Formation of thin luminescent Eu3+-LB films by in situ coordination with 2,3,5,6-tetra(2 '-pyridyl)pyrazine and 1-octadecanol in pure and mixed Langmuir monolayers

The in situ complexation between 2,3,5,6-tetra(2-pyridyl)pyrazine (tppz) molecules and europium ions at the air-liquid interface by means of mixed 1-octadecanol Langmuir films is reported. These films were transferred to solid supports by means of the Langmuir-Blodgett (LB) technique. The EDS maps attested the homogeneity of the LB films as well as the presence of the europium ions. The mixed alcohol/tppz LB film contained a larger amount of europium ions as compared to the pure octadecanol LB film. This work reports the production of a thin luminescent Eu3+ film containing europium ions using only alcohol molecules as ligands an unexpected result, since it is well known that there is an occurrence of non-radiative deactivation of excited europium by hydroxyl groups. Europium ion multiple binding sites were detected from lifetime decay measurements of these films in the presence of tppz molecules. (C) 2012 Elsevier B.V. All rights reserved.

In situ effect of sodium fluoride or titanium tetrafluoride varnish and solution on carious demineralization of enamel

This study evaluated the effect of titanium tetrafluoride (TiF4) formulations on enamel carious demineralization in situ. Thirteen subjects took part in this cross-over, split-mouth, double-blind study performed in three phases of 14 d each. In each subject, two sound and two predemineralized specimens of bovine enamel were worn intra-orally and plaque accumulation was allowed. One sound and one predemineralized specimen in each subject was treated once with sodium fluoride (NaF) varnish or solution (Treatment A); TiF4 varnish or solution (Treatment B); or placebo varnish or no treatment (Treatment C). The initially sound enamel specimens were exposed to severe cariogenic challenge (20% sucrose, eight times daily for 5 min each time), whereas the predemineralized specimens were not. Eleven subjects were able to finish all experimental phases. The enamel alterations were quantified by surface hardness and transversal microradiography. Demineralization of previously sound enamel was reduced by all test formulations except for the NaF solution, while both TiF4 formulations were as effective as NaF varnish. For the predemineralized specimens, enamel surface hardness was increased only by TiF4 formulations, while subsurface mineral remineralization could not be seen in any group. Within the experimental protocol, TiF4 was able to decrease enamel demineralization to a similar degree as NaF varnish under severe cariogenic challenges, while only TiF4 formulations remineralized the enamel surface.