Changes in the surface of four calcium silicate-containing endodontic materials and an epoxy resin-based sealer after a solubility test

Aim To compare the changes in the surface structure and elemental distribution, as well as the percentage of ion release, of four calcium silicate-containing endodontic materials with a well-established epoxy resin-based sealer, submitted to a solubility test. Methodology Solubility of AH Plus, iRoot SP, MTA Fillapex, Sealapex and MTA-Angelus (MTA-A) was tested according to ANSI/ADA Specification 57. The deionized water used in the solubility test was submitted to atomic absorption spectrophotometry to determine and quantify Ca2+, Na+, K+, Zn2+, Ni2+ and Pb2+ ions release. In addition, the outer and inner surfaces of nonsubmitted and submitted samples of each material to the solubility test were analysed by means of scanning electron microscopy and energy-dispersive spectroscopy (SEM/EDX). Statistical analysis was performed by using one-way anova and Tukeys post hoc tests (a = 0.05). Results Solubility results, in percentage, sorted in an increasing order were -1.24 +/- 0.19 (MTA-A), 0.28 +/- 0.08 (AH Plus), 5.65 +/- 0.80 (Sealapex), 14.89 +/- 0.73 (MTA Fillapex) and 20.64 +/- 1.42 (iRoot SP). AH Plus and MTA-A were statistically similar (P > 0.05), but different from the other materials (P < 0.05). High levels of Ca2+ ion release were observed in all groups except AH Plus sealer. MTA-A also had the highest release of Na2+ and K+ ions. Zn+2 ion release was observed only with AH Plus and Sealapex sealers. After the solubility test, all surfaces had morphological changes. The loss of matrix was evident and the filler particles were more distinguishable. EDX analysis displayed high levels of calcium and carbon at the surface of Sealapex, MTA Fillapex and iRoot SP. Conclusions AH Plus and MTA-A were in accordance with ANSI/ADAs requirements regarding solubility whilst iRoot SP, MTA Fillapex and Sealapex did not fulfil ANSI/ADAs protocols. High levels of Ca2+ ion release were observed in all materials except AH Plus. SEM/EDX analysis revealed that all samples had morphological changes in both outer and inner surfaces after the solubility test. High levels of calcium and carbon were also observed at the surface of all materials except AH Plus and MTA-A.

In vivo evaluation of tissue response to new endodontic sealers

Introduction: The sealers can be in direct contact with the periapical tissues. Thus, these materials must have appropriate physical and biological properties, providing conditions for repair to occur. Objective: The aim of this study was to evaluate the response of rat subcutaneous tissue to endodontics sealers. Material and methods: Three materials comprised the groups: group I – Zinc Oxide, Eugenol and Iodoform paste, group II – Portland cement with propylene glycol, and group III – MTA Fillapex® (Angelus). These materials were placed in polyethylene tubes and implanted into dorsal connective tissue of Wistar rats for seven and 15 days. The specimens were stained with hematoxylin and eosin and evaluated regarding to inflammatory reaction parameters through a light microscope. The data were compared using Kruskal-Wallis test with significance level of 5%. The intensity of inflammatory response against the sealers was analyzed by two blinded and previously calibrated observers for all experimental periods. Results: The histological evaluation showed that all the materials caused a moderated inflammatory reaction at seven days which decreased with time. A greater inflammatory reaction was observed at seven days in group I. The other specimens had significantly less inflammatory cells when compared to this group. Tubes with MTA Fillapex® presented some giant cells, macrophages and lymphocytes after seven days. At 15 days, the presence of fibroblasts and collagen fibers was observed indicating normal tissue healing. The group II showed similar results to those observed in MTA Fillapex® already at seven days. At 15 days the inflammatory reaction presented was almost absent at the tissue, with many collagen fibers indicating normal tissue healing. Statistical analysis showed a significant statistical difference amongst the group I (seven days) and II (15 days) (p < 0.05). In the other groups no (Continue)

