Minimal alterations on the enamel surface by micro-abrasion: in vitro roughness and wear assessments

Objective: To evaluate the in vitro changes on the enamel surface after a micro-abrasion treatment promoted by different products. Material and Methods: Fifty (50) fragments of bovine enamel (15 mm × 5 mm) were randomly assigned to five groups (n=10) according to the product utilized: G1 (control)= silicone polisher (TDV), G2= 37% phosphoric acid (3M/ESPE) + pumice stone (SS White), G3= Micropol (DMC Equipment), G4= Opalustre (Ultradent) and G5= Whiteness RM (FGM Dental Products). Roughness and wear were the responsible variables used to analyze these surfaces in four stages: baseline, 60 s and 120 s after the micro-abrasion and after polishing, using a Hommel Tester T1000 device. After the tests, a normal distribution of data was verified, with repeated ANOVA analyses (p?0.05) which were used to compare each product in different stages. One-way ANOVA and Tukey tests were applied for individual comparisons between the products in each stage (p?0.05). Results: Means and standard deviations of roughness and wear (µm) after all the promoted stages were: G1=7.26(1.81)/13.16(2.67), G2=2.02(0.62)/37.44(3.33), G3=1.81(0.91)/34.93(6.92), G4=1.92(0.29)/38.42(0.65) and G5=1.98(0.53)/33.45(2.66). At 60 seconds, all products tended to produce less surface roughness with a variable gradual decrease over time. After polishing, there were no statistically significant differences between the groups, except for G1. Independent of the product utilized, the enamel wear occurred after the micro-abrasion. Conclusions: In this in vitro study, enamel micro-abrasion presented itself as a conservative approach, regardless of the type of the paste compound utilized. These products promoted minor roughness alterations and minimal wear. The use of phosphoric acid and pumice stone showed similar results to commercial products for the micro-abrasion with regard to the surface roughness and wear.

Optical transition radiation used in the diagnostic of low energy and low current electron beams in particle accelerators

Optical transition radiation (OTR) plays an important role in beam diagnostics for high energy particle accelerators. Its linear intensity with beam current is a great advantage as compared to fluorescent screens, which are subject to saturation. Moreover, the measurement of the angular distribution of the emitted radiation enables the determination of many beam parameters in a single observation point. However, few works deals with the application of OTR to monitor low energy beams. In this work we describe the design of an OTR based beam monitor used to measure the transverse beam charge distribution of the 1.9-MeV electron beam of the linac injector of the IFUSP microtron using a standard vision machine camera. The average beam current in pulsed operation mode is of the order of tens of nano-Amps. Low energy and low beam current make OTR observation difficult. To improve sensitivity, the beam incidence angle on the target was chosen to maximize the photon flux in the camera field-of-view. Measurements that assess OTR observation (linearity with beam current, polarization, and spectrum shape) are presented, as well as a typical 1.9-MeV electron beam charge distribution obtained from OTR. Some aspects of emittance measurement using this device are also discussed. (C) 2012 American Institute of Physics. [http://dx.doi.org/10.1063/1.4748519]

Mass loss and wear mechanisms of HVOF-sprayed multi-component white cast iron coatings

In this work, multi-component white cast iron was applied by HVOF thermal spray process as alternative to other manufacture processes. Effects of substrate type, substrate pre-heating and heat treatment of coating on mass loss have been determined by rubber wheel apparatus in accordance with ASTM G-65. Furthermore, influence of heat treatment of coating on wear mechanisms was also determined by scanning electron microscopy analysis. Heat-treated coatings presented mass loss three times lower than as-sprayed coatings. Furthermore, wear mechanisms of as-sprayed coating are micro-cutting associated with cracks close to unmelted particles and pores. In heat-treated coating, lesser mass loss is due to sintering. (C) 2011 Elsevier B.V. All rights reserved.

Impact of different fluoride concentrations and pH of dentifrices on tooth erosion/abrasion in vitro

Background: This in vitro study analysed the effect of different fluoride concentrations in acidic or neutral liquid dentifrices in protecting enamel and dentine from erosive and abrasive wear. Methods: Bovine enamel and dentine specimens (n = 132) were randomly allocated to 11 groups (each n = 12): experimental liquid dentifrices with 550 ppm F, 1100 ppm F, 5000 ppm F or 0 ppm F/placebo (each at pH 4.5 and pH 7.0); and commercial dentifrices with 550 ppm F (Colgate Baby, pH 7.0), 1100 ppm F (Crest, pH 7.0) and 5000 ppm F (Duraphat, pH 7.0). The specimens were subjected to erosion for 90 seconds, 4 times/day, over 7 days. Immediately after the first and last erosion, the specimens were brushed for 15 seconds using one of the dentifrices. Tooth wear was measured profilometrically (lm) and analysed by ANOVA (p < 0.05). Results: All fluoridated liquid dentifrices significantly reduced enamel wear compared to the placebo and commercial dentifrices. Only liquid dentifrices with 1100 and 5000 ppm F significantly reduced dentine wear compared to placebo dentifrice. The pH had no effect, but the consistency had a significant impact on the effect of dentifrices. Conclusions: Liquid dentifrices with high F concentration appear to be a good option to prevent tooth wear