Shear bond strength of nanofilled flowable resins used for indirect bracket bonding

AIM: To evaluate the bond strength of brackets fixed with different materials (two light-cured nanofilled resins - Transbond Supreme LV and Flow Tain LV, a light-cured resin - Transbond XT (control) and two chemically cured resins for indirect bonding - Sondhi Rapid- Set and Custom I.Q.) using the indirect bonding technique after 10 min and 24 h, and evaluate the type of failure. METHODS: One hundred premolars were selected and randomly divided into groups (n=10) according to the material and fixation period. The brackets were bonded through the indirect technique following the manufacturer's instructions and stored in deionized water at 37°C for 10 min or 24 h. After, the specimens were submitted to a shear bond strength (SBS) test (Instron) at 0.5 mm/min and evaluated for adhesive remnant index (ARI). The data were submitted to ANOVA and Tukey's test (p<0.05) and the ARI scores were submitted to the chi-square test. RESULTS: It could be observed a significant difference among the materials (Flow Tain LV = Transbond Supreme LV = Transbond XT> Sondhi Rapid-Set > Custom I.Q.). There was no significant difference in resistance values between 10 min and 24 h, regardless of the materials. Most groups showed adhesive remaining adhered to the enamel (scores 2 and 3) without statistically significant difference (p>0.05). CONCLUSIONS: It was concluded that the light-cured nanofilled materials used in indirect bonding showed greater resistance than the chemically cured materials. The period of fixation had no influence on the resistance for different materials.

A method to investigate the shrinkage stress developed by resin-composites bonded to a single flat surface

Objectives. To purpose a method for predicting the shrinkage stress development in the adhesive layer of resin-composite cylinders that shrink bonded to a single flat surface, by measuring the deflection of a glass coverslip caused by the shrinkage of the bonded cylinders. The correlation between the volume of the bonded resin-composite and the stress-peak was also investigated. Methods. A glass coverslip deflection caused by the shrinkage of a bonded resin-composite cylinder (diameter: d = 8 mm, 4 mm, or 2 mm, height: h = 4 mm, 2 mm, 1 mm, or 0.5 mm) was measured, and the same set-up was simulated by finite element analysis (3D-FEA). Stresses generated in the adhesive layer were plotted versus two geometric variables of the resin-composite cylinder (C-Factor and volume) to verify the existence of correlations between them and stresses. Results. The FEA models were validated. A significant correlation (p < 0.01, Pearson's test) between the stress-peak and the coverslip deflection when the resin-composites were grouped by diameter was found for diameters of 2 and 4 mm. The stress-peak of the whole set of data showed a logarithmic correlation with the bonded resin-composite volume (p < 0.001, Pearson's test), but did not correlate with the C-Factor. Significance. The described method should be considered for standardizing the stress generated by the shrinkage of resin-composite blocks bonded to a single flat surface. (C) 2012 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

The filler content of the dental composite resins and their influence on different properties

The purpose of this study was to compare the inorganic content and morphology of one nanofilled and one nanohybrid composite with one universal microhybrid composite. The Vickers hardness, degree of conversion and scanning electron microscope of the materials light-cured using LED unit were also investigated. One nanofilled (Filtek (TM) Supreme XT), one nanohybrid (TPH (R) 3) and one universal microhybrid (Filtek (TM) Z-250) composite resins at color A2 were used in this study. The samples were made in a metallic mould (4 mm in diameter and 2 mm in thickness). Their filler weight content was measured by thermogravimetric analysis (TG). The morphology of the filler particles was determined using scanning electron microscope equipped with a field emission gun (SEM-FEG). Vickers hardness and degree of conversion using FT-IR spectroscopy were measured. Filtek (TM) Z-250 (microhybrid) composite resin shows higher degree of conversion and hardness than those of Filtek (TM) Supreme XT (nanofilled) and TPH (R) 3 (nanohybrid) composites, respectively. The TPH3 (R) (nanohybrid) composite exhibits by far the lowest mechanical property. Nanofilled composite resins show mechanical properties at least as good as those of universal hybrids and could thus be used for the same clinical indications as well as for anterior restorations due to their high aesthetic properties. Microsc. Res. Tech. 75:758765, 2012. (C) 2011 Wiley Periodicals, Inc