In vivo evaluation of tissue response to new endodontic sealers

Introduction: The sealers can be in direct contact with the periapical tissues. Thus, these materials must have appropriate physical and biological properties, providing conditions for repair to occur. Objective: The aim of this study was to evaluate the response of rat subcutaneous tissue to endodontics sealers. Material and methods: Three materials comprised the groups: group I – Zinc Oxide, Eugenol and Iodoform paste, group II – Portland cement with propylene glycol, and group III – MTA Fillapex® (Angelus). These materials were placed in polyethylene tubes and implanted into dorsal connective tissue of Wistar rats for seven and 15 days. The specimens were stained with hematoxylin and eosin and evaluated regarding to inflammatory reaction parameters through a light microscope. The data were compared using Kruskal-Wallis test with significance level of 5%. The intensity of inflammatory response against the sealers was analyzed by two blinded and previously calibrated observers for all experimental periods. Results: The histological evaluation showed that all the materials caused a moderated inflammatory reaction at seven days which decreased with time. A greater inflammatory reaction was observed at seven days in group I. The other specimens had significantly less inflammatory cells when compared to this group. Tubes with MTA Fillapex® presented some giant cells, macrophages and lymphocytes after seven days. At 15 days, the presence of fibroblasts and collagen fibers was observed indicating normal tissue healing. The group II showed similar results to those observed in MTA Fillapex® already at seven days. At 15 days the inflammatory reaction presented was almost absent at the tissue, with many collagen fibers indicating normal tissue healing. Statistical analysis showed a significant statistical difference amongst the group I (seven days) and II (15 days) (p < 0.05). In the other groups no significant statistical differences were observed. Conclusion: MTA Fillapex® and Portland cement with propylene glycol were more biocompatible than the other tested cements.

Physicochemical properties of endodontic sealers of different bases

Objective: To assess the setting time (ST), flow (FL), radiopacity (RD), solubility (SB) and dimensional change following setting (DC) of different sealers (AH Plus (R), Polifil, Apexit Plus (R), Sealapex (R), Endomethasone (R) and Endofill (R)) according to American National Standards Institute/American Dental Association (ANSI/ADA) Specification 57. Material and methods: Five samples of each material were used for each test. For ST, cast rings were filled with sealers and tested with a Gillmore needle. For FL, the sealer was placed on a glass plate. After 180 s, another plate with 20 g and a load of 100 g were applied on the material, and the diameters of the discs formed were measured. In RD, circular molds were filled with the sealers, radiographed and analyzed using Digora software. For SB, circular molds were filled with the sealers, a nylon thread was placed inside the material and another glass plate was positioned on the set, pressed and stored at 37 degrees C. Samples were weighed, placed in water, dried and reweighed. The water used for SB was analyzed by atomic absorption spectrometry. For DC, circular molds were filled with the sealers, covered by glass plates and stored at 37 degrees C. Samples were measured and stored in water for 30 days. After this period, they were dryed and measured again. Results: Regarding ST, AH Plus (R), Apexit (R) and Endofil (R) sealers are in accordance with ANSI/ADA standards. Endomethasone's manufacturer did not mention the ST; Polifil is an experimental sealer and Sealapex (R) did not set. Considering RD, SB and DC, all sealers were in accordance with ANSI/ADA. The spectrometric analysis showed that a significant amount of K+ and Zn2(+) ions was released from Apexit Plus (R) and Endofill (R), respectively. Conclusion: Except for DC, all other physicochemical properties of the tested sealers conformed to ANSI/ADA requirements.

Effects of curing protocol and storage time on the micro-hardness of resin cements used to lute fiber-reinforced resin posts

Objectives: To determine the micro-hardness profile of two dual cure resin cements (RelyX - U100 (R), 3M-ESPE and Panavia F 2.0 (R), Kuraray) used for cementing fiber-reinforced resin posts (Fibrekor (R) - Jeneric Pentron) under three different curing protocols and two water storage times. Material and methods: Sixty 16mm long bovine incisor roots were endodontically treated and prepared for cementation of the Fibrekor posts. The cements were mixed as instructed, dispensed in the canal, the posts were seated and the curing performed as follows: a) no light activation; b) light-activation immediately after seating the post, and; c) light-activation delayed 5 minutes after seating the post. The teeth were stored in water and retrieved for analysis after 7 days and 3 months. The roots were longitudinally sectioned and the microhardness was determined at the cervical, middle and apical regions along the cement line. The data was analyzed by the three-way ANOVA test (curing mode, storage time and thirds) for each cement. The Tukey test was used for the post-hoc analysis. Results: Light-activation resulted in a significant increase in the microhardness. This was more evident for the cervical region and for the Panavia cement. Storage in water for 3 months caused a reduction of the micro-hardness for both cements. The U100 cement showed less variation in the micro-hardness regardless of the curing protocol and storage time. Conclusions: The micro-hardness of the cements was affected by the curing and storage variables and were material-dependent.

