaction conditions lead to polymers with low regioregularity. Here, we report that by changing the reaction conditions, such as FeCl3 addition rate and reaction temperature, poly-3-octylthiophenes with different the regioregularities can be obtained, reaching about 80% of heat-to-tail coupling. Different molar mass distributions and polydispersivities were obtained. The preliminary results suggest that the oxidative polymerization process could be improved to yield polythiophenes with higher regioregularity degree and narrower molar mass distributions by just setting some reaction conditions. We also verified that it is possible to solvent extract part of the lower regioregular fraction of the polymer further improving the regioregularity degree. (C) 2011 Wiley Periodicals, Inc. J Appl Polym Sci, 2012

Study of La2-xCaxCuO4 perovskites for the low temperature water gas shift reaction

The effects of small fractions of calcium (x = 0, 0.05, 0.1, 0.15, and 0.20) on the structure and the catalytic properties of La2-xCaxCuO4 peroviskites have been investigated. The samples have been synthesized using the co-precipitation method. Perovskite-type oxides were characterized by XRD, TPR, XPS, XANES, SEM, and TEM. Catalytic tests for the water gas shift reaction (WGSR) were carried out in a tubular reactor at 290 degrees C. All samples showed a well-defined perovskite structure with surface areas between 6 and 18 m(2) g(-1). The partial substitution of La by Ca enhanced the stability of the perovskites and increased their reduction temperature. All catalysts were actives for WGSR, and the best catalytic performance was obtained for the La1.85Ca0.15CuO4 catalyst, but the samples with 5 and 10% of Ca had the best TOF values for reaction. These results can be associated to promoter effect of calcium, the high surface area, and the reducible species Cu-0 and Cu1+. (C) 2011 Elsevier B.V. All rights reserved.

Isolated total RNA and protein are preserved after thawing for more than twenty-four hours

OBJECTIVE: The preservation of biological samples at a low temperature is important for later biochemical and/or histological analyses. However, the molecular viability of thawed samples has not been studied sufficiently in depth. The present study was undertaken to evaluate the viability of intact tissues, tissue homogenates, and isolated total RNA after defrosting for more than twenty-four hours. METHODS: The molecular viability of the thawed samples (n = 82) was assessed using the A260/A280 ratio, the RNA concentration, the RNA integrity, the level of intact mRNA determined by reverse transcriptase polymerase chain reaction, the protein level determined by Western blotting, and an examination of the histological structure. RESULTS: The integrity of the total RNA was not preserved in the thawed intact tissue, but the RNA integrity and level of mRNA were perfectly preserved in isolated defrosted samples of total RNA. Additionally, the level of beta-actin protein was preserved in both thawed intact tissue and homogenates. CONCLUSION: Isolated total RNA does not undergo degradation due to thawing for at least 24 hours, and it is recommended to isolate the total RNA as soon as possible after tissue collection. Moreover, the protein level is preserved in defrosted tissues.

Microwave Hydrothermal Synthesis and Photocatalytic Performance of ZnO and M:ZnO Nanostructures (M = V, Fe, Co)

ZnO and doped M:ZnO (M = V, Fe and Co) nanostructures were synthesized by microwave hydrothermal synthesis using a low temperature route without addition of any surfactant. The transition metal ions were successfully doped in small amount (3% mol) into ZnO structure. Analysis by X-ray diffraction reveals the formation of ZnO with the hexagonal (wurtzite-type) crystal structure for all the samples. The as-obtained samples showed a similar flower-like morphology except for Fe:ZnO samples, which presented a plate-like morphology. The photocatalytic performance for Rhodamine B (RhB) degradation confirmed that the photoactivity of M:ZnO nanostructures decreased for all dopants in structure, according to their eletronegativity. Photoluminescence spectroscopy was employed to correlate M:ZnO structure with its photocatalytical properties. It was suggested that transition metal ions in ZnO lattice introduce defects that act as trapping or recombination centers for photogenerated electrons and holes, making it impossible for them reach the surface and promote the photocatalytical process.