Reforming of a model biogas on Ni and Rh-Ni catalysts: Effect of adding La

Ni catalysts supported on gamma-Al2O3 modified by Rh and La were prepared and evaluated on the reforming of a model biogas. The catalysts were characterized by EDS, XRD, TPR, XANES and surface area estimation (BET). The results showed that in the original Ni catalyst, the Ni interacted strongly with the alumina support, exhibiting high reduction temperatures in TPR tests. In the catalytic tests, the addition of Rh on Ni catalysts improved CH4 conversion but also increased carbon deposition, possible by causing the segregation of Ni species under the reaction conditions. The presence of La on Ni catalysts reduced the carbon deposition by favoring the gasification of carbon species. Addition of synthetic air to the process improved the CH4 conversion and also decreased the carbon formation. The catalysts Ni, Rh-NiLa, and Rh showed good results in the conversion of model sulfur-free biogas, which suggests that they are promising catalysts to be tested in conversion of real biogas. (C) 2012 Elsevier B.V. All rights reserved.

Ni catalyst on mixed support of CeO2-ZrO2 and Al2O3: Effect of composition of CeO2-ZrO2 solid solution on the methane steam reforming reaction

In this study, catalysts containing 5 wt.% Ni deposited on a support composed of a CeO2-ZrO2 solid solution deposited on alumina were tested in the steam reforming of methane. The supports, with various ratios of Ce to Zr, were prepared by co-precipitation of the oxide precursors, followed by calcination in synthetic air. The catalysts were then prepared by Ni impregnation of the supports. The prepared solids were characterized by temperature-programmed reduction with H-2 (TPR-H-2), in situ X-ray diffraction (XRD) and X-ray absorption near-edge structure (XANES) spectroscopy. The XRD analysis confirmed the formation of a solid solution between ZrO2 and CeO2. In the catalytic tests, it was found that catalysts with higher Ce content did not exhibit deactivation during 6 h of reaction. The catalyst with highest Ce content, Ni(0.8Ce0.2Zr)AI, provided the best result, with the highest rate of conversion of methane and the lowest carbon deposition, which may be partly due to the smaller Ni-0 crystallites in this sample and also the segregated CeO2 particles may have favored H2O adsorption which could lead to higher C gasification. (C) 2012 Elsevier B.V. All rights reserved.