Poly(2,5-bibenzimidazole) Membranes: Physico-Chemical Characterization Focused on Fuel Cell Applications

Membranes of Poly(2,5-benzimidazole) (ABPBI), prepared by polycondensation in polyphosphoric acid, were characterized from the fuel cell application point of view: mechanical properties of the membranes for different acid doping levels, thermal stability, permeability for the different gases/vapors susceptible of use in the cell (hydrogen, oxygen, methanol and ethanol), electro-osmotic water drag coefficient, oxidation stability to hydroxyl radicals, phosphoric acid leaching rate and, finally, in-plane membrane conductivity. ABPBI membranes presented an excellent thermal stability, above 500 degrees C in oxygen, suitable mechanical properties for high phosphoric acid doping levels, a low methanol and ethanol limiting permeation currents, and oxygen permeability compared to Nafion membranes, and a low phosphoric acid leaching rate when exposed to water vapor. On the contrary, hydrogen permeation current was higher than that of Nafion, and the chemical stability was very limited. Membrane conductivity achieved 0.07 S cm(-1) after equilibration with a humid environment. Fuel cell tests showed reasonable good performances, with a maximum power peak of 170 mW cm(-2) for H-2/air at 170 degrees C operating under a humidified hydrogen stream, 39.9 mW cm(-2) for CH3OH/O-2 at 200 degrees C for a methanol/water weight ratio of 1: 2, and 31.5 mW cm(-2) for CH3CH2OH/O-2 at the same conditions than for methanol. (C) 2012 The Electrochemical Society. [DOI: 10.1149/2.014207jes] All rights reserved.

SYNTHESIS OF N-15-ENRICHED UREA (CO((NH2)-N-15)(2)) FROM (NH3)-N-15, CO, AND S IN A DISCONTINUOUS PROCESS

CO((NH2)-N-15)(2) enriched with the stable isotope N-15 was synthesized based on a reaction involving CO, (NH3)-N-15, and S in the presence of CH3OH. The method differs from the industrial method; a stainless steel reactor internally lined with polytetrafluoroethylene (PTFE) was used in a discontinuous process under low pressure and temperature. The yield of the synthesis was evaluated as a function of the parameters: the amount of reagents, reaction time, addition of H2S, liquid solution and reaction temperature. The results showed that under optimum conditions (1.36, 4.01, and 4.48 g of (NH3)-N-15, CO, and S, respectively, 40 ml CH3OH, 40 mg H2S, 100 degrees C and 120 min of reaction) 1.82 g (yield 76.5%) of the compound was obtained per batch. The synthesized CO((NH2)-N-15)(2) contained 46.2% N, 0.55% biuret, melting point of 132.55 degrees C and did not exhibit isotopic fractionation. The production cost of CO((NH2)-N-15)(2) with 90.0 at. % N-15 was US$ 238.60 per gram.

Synthesis of 15N-enriched urea (CO(15NH2)2) from 15NH3, CO, and S in a discontinuous process

CO(15NH2)2 enriched with the stable isotope 15N was synthesized based on a reaction involving CO, 15NH3, and S in the presence of CH3OH. The method differs from the industrial method; a stainless steel reactor internally lined with polytetrafluoroethylene (PTFE) was used in a discontinuous process under low pressure and temperature. The yield of the synthesis was evaluated as a function of the parameters: the amount of reagents, reaction time, addition of H2S, liquid solution and reaction temperature. The results showed that under optimum conditions (1.36, 4.01, and 4.48 g of 15NH3, CO, and S, respectively, 40 ml CH3OH, 40 mg H2S, 100 ºC and 120 min of reaction) 1.82 g (yield 76.5%) of the compound was obtained per batch. The synthesized CO(15NH2)2 contained 46.2% N, 0.55% biuret, melting point of 132.55 ºC and did not exhibit isotopic fractionation. The production cost of CO(15NH2)2 with 90.0 at. % 15N was US$ 238.60 per gram.