Evaluation of Radiopacity, pH, Release of Calcium Ions, and Flow of a Bioceramic Root Canal Sealer

Introduction: The aim of the present study was to evaluate the physicochemical properties of a bioceramic root canal sealer, Endosequence BC Sealer. Radiopacity, pH, release of calcium ions (Ca2+), and flow were analyzed, and the results were compared with AH Plus cement. Methods: Radiopacity and flow were evaluated according to ISO 6876/2001 standards. For the radiopacity analysis, metallic rings with 10-mm diameter and 1-mm thickness were filled with cements. The radiopacity value was determined according to radiographic density (mm Al). The flow test was performed with 0.05 mL of cement placed on a glass plate. A 120-g weight was carefully placed over the cement. The largest and smallest diameters of the disks formed were measured by using a digital caliper. The release of Ca2+ and pH were measured at periods of 3, 24, 72, 168, and 240 hours with spectrophotometer and pH meter, respectively. Data were analyzed by analysis of variance and Tukey test (P < .05). Results: The bioceramic endodontic cement showed radiopacity (3.84 mm Al) significantly lower than that of AH Plus (6.90 mm Al). The pH analysis showed that Endosequence BC Sealer showed pH and release of Ca2+ greater than those of AH Plus (P < .05) during the experimental periods. The flow test revealed that BC Sealer and AH Plus presented flow of 26.96 mm and 21.17 mm, respectively (P < .05). Conclusions: Endosequence BC Sealer showed radiopacity and flow according to ISO 6876/2001 recommendations. The other physicochemical properties analyzed demonstrated favorable values for a root canal sealer. (J Endod 2012;38:842-845)

Effect of Temperature on the Degree of Conversion and Working Time of Dual-Cured Resin Cements Exposed to Different Curing Conditions

Objectives: This study evaluated the degree of conversion (DC) and working time (WT) of two commercial, dual-cured resin cements polymerized at varying temperatures and under different curing-light accessible conditions, using Fourier transformed infrared analysis (FTIR). Materials and Methods: Calibra (Cal; Dentsply Caulk) and Variolink II (Ivoclar Vivadent) were tested at 25 degrees C or preheated to 37 degrees C or 50 degrees C and applied to a similar-temperature surface of a horizontal attenuated-total-reflectance unit (ATR) attached to an infrared spectrometer. The products were polymerized using one of four conditions: direct light exposure only (600 mW/cm(2)) through a glass slide or through a 1.5- or 3.0-mm-thick ceramic disc (A2 shade, IPS e.max, Ivoclar Vivadent) or allowed to self-cure in the absence of light curing. FTIR spectra were recorded for 20 min (1 spectrum/s, 16 scans/spectrum, resolution 4 cm(-1)) immediately after application to the ATR. DC was calculated using standard techniques of observing changes in aliphatic-to-aromatic peak ratios precuring and 20-min postcuring as well as during each 1-second interval. Time-based monomer conversion analysis was used to determine WT at each temperature. DC and WT data (n=6) were analyzed by two-way analysis of variance and Tukey post hoc test (p=0.05). Results: Higher temperatures increased DC regardless of curing mode and product. For Calibra, only the 3-mm-thick ceramic group showed lower DC than the other groups at 25 degrees C (p=0.01830), while no significant difference was observed among groups at 37 degrees C and 50 degrees C. For Variolink, the 3-mm-thick ceramic group showed lower DC than the 1-mm-thick group only at 25 degrees C, while the self-cure group showed lower DC than the others at all temperatures (p=0.00001). WT decreased with increasing temperature: at 37 degrees C near 70% reduction and at 50 degrees C near 90% for both products, with WT reduction reaching clinically inappropriate times in some cases (p=0.00001). Conclusion: Elevated temperature during polymerization of dual-cured cements increased DC. WT was reduced with elevated temperature, but the extent of reduction might not be clinically acceptable.

Topography of four different endodontic rotary systems, before and after being used for the 12th time

Root canal preparation may damage NiTi instruments resulting in wear and deformation. The aim of this study was to make a comparative evaluation of the surface topography of the cervical third of four different rotary systems, before and after being used twelve times, in 1.440 resin blocks with simulated root canals with standardized 45 degrees curvatures, and analyzed by atomic force microscopy AFM. The blocks were divided into four groups and prepared according to the manufacturers recommendations: Group 1 - K3 (R); Group 2 - Protaper Universal (R); Group 3 - Twisted Files (R) and Group 4 - Biorace (R). After each preparation, the instruments were washed and autoclaved. A total of 240 instruments were selected, being 30 new instruments and 30 after having been used for the 12th time, from each group. These instruments were analyzed by AFM and for quantitative evaluation, the mean RMS (Root mean square) values of the cervical third of the specimens from the four groups were used. The result showed that all the rotary files used for the 12th time suffered wear with change in the topography of the cervical region of the active portion of the file (ANOVA p < 0.01). Classifying the specimens in increasing order, from the least to the greatest wear suffered, Group 3 (2.8993 nm) presented the least wear, followed by Group 4 (12.2520 nm), Group 1 (36.0043 nm) and lastly, Group 2 (59.8750 nm) with the largest amount of cervical surface wear. Microsc. Res. Tech. 75:97-102, 2012. (c) 2011 Wiley Periodicals, Inc.

