Effects of chemical composition on the corrosion of dental alloys

The aim of this study was to determine the effect of the oral environment on the corrosion of dental alloys with different compositions, using electrochemical methods. The corrosion rates were obtained from the current-potential curves and electrochemical impedance spectroscopy (EIS). The effect of artificial saliva on the corrosion of dental alloys was dependent on alloy composition. Dissolution of the ions occurred in all tested dental alloys and the results were strongly dependent on the general alloy composition. Regarding the alloys containing nickel, the Ni-Cr and Ni-Cr-Ti alloys released 0.62 mg/L of Ni on average, while the Co-Cr dental alloy released ions between 0.01 and 0.03 mg/L of Co and Cr, respectively.The open-circuit potential stabilized at a higher level with lower deviation (standard deviation: Ni-Cr-6Ti = 32 mV/SCE and Co-Cr = 54 mV/SCE). The potenciodynamic curves of the dental alloys showed that the Ni-based dental alloy with >70 wt% of Ni had a similar curve and the Co-Cr dental alloy showed a low current density and hence a high resistance to corrosion compared with the Ni-based dental alloys. Some changes in microstructure were observed and this fact influenced the corrosion behavior for the alloys. The lower corrosion resistance also led to greater release of nickel ions to the medium. The quantity of Co ions released from the Co-Cr-Mo alloy was relatively small in the solutions. In addition, the quantity of Cr ions released into the artificial saliva from the Co-Cr alloy was lower than Cr release from the Ni-based dental alloys.

Evaluation of corrosion resistance and cytotoxicity of electrodeposited gold on various types of intermediate layers

Gold plated surfaces are widely applied in several technical and decorative fields. The two main issues regarding the discussion on the field of precious metal coatings concern the increase in the use of thinner gold layers and 'Ni free' substrates. In order to ensure the quality of the final products, the effects of the plated surfaces on their performance require thorough and accurate research. In this paper, the corrosion resistance of gold plated nickel, copper and bronze was investigated by electrochemical methods specifically potentiodynamic polarisation and electrochemical impedance spectroscopy in phosphate buffered saline. The cytotoxicity of the gold plated substrates was also evaluated and compared. The results showed that the substrate related to the best corrosion resistance and cytotoxicity among the tested ones was bronze, and the one with the lowest performance was nickel.

Niobium Effects on the Recrystallization Behavior on a Full Austenitic 15Cr-15Ni Stainless Steel Investigated Using Adaptive Neural Networks (ANN)

A new series of austenitic stainless steels-Nb stabilized, without Mo additions, non-susceptible to delta ferrite formation and devoid of intemetallic phases (sigma and chi), without deformation induced martensite is being developed, aiming at high temperature applications as well as for corrosive environments. The base steel composition is a 15Cr-15Ni with normal additions of Nb of 0.5, 1.0 and 2 wt%. Mechanical properties, oxidation and corrosion resistance already have been invetigated in previous papers. In this paper, the effects of Nb on the SFE, strain hardening and recrystallization resistance are evaluated with the help of Adaptive Neural Networks (ANN).