Influence of artificial accelerated ageing on the colour stability of paints used for ocular prosthesis iris painting

Objectives: To evaluate the colour stability of paints used for ocular prosthesis iris painting submitted for accelerated artificial ageing (AAA). Materials and methods: Forty specimens of acrylic resin for sclera (16 x 2 mm) were made and separated into eight groups (n = 10) according to the type of paint (gouache, GP; oil, OP; acrylic AP; and composite resin for characterisation, CR) and the colours used (blue/brown). After drying (72 h), a new layer of colourless acrylic resin was applied and the initial colour readout was performed (Spectrophotometer PCB 6807). New colour readouts were performed after AAA, and Delta E was calculated. Results: Statistical analysis (two-way ANOVA-Bonferroni, p < 0.05) demonstrated that the brown colour showed lower Delta E means in comparison with the blue colour, with statistically significant difference for AP only. Blue colour showed no statistically significant difference with regard to the type of paint used. Brown AP showed lower Delta E than the other groups, with significant difference for OP and GP. GP showed greater alteration in Delta E for the brown colour, being statistically similar only to OP. Conclusions: Only the AP group for brown pigment shows clinically acceptable values for colour stability after AAA.

Evaluation of experimental cleanser solution of Ricinus communis: effect on soft denture liner properties

Objective: This study evaluated colour stability, hardness and roughness of soft denture liners after immersion in various cleansers. Materials and methods: Thirty specimens (14 mm x 4 mm) of Elite Soft Relining (ES) and Mucopren Soft (MS) were randomly immersed in distilled water at 37 degrees C, sodium hypochlorite 1%, and an experimental Ricinus communis solution (RC) for 7, 15 and 183 continuous days. Results: ANOVA (p < 0.05) and Tukey's test indicated that after T7 (mu =8.79 +/- 7.36); T15 (mu = 4.23 +/- 2.62) and T183 (mu = 8.78 +/- 3.16), MS presented a higher increase in hardness than ES. After T7, MS underwent an increase in roughness (mu = 0.09 +/- 0.80); ES underwent a decrease (mu = -0.08 +/- 0.16). RC caused the smallest variation in roughness. After T15, both materials presented an increase in roughness. After T183, ES (mu = -0.30 +/- 0.48) presented a higher roughness variation than MS (mu = -0.07 +/- 0.32). Hypochlorite caused an increase in roughness (mu = 0.02 +/- 0.19). Conclusion: After all periods ES presented higher colour alteration than MS; highest colour alteration was caused by hypochlorite. Both materials were more stable after immersion in RC.