Effects of the Compaction Pressure on the Magnetic Properties of a Sintered Fe-Based Alloy

The structural and magnetic properties of a Fe-based alloy before and after sintering have been analyzed. X ray diffraction measurements confirm the deformation of the magnetic particles in the compacted samples. After sintering, hysteresis energy dissipation, remanence and intrinsic coercivity differ by less than 10% as porosity changes from 15 to 7%.

Texture analysis of cold rolled and annealed aluminum alloy produced by twin-roll casting

A 7.4 mm thick strip of 3003 aluminum alloy produced by the industrial twin-roll casting (TRC) process was homogenized at 500 °C for 12 hours, after which it was cold rolled in two conditions: 1) to reduce the strip's thickness by 67%, and 2) to reduce it by 91%. The alloy was annealed at 400 °C for 1 hour in both conditions. The results revealed that a rotated cube texture, the {001}<110> component, predominated in the as-cast condition and was transformed into brass, copper and S type textures during the cold rolling process. There was practically no difference between the deformation textures at the two thickness reductions.