Clinical microscopic analysis of protaper retreatment system efficacy considering root canal thirds using three endodontic sealers

To evaluate the efficacy of ProTaper Universal rotary retreatment system and the influence of sealer type on the presence of filling debris in the reinstrumented canals viewed in an operative clinical microscope. Forty-five palatal root canals of first molars were filled with gutta-percha and one of the following sealers: G1, EndoFill; G2, AH Plus; G3, Sealapex. The canals were then reinstrumented with ProTaper Universal rotary system. Roots were longitudinally sectioned and examined under an operative clinical microscope (10x), and the amount of filling debris on canal walls was analyzed using the AutoCAD 2004 software. A single operator used a specific software tool to outline the canal area and the filling debris area in each third (cervical, middle, and apical), as well as the total canal area. Data were analyzed by Kruskal-Wallis test and Tukey test at P < 0.05. Sealapex demonstrated significant differences in the average of filling debris area/canal among the 3 thirds. This group revealed that apical third showed more debris than the both cervical and middle third (P < 0.0001). Endofill presented significantly more filling debris than Sealapex in the cervical third (P < 0.05). In the middle (P = 0.12) and apical third (P = 0.10), there were no differences amongst groups. Debris was left in all canal thirds, regardless of the retreatment technique. The greatest differences between techniques and sealers were found in the cervical third. Microsc. Res. Tech. 75:12331236, 2012. (C) 2012 Wiley Periodicals, Inc.

Antimicrobial effect of endodontic solutions used as final irrigants on a dentine biofilm model

Aim To evaluate the residual biovolume of live bacterial cells, the mean biofilm thickness and the substratum coverage found in mixed biofilms treated with different endodontic irrigant solutions. Methodology Twenty-five bovine dentine specimens were infected intraorally using a removable orthodontic device. Five samples were used for each irrigant solution: 2% chlorhexidine, 1% sodium hypochlorite (NaOCl), 10% citric acid, 17% EDTA and distilled water. The solutions were used for 5 min. The samples were stained using the Live/Dead technique and evaluated using a confocal microscope. Differences in the amount of total biovolume (mu m3), number of surviving cells (mu m3), mean biofilm thickness (mu m) and substratum coverage (%) of the treated biofilms were determined using nonparametric statistical tests (P < 0.05). Results Similar values of biovolume total, biovolume of live subpopulations and substratum coverage were found in 2% chlorhexidine, 10% citric acid, 17% EDTA and distilled water-treated biofilms (P > 0.05). The lower values of the studied parameters were found in 1% NaOCl-treated dentine (P < 0.05) with the exception of the mean biofilm height criteria that did not reveal significant differences amongst the irrigant solutions (P > 0.05). Conclusions One per cent sodium hypochlorite was the only irrigant that had a significant effect on biofilm viability and architecture.

Shear bond strength between different materials bonded with two resin cements

Background: The aim of this study was to compare the shear bond strength between Ni-Cr alloy specimens bonded to air-abraded Ni-Cr, bur-abraded Ni-Cr, etched ceramic and etched enamel substrates using the resin cements RelyX ARC or Enforce. Materials and methods: Ni-Cr specimens were made and sandblasted with Al2O3 airborne-particles. Disc-shaped patterns were made for each of the four experimental substrates: Ni-Cr treated with Al2O3 airborne-particles, Ni-Cr treated with diamond bur abrasion, etched enamel and etched ceramic. Results: Significant differences in shear bond strength were found between the different materials and luting agents evaluated. The Ni-Cr alloy cylinders bonded to Ni-Cr surfaces sandblasted with 50 lm Al2O3 particles and bonded with Enforce achieved the highest bond strength when compared with other substrates (28.9 MPa, p < 0.05). Bur-abraded metal discs had lowest values, regardless the cement used (2.9 and 6.9 MPa for RelyX and Enforce, respectively). Etched enamel and etched ceramic had similar shear bond strengths within cement groups and performed better when RelyX was used. Conclusions: Bonding Ni-Cr to Ni-Cr and ceramic may result in similar and higher bond strength when compared to Ni-Cr/enamel bonding. For metal/metal bonding, higher shear bond strength was achieved with resin cement Enforce, and for metal/ceramic and metal/enamel bonding, RelyX had higher results.

