Clinical microscopic analysis of protaper retreatment system efficacy considering root canal thirds using three endodontic sealers

To evaluate the efficacy of ProTaper Universal rotary retreatment system and the influence of sealer type on the presence of filling debris in the reinstrumented canals viewed in an operative clinical microscope. Forty-five palatal root canals of first molars were filled with gutta-percha and one of the following sealers: G1, EndoFill; G2, AH Plus; G3, Sealapex. The canals were then reinstrumented with ProTaper Universal rotary system. Roots were longitudinally sectioned and examined under an operative clinical microscope (10x), and the amount of filling debris on canal walls was analyzed using the AutoCAD 2004 software. A single operator used a specific software tool to outline the canal area and the filling debris area in each third (cervical, middle, and apical), as well as the total canal area. Data were analyzed by Kruskal-Wallis test and Tukey test at P < 0.05. Sealapex demonstrated significant differences in the average of filling debris area/canal among the 3 thirds. This group revealed that apical third showed more debris than the both cervical and middle third (P < 0.0001). Endofill presented significantly more filling debris than Sealapex in the cervical third (P < 0.05). In the middle (P = 0.12) and apical third (P = 0.10), there were no differences amongst groups. Debris was left in all canal thirds, regardless of the retreatment technique. The greatest differences between techniques and sealers were found in the cervical third. Microsc. Res. Tech. 75:12331236, 2012. (C) 2012 Wiley Periodicals, Inc.

Selection of compositions with high glass forming ability in the Ni-Nb-B alloy system

A combination of an extension of the topological instability "λ criterion" and the "average electronegativity" has been recently reported in the literature to predict compositions with high glass-forming ability (GFA). In the present work, both criteria have been applied to select the Ni61.0Nb36.0B3 alloy with a high glass-forming ability. Ingots were prepared by arc-melting and were used to produce ribbons processed by the melt-spinning technique further characterized by differential scanning calorimetry (DSC), X-ray diffraction (XRD) and scanning electron microscopy (SEM). The Ni61.0Nb36.0B3 alloy revealed a complete amorphization and supercooled liquid region ΔTx = 68 K. In addition, wedge-shaped samples were prepared using copper mold casting in order to determine the critical thickness for amorphous formation. Scanning electron microscopy (SEM) revealed that fully amorphous samples could be obtained, reaching up to ~800 µm in thickness.