Effectiveness of immediate bonding of etch-and-rinse adhesives to simplified ethanol-saturated dentin

This study examined the immediate bond strength of etch-and-rinse adhesives to demineralized dentin saturated with either water or absolute ethanol. The research hypothesis was that there would be no difference in bond strength to dentin between water or ethanol wet-bonding techniques. The medium dentin of 20 third molars was exposed (n = 5). The dentin surface was then acid-etched, left moist and randomly assigned to be saturated via either water wet-bonding (WBT) or absolute ethanol wet-bonding (EBT). The specimens were then treated with one of the following etch-and-rinse adhesive systems: a 3-step, water-based system (Adper Scotchbond Multipurpose, or SBMP) or a 2-step, ethanol/water-based system (Adper Single Bond 2, or SB). Resin composite build-ups were then incrementally constructed. After water storage for 24 h at 37 degrees C, the tensile strength of the specimens was tested in a universal testing machine (0.5 mm/min). Data were analyzed by two-way ANOVA and Tukey's test (alpha = 5%). The failure modes were verified using a stereomicroscope (40x). For both adhesives, no significant difference in bond strength was observed between WBT and EBT (p > 0.05). The highest bond strength was observed for SB, regardless of the bonding technique (p < 0.05). No significant interaction between adhesives and bonding techniques was noticed (p = 0.597). There was a predominance of adhesive failures for all tested groups. The EBT and WBT displayed similar immediate bond strength means for both adhesives. The SB adhesive exhibited higher means for all conditions tested. Further investigations are needed to evaluate long-term bonding to dentin mediated by commercial etch-and-rinse adhesives using the EBT approach.

Kinetic parameters and monomeric conversion of different dental composites using standard and soft-start photoactivation modes

This paper evaluates the photopolymerization kinetics and degree of conversion of different commercial dental composites when photoactivated by a LED curing unit using two different modes (standard and soft-start mode). The investigation was performed on with RelyX ARC (dual-cured), Filtek Z-350 (Nanocomposite), Filtek Z-250 (Hybrid), and Filtek Z-350flow (Flowable) resin composites. The analysis used was attenuated total reflection with a Fourier transform infrared (ATR-FTIR). The RelyX ARC resin demonstrated the highest degree of conversion with both LED photoactivation modes. For this resin a 28% decrease in maximum rate was observed and the time to reach its highest rate was almost 2.3 times higher than when the soft-start photoactivation light curing was used. Z-350flow resin recorder a higher maximum rate using the soft-start mode rather than the standard mode. In contrast, the Z-250 showed a higher value using the standard mode. Although Z-250 and Z-350 showed a higher total degree of conversion effectiveness using the soft-start mode, RelyX and Z-350flow achieved a higher value using the standard mode.

Systemically alendronate was incorporated into dental tissues but did not cause morphological or mechanical changes in rats teeth

This study evaluated the effect of the systemic use of sodium alendronate in rats in vivo. Forty-five Wistar rats aged 36 to 42 days and weighing 200 to 230 g were randomly assigned to a control group (n = 20), which received distilled water, and an experimental group (n = 25), which received 2 weekly doses of 1 mg/kg of chemically pure sodium alendronate. The animals were killed after 60 days of treatment. The tibias were removed for analysis of bone mineral density by dual-energy X-ray absorptiometry (DXA). Then, the maxillary incisors were extracted for analysis of the mineralized dental tissues using fluorescence spectroscopy (FS), scanning electron microscopy (SEM), bright field microscopy (BFM), and cross-sectional microhardness (CSMH) testing. DXA and CSMH data were subjected to statistical analysis by Kruskal-Wallis test (5% significance level). The experimental group presented higher bone mineral density than the control group by DXA. FS analysis revealed presence of alendronate in the mineralized dental tissues of the specimens of the experimental group. Significant morphological differences were not found by SEM and BFM. Enamel and dentin (100 and 300 mu m from the dentinoenamel junction) CSMH data did not show significant difference between the control and experimental groups. Based on the obtained results, we conclude that while alendronate increased the bone mineral density and was incorporated into the mineralized dental tissues it did not cause significant alterations in the morphology and microhardness of rat incisor enamel and dentin. Microsc. Res. Tech. 75:12651271, 2012. (C) 2012 Wiley Periodicals, Inc.