Orbital Abscess during Endodontic Treatment: A Case Report

Introduction: Orbital infections may result in permanent morbidity because of the severity of infection. Furthermore, delayed diagnosis or treatment of orbital infections can lead to intracranial complications and even death. The majority of orbital infections develop from paranasal sinus infections, cutaneous infections, and periorbital trauma. Dacryocystitis and odontogenic infection are also accounted as potential etiologies but are scarcely reported in scientific literature. Methods: The patient revealed a history of having endodontic treatment on left maxillary second molar performed 2 weeks previously. Moreover, she exhibited signs of facial pain accompanied by sinusitis symptoms, fever, and nasal obstruction the week after this endodontic procedure. The patient presented proptosis, impairment of ocular motility to the right side, facial tenderness, palpebral erythema, and referred decreased visual acuity. Intraoral exam revealed root fragments of left maxillary first molar and an extensive carious lesion on left maxillary second molar. Computed tomography enabled the observation of frontal sinus, left-sided maxillary, opacity of sphenoidal and ethmoidal sinuses, and apical lesion of left maxillary first and second molars, all suggesting the presence of their apex in the maxillary sinus. In addition, images revealed ocular proptosis and presence of high-density areas suggestive of pus in the medial orbital wall region. Results: The patient was submitted to surgical drainage under general anesthesia approximately 8 hours after the clinical evaluation. Conclusions: Early detection of orbital infection, proper diagnostic tests, and treatment may provide successful outcomes of this rarely occurring disease. (J Endod 2012;38:1541-1543)

The effect of curing light and chemical catalyst on the degree of conversion of two dual cured resin luting cements

The aim of this study was to evaluate the influence of different curing lights and chemical catalysts on the degree of conversion of resin luting cements. A total of 60 disk-shaped specimens of RelyX ARC or Panavia F of diameter 5 mm and thickness 0.5 mm were prepared and the respective chemical catalyst (Scotchbond Multi-Purpose Plus or ED Primer) was added. The specimens were light-cured using different curing units (an argon ion laser, an LED or a quartz-tungsten-halogen light) through shade A2 composite disks of diameter 10 mm and thickness 2 mm. After 24 h of dry storage at 37A degrees C, the degree of conversion of the resin luting cements was measured by Fourier-transformed infrared spectroscopy. For statistical analysis, ANOVA and the Tukey test were used, with p a parts per thousand currency signaEuro parts per thousand 0.05. Panavia F when used without catalyst and cured using the LED or the argon ion laser showed degree of conversion values significantly lower than RelyX ARC, with and without catalyst, and cured with any of the light sources. Therefore, the degree of conversion of Panavia F with ED Primer cured with the quartz-tungsten-halogen light was significantly different from that of RelyX ARC regardless of the use of the chemical catalyst and light curing source. In conclusion, RelyX ARC can be cured satisfactorily with the argon ion laser, LED or quartz-tungsten-halogen light with or without a chemical catalyst. To obtain a satisfactory degree of conversion, Panavia F luting cement should be used with ED Primer and cured with halogen light.

Optimizing endodontic irrigation: advantages of negative apical pressure technology

FAPESP #2010/16002-4

The antimicrobial effect of new and conventional endodontic irrigants on intra-orally infected dentin

Objectives. To evaluate if the incorporation of antimicrobial compounds to chelating agents or the use of chelating agents with antimicrobial activity as 7% maleic acid and peracetic acid show similar disinfection ability in comparison to conventional irrigants as sodium hypochlorite or iodine potassium iodide against biofilms developed on dentin. Materials and methods. The total bio-volume of live cells, the ratio of live cells and the substratum coverage of dentin infected intra-orally and treated with the irrigant solutions: MTAD, Qmix, Smear Clear, 7% maleic acid, 2% iodine potassium iodide, 4% peracetic acid, 2.5% and 5.25% sodium hypochlorite was measured by using confocal microscopy and the live/dead technique. Five samples were used for each irrigant solution. Results. Several endodontic irrigants containing antimicrobials as clorhexidine (Qmix), cetrimide (Smear Clear), maleic acid, iodine compounds or antibiotics (MTAD) lacked an effective antibiofilm activity when the dentin was infected intra-orally. The irrigant solutions 4% peracetic acid and 2.5–5.25% sodium hypochlorite decrease significantly the number of live bacteria in biofilms, providing also cleaner dentin surfaces (p < 0.05). Conclusions. Several chelating agents containing antimicrobials could not remove nor kill significantly biofilms developed on intra-orally infected dentin, with the exception of sodium hypochlorite and 4% peracetic acid. Dissolution ability is mandatory for an appropriate eradication of biofilms attached to dentin.